This work was funded by a New Faculty Award II from the California Institute of Regenerative Medicine (CIRM; RN2-00921-1), NIH-funded National Research Award (F32-HL104924), and CIRM Training Grant (TG21163). Materials were provided by: Glycosan Biosystems Inc / BioTime and Dr. Stephen Badylak (University of Pittsburgh)

1. Creation of pNIPAAM-coated Plates
<ol>
	<li>Dissolve the 2.6 g of pNIPAAM in 2 ml of a 60% toluene/40% hexane solution.</li>
	<li>Heat the mixture to 60 &#176;C for 10 min stirred, until the pNIPAAM is dissolved.</li>
	<li>Cut filter paper into a 60 mm diameter circle and place paper in the Buchner funnel.</li>
	<li>Filter the solution through Buchner Funnel into the pre-weighed glass beaker (do not use plastics, as hexane will melt plastics).</li>
	<li>Place the beaker and contents into a bell vacuum (24 psi) O/N&#160;(16 hr). Note: Until the residue is reacted with isopropyl it will oxidize so make sure it does not come into contact with oxygen.</li>
	<li>Weigh the beaker to establish the weight of the pNIPAAM.</li>
	<li>Add isopropyl alcohol to the pNIPAAM, creating a 50/50 w/w solution.</li>
	<li>Place 2 ml of the solution on the surface of the tissue culture plate, and coat for 5 min under UV light.</li>
	<li>Wash the plate with 2 ml of warm PBS twice before using for cell culture.</li>
</ol>
2. Creation of Cell Sheets
Note: Cell sheets of primary cells for the target organ can be created using a number of different methods, or by coating tissue culture surfaces with thermo-responsive polymer as described here. Pre-coated thermo-sensitive plates are also offered by a number of vendors.
Note: This protocol is for culture using a 35 mm dish. Briefly, cells are first incubated at 37 &#176;C for a minimum of 24 hr at confluence to establish lateral connections between adjacent cells. To release cell sheets, plates are subjected to temperatures below 32 &#176;C. The cell sheet is then transferred to the strong base fibrous matrix containing a neovascular permissive hydrogel with vascular endothelial cells.
<ol>
	<li>Isolate the cell population. Note: This method is dependent on the individual derivation procedures and the type of cells. Rat aortic smooth muscle cells (RASMC) are used in this example. These are primary smooth muscle cells isolated from the abdominal aorta of a rat.</li>
	<li>Wash the cells with 2 ml of warm PBS.</li>
	<li>Add 3 ml of trypsin (or other cleaving/disassociating solution) to the cells for 5 min.</li>
	<li>Inhibit the trypsin by the addition of 3 ml of the culture media, or phosphate buffer solution (PBS) containing 10% Fetal Bovine Serum (FBS).</li>
	<li>Collect the cells in a conical tube and count an aliquot.</li>
	<li>Spin the cells at 1,000 rpm (228 x g) for 5 min.</li>
	<li>Aspirate the supernatant and resuspend the cells in their growth media (SmGM2 plus bullet kit culture medium is used for RASMC).</li>
	<li>Place the media containing the cells on a 35 mm thermo-sensitive plate &#8211; pNIPAAM coated plate at a concentration that will achieve 100% confluence. Note: For RASMCs that number was determined to be 100,000 cells/cm2. However, due to loss of cells during the passing, 120% of that value is used.</li>
	<li>Place into an incubator at 37 &#176;C O/N. Note: It is important to maintain the cells at 37 &#176;C to maintain the cell adhesion to the plate.</li>
</ol>
3. Preparation of Foundational Matrix
Note: Various 3D fibrous matrices can be used to layer strong fibrous matrix between the delicate cell sheets. Some examples include: gelfoam, bioglass, natural acellularized materials26 or nanospun materials27,28 The porcine urinary bladder matrix (UBM) used in these studies was generously provided from our collaborator, Dr Badylak.29
<ol>
	<li>Prior to use, determine matrix characteristics including the lack of cellular content if decellularized matrix is used,27,28 cell specific viability, and void space.22</li>
	<li>Cut the pre-sterilized matrix into a desired size and shape. Note: Here, a hole-punch is used to cut a 4 mm diameter circle.</li>
</ol>
4. Seeding Endothelial Cells into a Neovascular Permissive Hydrogel
Note: Endothelial cells can be obtained from a variety of sources, including differentiation from stem or progenitor cells. Here, HuVECs are used.
<ol>
	<li>Use any permissive hydrogel (fibrin, collagen gels) as long as the cross-linking time is short enough to allow the cells stay viable. Note: Here, a Hyaluronan (HA) based gel cross-linked with a disulfide bridge is used.</li>
	<li>Prepare the HA hydrogel in accordance with the company protocol.</li>
	<li>Collect the endothelial cells and disperse into a single cell solution using 1x trypsin. Note: Accutase or Cell Dissociation Buffer could also be used for single cell dispersion.</li>
	<li>Deactivate the trypsin enzyme by using an equal amount of soybean trypsin inhibitor (if it is important that cells do not come into contact with serum) or 10% FBS in PBS, collecting the solution/cells into a 15 ml conical tube.</li>
	<li>Count the cells, and calculate the volume needed for the patch dimensions (previously quantified). Note: For a 4 mm patch, here 2 million endothelial cells are used.</li>
	<li>Extract 2 million cells, and place into a new 15 ml conical tube.</li>
	<li>Spin at (228 x g) for 5 min.</li>
	<li>Aspirate the supernatant, leaving the cells as a pellet in a conical tube.</li>
	<li>Mix the HA and Gelatin liquid materials in a 1:1 ration. Then add 80% of the total volume into the conical tube containing the pellet.</li>
	<li>Resuspend the endothelial cells in the 1:1 HA /Gelatin mixture</li>
	<li>Place the suspended cells in the HA /Gelatin mixture into the base fibrous matrix from Step 2.</li>
	<li>Add 1/5 (20 percent) of the total volume desired of the cross-linker</li>
	<li>Incubate for 1 hr at 37 &#176;C.</li>
</ol>
5. Isolation of Cell Sheets
<ol>
	<li>Remove the 35 mm pNIPAAM-treated plates containing the cells from the incubator and place in a cell culture hood at RT.</li>
	<li>Quickly aspirate the media from the cells, and add 2 ml of 6% normal gelatin that has been heated to 37 &#176;C.</li>
	<li>While the gelatin is still warm, place the metal lattice into the gelatin, submerging it below the surface of the normal gelatin (Movie 1).</li>
	<li>Place the entire plate onto ice for 5 to 7 min, allowing the gelatin to harden.</li>
	<li>After 7 min, use a spatula to carefully separate the gelatin edges from the side of the plate, and then use forceps to lift the metal lattice from the plate Note: The 6% gelatin, and the cell sheet should lift with the lattice.</li>
	<li>Move the cell sheet to the dish and place on top of the base fibrous matrix-hydrogel combination, carefully setting the lattice on top of the construct. Note: The apical side of the cell sheet will still be in the top position.</li>
	<li>Add 2 ml of warm media (37 &#176;C).</li>
	<li>Incubate O/N&#160;allowing the sheet of cells to adhere to the hydrogel surface.</li>
	<li>Remove the metal lattice after the solution warms (approximately 1 hr), or the next day.</li>
</ol>

<ol>
	<li>Ohashi, K., Okano, T. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Functional+tissue+engineering+of+the+liver+and+islets.">Functional tissue engineering of the liver and islets.</a> Anat Rec (Hoboken). 297, 73-82 (2014).</li><li>Chen, Q. Z., Harding, S. E., Ali, N. N., Lyon, A. R., Boccaccini, A. R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Biomaterials+in+cardiac+tissue+engineering:+Ten+years+of+research+survey.">Biomaterials in cardiac tissue engineering: Ten years of research survey.</a> Mat Sci Eng R. 59, 1-37 (2008).</li><li>Jakob, P., Landmesser, U. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Current+status+of+cell-based+therapy+for+heart+failure.">Current status of cell-based therapy for heart failure.</a> Curr Heart Fail Rep. 10, 165-176 (2013).</li><li>Tongers, J., Losordo, D. W., Landmesser, U. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Stem+and+progenitor+cell-based+therapy+in+ischaemic+heart+disease:+promise,+uncertainties,+and+challenges.">Stem and progenitor cell-based therapy in ischaemic heart disease: promise, uncertainties, and challenges.</a> Eur Heart J. 32, 1197-1206 (2011).</li><li>Etzion, S., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Influence+of+embryonic+cardiomyocyte+transplantation+on+the+progression+of+heart+failure+in+a+rat+model+of+extensive+myocardial+infarction.">Influence of embryonic cardiomyocyte transplantation on the progression of heart failure in a rat model of extensive myocardial infarction.</a> J Mol Cell Cardiol. 33, 1321-1330 (2001).</li><li>Masuda, S., Shimizu, T., Yamato, M., Okano, T. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Cell+sheet+engineering+for+heart+tissue+repair.">Cell sheet engineering for heart tissue repair.</a> Adv Drug Deliv Rev. 60, 277-285 (2008).</li><li>Koh, G. Y., Soonpaa, M. H., Klug, M. G., Field, L. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Strategies+for+myocardial+repair.">Strategies for myocardial repair.</a> J Interv Cardiol. 8, 387-393 (1995).</li><li>Li, R. K., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Construction+of+a+bioengineered+cardiac+graft.">Construction of a bioengineered cardiac graft.</a> J Thorac Cardiovasc Surg. 119, 368-375 (2000).</li><li>Muller-Ehmsen, J., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Rebuilding+a+damaged+heart:+long-term+survival+of+transplanted+neonatal+rat+cardiomyocytes+after+myocardial+infarction+and+effect+on+cardiac+function.">Rebuilding a damaged heart: long-term survival of transplanted neonatal rat cardiomyocytes after myocardial infarction and effect on cardiac function.</a> Circulation. , 105-1720 (2002).</li><li>Reinecke, H., Zhang, M., Bartosek, T., Murry, C. E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Survival,+integration,+and+differentiation+of+cardiomyocyte+grafts:+a+study+in+normal+and+injured+rat+hearts.">Survival, integration, and differentiation of cardiomyocyte grafts: a study in normal and injured rat hearts.</a> Circulation. , 100-193 (1999).</li><li>Roell, W., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Cellular+cardiomyoplasty+improves+survival+after+myocardial+injury.">Cellular cardiomyoplasty improves survival after myocardial injury.</a> Circulation. 105, 2435-2441 (2002).</li><li>Soonpaa, M. H., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Potential+approaches+for+myocardial+regeneration.">Potential approaches for myocardial regeneration.</a> Ann N Y Acad Sci. 752, 446-454 (1995).</li><li>Akins, R. E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Can+tissue+engineering+mend+broken+hearts.">Can tissue engineering mend broken hearts.</a> Circ Res. 90, 120-122 (2002).</li><li>Goodell, M. A., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Stem+cell+plasticity+in+muscle+and+bone+marrow.">Stem cell plasticity in muscle and bone marrow.</a> Ann N Y Acad Sci. 938, 208-218 (2001).</li><li>Menasche, P., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Myoblast+transplantation+for+heart+failure.">Myoblast transplantation for heart failure.</a> Lancet. 357, 279-280 (2001).</li><li>Murry, C. E., Wiseman, R. W., Schwartz, S. M., Hauschka, S. D. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Skeletal+myoblast+transplantation+for+repair+of+myocardial+necrosis.">Skeletal myoblast transplantation for repair of myocardial necrosis.</a> J Clin Invest. 98, 2512-2523 (1172).</li><li>Orlic, D., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Transplanted+adult+bone+marrow+cells+repair+myocardial+infarcts+in+mice.">Transplanted adult bone marrow cells repair myocardial infarcts in mice.</a> Ann N Y Acad Sci. 938, 221-229 (2001).</li><li>Elia, R., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Silk-hyaluronan-based+composite+hydrogels:+a+novel,+securable+vehicle+for+drug+delivery.">Silk-hyaluronan-based composite hydrogels: a novel, securable vehicle for drug delivery.</a> J Biomater Appl. 27, 749-762 (2013).</li><li>Kai, D., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Stem+cell-loaded+nanofibrous+patch+promotes+the+regeneration+of+infarcted+myocardium+with+functional+improvement+in+rat+model.">Stem cell-loaded nanofibrous patch promotes the regeneration of infarcted myocardium with functional improvement in rat model.</a> Acta Biomater. , (2014).</li><li>Hong, H. J., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Tracheal+reconstruction+using+chondrocytes+seeded+on+a+poly(l-lactic-co-glycolic+acid)-fibrin/hyaluronan.">Tracheal reconstruction using chondrocytes seeded on a poly(l-lactic-co-glycolic acid)-fibrin/hyaluronan.</a> J Biomed Mater Res A. , (2014).</li><li>Serpooshan, V., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=The+effect+of+bioengineered+acellular+collagen+patch+on+cardiac+remodeling+and+ventricular+function+post+myocardial+infarction.">The effect of bioengineered acellular collagen patch on cardiac remodeling and ventricular function post myocardial infarction.</a> Biomaterials. 34, 9048-9055 (2013).</li><li>Turner, W. S., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Cardiac+tissue+development+for+delivery+of+embryonic+stem+cell-derived+endothelial+and+cardiac+cells+in+natural+matrices.">Cardiac tissue development for delivery of embryonic stem cell-derived endothelial and cardiac cells in natural matrices.</a> J Biomed Mater Res B Appl Biomater. 100, 2060-2072 (2012).</li><li>Sato, M., Yamato, M., Hamahashi, K., Okano, T., Mochida, J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Articular+cartilage+regeneration+using+cell+sheet+technology.">Articular cartilage regeneration using cell sheet technology.</a> Anat Rec (Hoboken). 297, 36-43 (2014).</li><li>Sawa, Y., Miyagawa, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Present+and+future+perspectives+on+cell+sheet-based+myocardial+regeneration+therapy.">Present and future perspectives on cell sheet-based myocardial regeneration therapy.</a> Biomed Res Int. 2013, 583912 (2013).</li><li>Demirbag, B., Huri, P. Y., Kose, G. T., Buyuksungur, A., Hasirci, V. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Advanced+cell+therapies+with+and+without+scaffolds.">Advanced cell therapies with and without scaffolds.</a> Biotechnol J. 6, 1437-1453 (2011).</li><li>Song, J. J., Ott, H. C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Organ+engineering+based+on+decellularized+matrix+scaffolds.">Organ engineering based on decellularized matrix scaffolds.</a> Trends Mol Med. 17, 424-432 (2011).</li><li>Badylak, S. F., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=The+use+of+extracellular+matrix+as+an+inductive+scaffold+for+the+partial+replacement+of+functional+myocardium.">The use of extracellular matrix as an inductive scaffold for the partial replacement of functional myocardium.</a> Cell Transplant. 15, S29-S40 (2006).</li><li>Wang, Y., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Lineage+restriction+of+human+hepatic+stem+cells+to+mature+fates+is+made+efficient+by+tissue-specific+biomatrix+scaffolds.">Lineage restriction of human hepatic stem cells to mature fates is made efficient by tissue-specific biomatrix scaffolds.</a> Hepatology. 53, 293-305 (2011).</li><li>Gilbert, T. W., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Collagen+fiber+alignment+and+biaxial+mechanical+behavior+of+porcine+urinary+bladder+derived+extracellular+matrix.">Collagen fiber alignment and biaxial mechanical behavior of porcine urinary bladder derived extracellular matrix.</a> Biomaterials. 29, 4775-4782 (2008).</li><li>Luna, J. I., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Multiscale+biomimetic+topography+for+the+alignment+of+neonatal+and+embryonic+stem+cell-derived+heart+cells.">Multiscale biomimetic topography for the alignment of neonatal and embryonic stem cell-derived heart cells.</a> Tissue Eng Part C Methods. 17, 579-588 (2011).</li></ol>

We have nothing to disclose.

The critical steps in the protocol include: coating the plate surfaces with the thermoresponsive polymer and manipulating the cell sheets after cooling the plates. Because different cells exhibit different physical properties, like adhesivity, the lifting time should be optimized for each different cell type. The second, and most significantly challenging component of this protocol, centers on the manipulation of the cell sheet, a critical aspect of methods for tissue assembly. The single cell layer in the cell sheet is ...

Injection of cells and/or single materials alone has shown variable success in other organ systems and limited success in cardiac regeneration.5,7-12 Currently, stem cell-derived cells are delivered to damaged tissue using a variety of delivery methods including: direct cell injection into tissue and perfusion into the blood supply.13-17 Others have implanted cells alone, materials alone and/or in combination with material carriers to help regenerate damaged organs.18-21 This design combines multiple strategies that provide material strength, patterning in multiple materials and multiple cell types. 
Specifically, the base acellularized fibrous matrix provides the foundational physical strength to the construct, making it suitable for suturing in into the patient, if necessary. The void spaces in the base matrix are filled with endothelial cells in a neovascular permissive hydrogel22 for rapidly establishing vascularization of the implanted construct. This composite is then integrated with pre-patterned cell sheets that allow enhanced cell-to-cell communication, more closely mimic the native tissue.1,23-25 The overall production process for the layered cellular patch is outlined by the flowchart in Figure 1.

<table border="0" cellpadding="0" cellspacing="0" width="695">
	<tbody>
		<tr height="22">
			<td height="22" style="height:22px;width:207px;">Table of Reagents:</td>
			<td style="width:128px;"></td>
			<td style="width:140px;"></td>
			<td style="width:221px;"></td>
		</tr>
		<tr height="42">
			<td height="42" style="height:42px;width:207px;">Reagent</td>
			<td style="width:128px;">Company</td>
			<td style="width:140px;">Catalogue number</td>
			<td style="width:221px;">Comments</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:207px;">Calcein-AM</td>
			<td style="width:128px;">Invitrogen</td>
			<td style="width:140px;">C3099</td>
			<td style="width:221px;">Cell tracker / live dye</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:207px;">Lysotracker Red</td>
			<td style="width:128px;">Invitrogen</td>
			<td style="width:140px;">L7528</td>
			<td style="width:221px;">Cell tracker</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:207px;">Neutral Red</td>
			<td style="width:128px;">Sigma</td>
			<td style="width:140px;">N7005</td>
			<td style="width:221px;">Visible Cell dye</td>
		</tr>
		<tr height="24">
			<td height="24" style="height:24px;width:207px;">pNIPAAM</td>
			<td style="width:128px;">Sigma Aldrich</td>
			<td style="width:140px;">412780250</td>
			<td style="width:221px;">Poly(N-isopropylacrylamide)</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:207px;">Toluene</td>
			<td style="width:128px;">Sigma Aldrich</td>
			<td style="width:140px;">244511-1L</td>
			<td style="width:221px;"></td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:207px;">Hexane</td>
			<td style="width:128px;">Sigma Aldrich</td>
			<td style="width:140px;">296090-1L</td>
			<td style="width:221px;"></td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:207px;">RAOSMC</td>
			<td style="width:128px;">Lonza</td>
			<td style="width:140px;">R-ASM-580</td>
			<td style="width:221px;">Rat Aortic Smooth Muscle Cells</td>
		</tr>
		<tr height="23">
			<td height="23" style="height:23px;width:207px;">SmGM2</td>
			<td style="width:128px;">Lonza</td>
			<td style="width:140px;">CC-4149</td>
			<td style="width:221px;">Smooth Muscle Media</td>
		</tr>
		<tr height="24">
			<td height="24" style="height:24px;width:207px;">HUVEC</td>
			<td style="width:128px;">Invitrogen</td>
			<td style="width:140px;">C-003-5C</td>
			<td style="width:221px;">Human Venous Endothelial Cells</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:207px;">HyStem</td>
			<td style="width:128px;">Glycosan/Biotime</td>
			<td style="width:140px;">------------</td>
			<td style="width:221px;"></td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:207px;">Isopropyl alcohol</td>
			<td style="width:128px;">VWR International</td>
			<td style="width:140px;">BDH1133-4LP</td>
			<td style="width:221px;"></td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:207px;">Trypsin</td>
			<td style="width:128px;">Corning Cellgro</td>
			<td style="width:140px;">25-053-C1</td>
			<td style="width:221px;"></td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:207px;">PBS</td>
			<td style="width:128px;">Gibco</td>
			<td style="width:140px;">14287-072</td>
			<td style="width:221px;"></td>
		</tr>
		<tr height="22">
			<td height="22" style="height:22px;width:207px;">FBS</td>
			<td style="width:128px;">Gibco</td>
			<td style="width:140px;">16140-071</td>
			<td style="width:221px;"></td>
		</tr>
		<tr height="20">
			<td height="20" style="height:20px;"></td>
			<td></td>
			<td></td>
			<td></td>
		</tr>
		<tr height="22">
			<td height="22" style="height:22px;">Table of Specific Equipment:</td>
			<td></td>
			<td></td>
			<td></td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:207px;">&#160;Equipment&#160;</td>
			<td style="width:128px;">&#160;Company&#160;</td>
			<td style="width:140px;">&#160;Catalogue number&#160;</td>
			<td style="width:221px;">&#160;Comments (optional)&#160;</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:207px;">&#160;Filter paper&#160;</td>
			<td style="width:128px;">&#160;Ahlstrom&#160;</td>
			<td style="width:140px;">&#160;6310-0900&#160;</td>
			<td style="width:221px;"></td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:207px;">&#160;Buchner Funnel&#160;</td>
			<td style="width:128px;">&#160;Sigma Aldrich&#160;</td>
			<td style="width:140px;">&#160;Z247308&#160;</td>
			<td style="width:221px;"></td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:207px;">&#160;UpCell Plates&#160;</td>
			<td style="width:128px;">&#160;Nunc&#160;</td>
			<td style="width:140px;">&#160;2014-11&#160;</td>
			<td style="width:221px;"></td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:207px;">&#160;UV light.&#160;</td>
			<td style="width:128px;">&#160;Jelight Company&#160;</td>
			<td style="width:140px;">&#160;UVO Cleaner Model No.42&#160;</td>
			<td style="width:221px;"></td>
		</tr>
	</tbody>
</table>

tissue engineering: construction of a multicellular 3d scaffold for the delivery of layered cell sheets

Many tissues, such as the adult human hearts, are unable to adequately regenerate after damage.2,3 Strategies in tissue engineering propose innovations to assist the body in recovery and repair. For example, TE approaches may be able to attenuate heart remodeling after myocardial infarction (MI) and possibly increase total heart function to a near normal pre-MI level.4 As with any functional tissue, successful regeneration of cardiac tissue involves the proper delivery of multiple cell types with environmental cues favoring integration and survival of the implanted cell/tissue graft. Engineered tissues should address multiple parameters including: soluble signals, cell-to-cell interactions, and matrix materials evaluated as delivery vehicles, their effects on cell survival, material strength, and facilitation of cell-to-tissue organization. Studies employing the direct injection of graft cells only ignore these essential elements.2,5,6 A tissue design combining these ingredients has yet to be developed. Here, we present an example of integrated designs using layering of patterned cell sheets with two distinct types of biological-derived materials containing the target organ cell type and endothelial cells for enhancing new vessels formation in the &#8220;tissue&#8221;. Although these studies focus on the generation of heart-like tissue, this tissue design can be applied to many organs other than heart with minimal design and material changes, and is meant to be an off-the-shelf product for regenerative therapies. The protocol contains five detailed steps. A temperature sensitive Poly(N-isopropylacrylamide) (pNIPAAM) is used to coat tissue culture dishes. Then, tissue specific cells are cultured on the surface of the coated plates/micropattern surfaces to form cell sheets with strong lateral adhesions. Thirdly, a base matrix is created for the tissue by combining porous matrix with neovascular permissive hydrogels and endothelial cells. Finally, the cell sheets are lifted from the pNIPAAM coated dishes and transferred to the base element, making the complete construct.

The flow diagram (Figure 1) shows the overall method of making the multilayered patch. Cell sheets are detached from the pNIPAAM treated plate by dropping the temperature below 32 &#176;C. Then the cell sheet is placed on top of the cross-linked hydrogel containing the endothelial cells seeded into the underlying fibrous matrix (Figure 1). The pretreated thermo-sensitive plates can also be used for creating the cell sheets. Special topological surfaces are used to specifically pattern (<...

Watch this Scientific Journal Video about Tissue Engineering: Construction of a Multicellular 3D Scaffold for the Delivery of Layered Cell Sheets at JoVE.com

Tissue Engineering: Construction of a Multicellular 3D Scaffold for the Delivery of Layered Cell Sheets

For creation of highly organized structures of complex tissue, one must assemble multiple material and cell types into an integrated composite. This combinatorial design incorporates organ-specific layered cell sheets with two distinct biologically-derived materials containing a strong fibrous matrix base, and endothelial cells for enhancing new vessels formation.

Many tissues, such as the adult human hearts, are unable to adequately regenerate after damage.2,3 Strategies in tissue engineering propose innovations to ...

tissue-engineering-construction-multicellular-3d-scaffold-for

Research

JoVE Journal

Bioengineering

14.4K vistas.  University of California, Merced. For creation of highly organized structures of complex tissue, one must assemble multiple material and cell types into an integrated composite. This combinatorial design incorporates organ-specific layered cell sheets with two distinct biologically-derived materials containing a strong fibrous matrix base, and endothelial cells for enhancing new vessels formation.

Video: Tissue Engineering: Construction of a Multicellular 3D Scaffold for the Delivery of Layered Cell Sheets

Design of a Biaxial Mechanical Loading Bioreactor for Tissue Engineering

We designed a loading device that is capable of applying uniaxial or biaxial mechanical strain to a tissue engineered biocomposites fabricated for transplantation. While the device primarily functions as a bioreactor that mimics the native mechanical strains, it is also outfitted with a load cell for providing force feedback or mechanical testing of the constructs. The device subjects engineered cartilage constructs to biaxial mechanical loading with great precision of loading dose (amplitude and frequency) and is compact enough to fit inside a standard tissue culture incubator. It loads samples directly in a tissue culture plate, and multiple plate sizes are compatible with the system. The device has been designed using components manufactured for precision-guided laser applications. Bi-axial loading is accomplished by two orthogonal stages. The stages have a 50 mm travel range and are driven independently by stepper motor actuators, controlled by a closed-loop stepper motor driver that features micro-stepping capabilities, enabling step sizes of less than 50 nm. A polysulfone loading platen is coupled to the bi-axial moving platform. Movements of the stages are controlled by Thor-labs Advanced Positioning Technology (APT) software. The stepper motor driver is used with the software to adjust load parameters of frequency and amplitude of both shear and compression independently and simultaneously. Positional feedback is provided by linear optical encoders that have a bidirectional repeatability of 0.1 &mu;m and a resolution of 20 nm, translating to a positional accuracy of less than 3 &mu;m over the full 50 mm of travel. These encoders provide the necessary position feedback to the drive electronics to ensure true nanopositioning capabilities. In order to provide the force feedback to detect contact and evaluate loading responses, a precision miniature load cell is positioned between the loading platen and the moving platform. The load cell has high accuracies of 0.15% to 0.25% full scale.

We designed a novel mechanical loading bioreactor that can apply uniaxial or biaxial mechanical strain to a cartilage biocomposite prior to transplantation into an articular cartilage defect.

We  designed a loading device that is capable of applying uniaxial or biaxial  mechanical strain to a tissue engineered biocomposites fabricated for  ...

Tissue Engineering of a Human 3D in vitro Tumor Test System

Cancer is one of the leading causes of death worldwide. Current therapeutic strategies are predominantly developed in 2D culture systems, which inadequately reflect physiological conditions in vivo. Biological 3D matrices provide cells an environment in which cells can self-organize, allowing the study of tissue organization and cell differentiation. Such scaffolds can be seeded with a mixture of different cell types to study direct 3D cell-cell-interactions. To mimic the 3D complexity of cancer tumors, our group has developed a 3D in vitro tumor test system.	
	Our 3D tissue test system models the in vivo situation of malignant peripheral nerve sheath tumors (MPNSTs), which we established with our decellularized porcine jejunal segment derived biological vascularized scaffold (BioVaSc). In our model, we reseeded a modified BioVaSc matrix with primary fibroblasts, microvascular endothelial cells (mvECs) and the S462 tumor cell line. For static culture, the vascular structure of the BioVaSc is removed and the remaining scaffold is cut open on one side (Small Intestinal Submucosa SIS-Muc). The resulting matrix is then fixed between two metal rings (cell crowns).	
	Another option is to culture the cell-seeded SIS-Muc in a flow bioreactor system that exposes the cells to shear stress. Here, the bioreactor is connected to a peristaltic pump in a self-constructed incubator. A computer regulates the arterial oxygen and nutrient supply via parameters such as blood pressure, temperature, and flow rate. This setup allows for a dynamic culture with either pressure-regulated pulsatile or constant flow.	
	In this study, we could successfully establish both a static and dynamic 3D culture system for MPNSTs. The ability to model cancer tumors in a more natural 3D environment will enable the discovery, testing, and validation of future pharmaceuticals in a human-like model.

Tissue Engineering of a Human 3D in vitro Tumor Test System

Methods to create human 3D tumor tissues as test systems are described. These technologies are based on a decellularized Biological Vascularized Scaffold (BioVaSc), primary human cells and a tumor cell line, which can be cultured under static as well as under dynamic conditions in a flow bioreactor.

Cancer is one of the leading causes of death worldwide.  Current therapeutic strategies are predominantly developed in 2D culture  systems, which ...

Self-reporting Scaffolds for 3-Dimensional Cell Culture

Culturing cells in 3D on appropriate scaffolds is thought to better mimic the in vivo microenvironment and increase cell-cell interactions. The resulting 3D cellular construct can often be more relevant to studying the molecular events and cell-cell interactions than similar experiments studied in 2D. To create effective 3D cultures with high cell viability throughout the scaffold the culture conditions such as oxygen and pH need to be carefully controlled as gradients in analyte concentration can exist throughout the 3D construct. Here we describe the methods of preparing biocompatible pH responsive sol-gel nanosensors and their incorporation into poly(lactic-co-glycolic acid) (PLGA) electrospun scaffolds along with their subsequent preparation for the culture of mammalian cells. The pH responsive scaffolds can be used as tools to determine microenvironmental pH within a 3D cellular construct. Furthermore, we detail the delivery of pH responsive nanosensors to the intracellular environment of mammalian cells whose growth was supported by electrospun PLGA scaffolds. The cytoplasmic location of the pH responsive nanosensors can be utilized to monitor intracellular pH (pHi) during ongoing experimentation.

Biocompatible pH responsive sol-gel nanosensors can be incorporated into poly(lactic-co-glycolic acid) (PLGA) electrospun scaffolds. The produced self-reporting scaffolds can be used for in&#160;situ monitoring of microenvironmental conditions whilst culturing cells upon the scaffold. This is beneficial as the 3D cellular construct can be monitored in real-time without disturbing the experiment.

Culturing cells in 3D on appropriate scaffolds is thought to better mimic the in vivo microenvironment and increase cell-cell interactions. The resulting ...

Engineering 3D Cellularized Collagen Gels for Vascular Tissue Regeneration

Synthetic materials are known to initiate clinical complications such as inflammation, stenosis, and infections when implanted as vascular substitutes. Collagen has been extensively used for a wide range of biomedical applications and is considered a valid alternative to synthetic materials due to its inherent biocompatibility (i.e., low antigenicity, inflammation, and cytotoxic responses). However, the limited mechanical properties and the related low hand-ability of collagen gels have hampered their use as scaffold materials for vascular tissue engineering. Therefore, the rationale behind this work was first to engineer cellularized collagen gels into a tubular-shaped geometry and second to enhance smooth muscle cells driven reorganization of collagen matrix to obtain tissues stiff enough to be handled.
The strategy described here is based on the direct assembling of collagen and smooth muscle cells (construct) in a 3D cylindrical geometry with the use of a molding technique. This process requires a maturation period, during which the constructs are cultured in a bioreactor under static conditions (without applied external dynamic mechanical constraints) for 1 or 2 weeks. The &#8220;static bioreactor&#8221; provides a monitored and controlled sterile environment (pH, temperature, gas exchange, nutrient supply and waste removal) to the constructs. During culture period, thickness measurements were performed to evaluate the cells-driven remodeling of the collagen matrix, and glucose consumption and lactate production rates were measured to monitor the cells metabolic activity. Finally, mechanical and viscoelastic properties were assessed for the resulting tubular constructs. To this end, specific protocols and a focused know-how (manipulation, gripping, working in hydrated environment, and so on) were developed to characterize the engineered tissues.

In this work, we present a technique for the rapid fabrication of living vascular tissues by direct culturing of collagen, smooth muscle cells and endothelial cells. In addition, a new protocol for the mechanical characterization of engineered vascular tissues is described.

Synthetic materials are known to initiate clinical complications such as inflammation, stenosis, and infections when implanted as vascular substitutes. ...

Adapting the Electrospinning Process to Provide Three Unique Environments for a Tri-layered In Vitro Model of the Airway Wall

Electrospinning is a highly adaptable method producing porous 3D fibrous scaffolds that can be exploited in in vitro cell culture. Alterations to intrinsic parameters within the process allow a high degree of control over scaffold characteristics including fiber diameter, alignment and porosity. By developing scaffolds with similar dimensions and topographies to organ- or tissue-specific extracellular matrices (ECM), micro-environments representative to those that cells are exposed to in situ can be created. 
The airway bronchiole wall, comprised of three main micro-environments, was selected as a model tissue. Using decellularized airway ECM as a guide, we electrospun the non-degradable polymer, polyethylene terephthalate (PET), by three different protocols to produce three individual electrospun scaffolds optimized for epithelial, fibroblast or smooth muscle cell-culture. Using a commercially available bioreactor system, we stably co-cultured the three cell-types to provide an in vitro model of the airway wall over an extended time period.
This model highlights the potential for such methods being employed in in vitro diagnostic studies investigating important inter-cellular cross-talk mechanisms or assessing novel pharmaceutical targets, by providing a relevant platform to allow the culture of fully differentiated adult cells within 3D, tissue-specific environments.

Adapting the Electrospinning Process to Provide Three Unique Environments for a Tri-layered In Vitro Model of the Airway Wall

Advancements in biomaterial technologies enable the development of three-dimensional multi-cell-type constructs. We have developed electrospinning protocols to produce three individual scaffolds to culture the main structural cells of the airway to provide a 3D in vitro model of the airway bronchiole wall.

Electrospinning is a highly adaptable method producing porous 3D fibrous scaffolds that can be exploited in in vitro cell culture. Alterations to ...

Construction of Modular Hydrogel Sheets for Micropatterned Macro-scaled 3D Cellular Architecture

Hydrogels can be patterned at the micro-scale using microfluidic or micropatterning technologies to provide an in vivo-like three-dimensional (3D) tissue geometry. The resulting 3D hydrogel-based cellular constructs have been introduced as an alternative to animal experiments for advanced biological studies, pharmacological assays and organ transplant applications. Although hydrogel-based particles and fibers can be easily fabricated, it is difficult to manipulate them for tissue reconstruction. In this video, we describe a fabrication method for micropatterned alginate hydrogel sheets, together with their assembly to form a macro-scale 3D cell culture system with a controlled cellular microenvironment. Using a mist form of the calcium gelling agent, thin hydrogel sheets are easily generated with a thickness in the range of 100 - 200 &#181;m, and with precise micropatterns. Cells can then be cultured with the geometric guidance of the hydrogel sheets in freestanding conditions. Furthermore, the hydrogel sheets can be readily manipulated using a micropipette with an end-cut tip, and can be assembled into multi-layered structures by stacking them using a patterned polydimethylsiloxane (PDMS) frame. These modular hydrogel sheets, which can be fabricated using a facile process, have potential applications of in vitro drug assays and biological studies, including functional studies of micro- and macrostructure and tissue reconstruction.

We describe the fabrication of micropatterned hydrogel sheets using a simple process, which can be assembled and manipulated in a freestanding form. Using these modular hydrogel sheets, a simple macro-scaled 3D cell culture system can be generated with a controlled cellular microenvironment.

Hydrogels can be patterned at the micro-scale using microfluidic or micropatterning technologies to provide an in vivo-like three-dimensional (3D) tissue ...

Fabrication of Inverted Colloidal Crystal Poly(ethylene glycol) Scaffold: A Three-dimensional Cell Culture Platform for Liver Tissue Engineering

The ability to maintain hepatocyte function in vitro, for the purpose of testing xenobiotics&#39; cytotoxicity, studying virus infection and developing drugs targeted at the liver, requires a platform in which cells receive proper biochemical and mechanical cues. Recent liver tissue engineering systems have employed three-dimensional (3D) scaffolds composed of synthetic or natural hydrogels, given their high water retention and their ability to provide the mechanical stimuli needed by the cells. There has been growing interest in the inverted colloidal crystal (ICC) scaffold, a recent development, which allows high spatial organization, homotypic and heterotypic cell interaction, as well as cell-extracellular matrix (ECM) interaction. Herein, we describe a protocol to fabricate the ICC scaffold using poly (ethylene glycol) diacrylate (PEGDA) and the particle leaching method. Briefly, a lattice is made from microsphere particles, after which a pre-polymer solution is added, properly polymerized, and the particles are then removed, or leached, using an organic solvent (e.g., tetrahydrofuran). The dissolution of the lattice results in a highly porous scaffold with controlled pore sizes and interconnectivities that allow media to reach cells more easily. This unique structure allows high surface area for the cells to adhere to as well as easy communication between pores, and the ability to coat the PEGDA ICC scaffold with proteins also shows a marked effect on cell performance. We analyze the morphology of the scaffold as well as the hepatocarcinoma cell (Huh-7.5) behavior in terms of viability and function to explore the effect of ICC structure and ECM coatings. Overall, this paper provides a detailed protocol of an emerging scaffold that has wide applications in tissue engineering, especially liver tissue engineering.

Fabrication of Inverted Colloidal Crystal Polyethylene glycol Scaffold: A Three-dimensional Cell Culture Platform for Liver Tissue Engineering

This manuscript presents a detailed protocol for the fabrication of an emerging three-dimensional hepatocyte culture platform, the inverted colloidal crystal scaffold, and the concomitant techniques to assess hepatocyte behavior. The size-controllable pores, interconnectivity and ability to conjugate extracellular matrix proteins to the poly(ethylene glycol) (PEG) scaffold enhance Huh-7.5 cell performance.

The ability to maintain hepatocyte function in vitro, for the purpose of testing xenobiotics&#39; cytotoxicity, studying virus infection and developing ...

Fabrication of Extracellular Matrix-derived Foams and Microcarriers as Tissue-specific Cell Culture and Delivery Platforms

Cell function is mediated by interactions with the extracellular matrix (ECM), which has complex tissue-specific composition and architecture. The focus of this article is on the methods for fabricating ECM-derived porous foams and microcarriers for use as biologically-relevant substrates in advanced 3D in vitro cell culture models or as pro-regenerative scaffolds and cell delivery systems for tissue engineering and regenerative medicine. Using decellularized tissues or purified insoluble collagen as a starting material, the techniques can be applied to synthesize a broad array of tissue-specific bioscaffolds with customizable geometries. The approach involves mechanical processing and mild enzymatic digestion to yield an ECM suspension that is used to fabricate the three-dimensional foams or microcarriers through controlled freezing and lyophilization procedures. These pure ECM-derived scaffolds are highly porous, yet stable without the need for chemical crosslinking agents or other additives that may negatively impact cell function. The scaffold properties can be tuned to some extent by varying factors such as the ECM suspension concentration, mechanical processing methods, or synthesis conditions. In general, the scaffolds are robust and easy to handle, and can be processed as tissues for most standard biological assays, providing a versatile and user-friendly 3D cell culture platform that mimics the native ECM composition. Overall, these straightforward methods for fabricating customized ECM-derived foams and microcarriers may be of interest to both biologists and biomedical engineers as tissue-specific cell-instructive platforms for in vitro and in vivo applications.

The tissue-specific extracellular matrix (ECM) is a key mediator of cell function. This article describes methods for synthesizing pure ECM-derived foams and microcarriers that are stable in culture without the need for chemical crosslinking for applications in advanced 3D in vitro cell culture models or as pro-regenerative bioscaffolds.

Cell function is mediated by interactions with the extracellular matrix (ECM), which has complex tissue-specific composition and architecture. The focus ...

Bioprinting of Cartilage and Skin Tissue Analogs Utilizing a Novel Passive Mixing Unit Technique for Bioink Precellularization

Bioprinting is a powerful technique for the rapid and reproducible fabrication of constructs for tissue engineering applications. In this study, both cartilage and skin analogs were fabricated after bioink pre-cellularization utilizing a novel passive mixing unit technique. This technique was developed with the aim to simplify the steps involved in the mixing of a cell suspension into a highly viscous bioink. The resolution of filaments deposited through bioprinting necessitates the assurance of uniformity in cell distribution prior to printing to avoid the deposition of regions without cells or retention of large cell clumps that can clog the needle. We demonstrate the ability to rapidly blend a cell suspension with a bioink prior to bioprinting of both cartilage and skin analogs. Both tissue analogs could be cultured for up to 4 weeks. Histological analysis demonstrated both cell viability and deposition of tissue specific extracellular matrix (ECM) markers such as glycosaminoglycans (GAGs) and collagen I respectively.

Cartilage and skin analogs were bioprinted using a nanocellulose-alginate based bioink. The bioinks were cellularized prior to printing via a single step passive mixing unit. The constructs were demonstrated to be uniformly cellularized, have high viability, and exhibit favorable markers of differentiation.

Bioprinting is a powerful technique for the rapid and reproducible fabrication of constructs for tissue engineering applications. In this study, both ...

Fabrication of Custom Agarose Wells for Cell Seeding and Tissue Ring Self-assembly Using 3D-Printed Molds

Engineered tissues are being used clinically for tissue repair and replacement, and are being developed as tools for drug screening and human disease modeling. Self-assembled tissues offer advantages over scaffold-based tissue engineering, such as enhanced matrix deposition, strength, and function. However, there are few available methods for fabricating 3D tissues without seeding cells on or within a supporting scaffold. Previously, we developed a system for fabricating self-assembled tissue rings by seeding cells into non-adhesive agarose wells. A polydimethylsiloxane (PDMS) negative was first cast in a machined polycarbonate mold, and then agarose was gelled in the PDMS negative to create ring-shaped cell seeding wells. However, the versatility of this approach was limited by the resolution of the tools available for machining the polycarbonate mold. Here, we demonstrate that 3D-printed plastic can be used as an alternative to machined polycarbonate for fabricating PDMS negatives. The 3D-printed mold and revised mold design is simpler to use, inexpensive to produce, and requires significantly less agarose and PDMS per cell seeding well. We have demonstrated that the resulting agarose wells can be used to create self-assembled tissue rings with customized diameters from a variety of different cell types. Rings can then be used for mechanical, functional, and histological analysis, or for fabricating larger and more complex tubular tissues.

This protocol describes a platform for fabricating self-assembled tissue rings in variable sizes using a customized 3D-printed plastic mold. PDMS negatives are cured in the 3D-printed mold; then agarose is cast in the cured PDMS negatives. Cells are seeded into the resulting agarose wells where they aggregate into tissue rings.

Engineered tissues are being used clinically for tissue repair and replacement, and are being developed as tools for drug screening and human disease ...