Part I: Patterning of the electrodes
<ol>
<li>Clean and dehydrated ITO coated glass slides were coated with positive photoresist</li>
<li>The surface was baked at 100&deg;C to remove solvents from the resist</li>
<li>After baking, the surface was exposed to ultraviolet light through a photomask using the Canon Mask Aligner</li>
<li>The exposed regions were removed in a developer solution</li>
<li>The surface was hard baked to remove any remaining developer solution</li>
<li>The ITO regions not protected by photoresist patterning were etched away in an acid etchant</li>
<li>Remaining photoresist was removed by sonicating in acetone to form the ITO electrodes</li>
</ol>
Part II: Surface modification
<ol>
<li>Modified electrodes are cleaned in a plasma chamber and modified with 2% PEG silane in toluene. Incubation is carried out for 2 hours, followed by 2 hours of baking.</li>
</ol>
Note: This process is carried out in a glove bag filled with nitrogen to avoid presence of moisture, as PEG silane is reactive towards it.
Part III: Electrochemistry
<ol>
<li>Steel wires are attached to electrode pads.</li>
<li>The PEG silane modified electrodes are placed in an electrochemical cell to perform electrochemical experiments.</li>
<li>PEG silane from interconnected regions is stripped using a three-electrode system in PBS.</li>
</ol>
Part IV: Cell patterning
<ol>
<li>Fibroblasts are incubated with the recently stripped substrates. Upon incubation, these cells attach to the PEG silane stripped regions; however, the cells will not bind anywhere else on the surface.</li>
<li>Patterned cells are incubated in fresh media and visualized using a microscope.</li>
</ol>

<ol>
	<li>Lee, J. Y., Jones, C., Zern, M. A., Revzin, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Analysis+of+Local+Tissue-Specific+Gene+Expression+in+Cellular+Micropatterns.">Analysis of Local Tissue-Specific Gene Expression in Cellular Micropatterns.</a> Analytical Chemistry. 78, 8305-8312 (2006).</li></ol>

In this video, we have demonstrated the cell patterning on optically transparent indium tin oxide electrodes. After fabricating the ITO electrodes using photolithography, they were modified with a cell-resistive monolayer of PEG silane. This monolayer was desorbed using electrochemistry switching the surface from cell-resistive to cell-adhesive. Patterning of 3T3 murine fibroblasts has been shown in his video. We have also patterning hepatocytes, primary cells, and stellate cells using the same technique. In addition...

<!DOCTYPE html PUBLIC "-//W3C//DTD XHTML 1.0 Transitional//EN" "http://www.w3.org/TR/xhtml1/DTD/xhtml1-transitional.dtd">
<html xmlns="http://www.w3.org/1999/xhtml" xml:lang="en" lang="en">	
		
		<div>
		<table border="1">
		<thead>
		<tr>
		<th>Material Name</th>
		<th>Type</th>
		<th>Company</th>
		<th>Catalogue Number</th>
		<th>Comment</th>
		</tr>
		</thead>
		<tbody>
		
<tr>
<td>Indium Tin Oxide</td>
<td>Other</td>
<td>Delta Technologies</td>
<td>CB 40IN</td>
<td>&nbsp;</td>
<tr>
<td>PEG silane</td>
<td>Reagent</td>
<td>Gelest Inc.</td>
<td>SIM6492.66</td>
<td>&nbsp;</td>
<tr>
<td>Hydrochloric Acid</td>
<td>Reagent</td>
<td>Sigma-Aldrich</td>
<td>320331</td>
<td>&nbsp;</td>
<tr>
<td>Nitric Acid</td>
<td>Reagent</td>
<td>Sigma Aldrich</td>
<td>258121</td>
<td>&nbsp;</td>
<tr>
<td>Ethanol</td>
<td>Reagent</td>
<td>Sigma-Aldrich</td>
<td>459836</td>
<td>&nbsp;</td>
<tr>
<td>Acetone</td>
<td>Reagent</td>
<td>Sigma-Aldrich</td>
<td>650501</td>
<td>&nbsp;</td>
<tr>
<td>Toluene</td>
<td>Reagent</td>
<td>Sigma-Aldrich</td>
<td>34866</td>
<td>&nbsp;</td>
<tr>
<td>Media</td>
<td>Reagent</td>
<td>Invitrogen Technologies</td>
<td>&nbsp;</td>
<td>&nbsp;</td>
<tr>
<td>Collagen</td>
<td>Reagent</td>
<td>Sigma-Aldrich</td>
<td>C3867</td>
<td>&nbsp;</td>
<tr>
<td>3T3 murine Fibroblasts</td>
<td>Cell Line</td>
<td>ATCC</td>
<td>&nbsp;</td>
<td>&nbsp;</td>		</tbody>
		</table>
		</div>
			<div>
					</div>

patterning cells on optically transparent indium tin oxide electrodes

The ability to exercise precise spatial and temporal control over cell-surface interactions is an important prerequisite to the assembly of multi-cellular constructs serving as in vitro mimics of native tissues.  In this study, photolithography and wet etching techniques were used to fabricate individually addressable indium tin oxide (ITO) electrodes on glass substrates.  The glass substrates containing ITO microelectrodes were modified with poly(ethylene glycol) (PEG) silane to make them protein and cell resistive.  Presence of insulating PEG molecules on the electrode surface was verified by cyclic voltammetry employing potassium ferricyanide as a redox reporter molecule.  Importantly, the application of reductive potential caused desorption of the PEG layer, resulting in regeneration of the conductive electrode surface and appearance of typical ferricyanide redox peaks.    Application of reductive potential also corresponded to switching of ITO electrode properties from cell non-adhesive to cell-adhesive. Electrochemical stripping of PEG-silane layer from ITO microelectrodes allowed for cell adhesion to take place in a spatially defined fashion, with cellular patterns corresponding closely to electrode patterns.  Micropatterning of several cell types was demonstrated on these substrates.   In the future, the control of the biointerfacial properties afforded by this method will allow to engineer cellular microenvironments through the assembly of three or more cell types into a precise geometric configuration on an optically transparent substrate.

Watch this Scientific Journal Video about Patterning Cells on Optically Transparent Indium Tin Oxide Electrodes at JoVE.com

Patterning Cells on Optically Transparent Indium Tin Oxide Electrodes

Non-fouling PEG silane monolayer was desorbed from individually addressable ITO electrodes on glass by application of a reductive potential. Electrochemical stripping of PEG-silane layer from ITO microelectrodes allowed for cell adhesion to take place in a spatially defined fashion, with cellular patterns corresponding closely to electrode patterns.

The ability to exercise precise spatial and temporal control over cell-surface interactions is an important prerequisite to the assembly of multi-cellular ...

patterning-cells-on-optically-transparent-indium-tin-oxide-electrodes

Research

JoVE Journal

Biology

11.7K ビュー.  University of California, Davis. 非汚染のPEGシラン単分子膜は、還元電位の印加によって、ガラス上に個々にアドレス可能なITO電極から脱着した。電気化学的には、電極パターンに密接に対応する携帯電話のパターンで、空間的に定義された方法で行われているように細胞接着に許可されるITO微小電極からPEG -シラン層の除去。

ビデオ: Patterning Cells on Optically Transparent Indium Tin Oxide Electrodes

Patterning of Embryonic Stem Cells Using the Bio Flip Chip

Cell-cell interactions consisting of diffusible signaling and cell-cell contact (juxtacrine signaling) are important in numerous biological processes such as tumor growth, stem cell differentiation, and stem cell self-renewal. A number of methods currently exist to modulate cell signaling in vitro. One method of modulating the total amount of diffusible signaling is to vary the cell seeding density during culture. Due to the random nature of cell seeding, this results in considerable variation in the actual cell-cell spacing and amount of cell-cell contact, and cannot prescribe the local environment. A more specific approach for modulating cell signaling is to use molecular inhibitors or genetic approaches to knock down specific signaling proteins, but both of these methods are best suited to manipulating small numbers of molecules. Here, we demonstrate a new approach to modulating cell-cell signaling that modulates the local environment of a cluster of cells by placing different numbers of cells at desired locations on a substrate. This method provides a complementary way to control the local diffusible and juxtacrine signaling between cells. Our method makes use of the Bio Flip Chip (BFC), a microfabricated silicone chip containing hundreds-to-thousands of microwells, each sized to hold either a single cell or small numbers of cells. We load the chip with cells simply by pipetting them onto the array of wells and washing unloaded cells off the array. The chip is then flipped onto a substrate, whereby the cells fall out of the wells and onto the substrate, maintaining their patterning. After the cells have attached, the chip can be removed (or left on). This approach to cell patterning is unique in that it: 1) doesn't alter the chemistry of the substrate, thus allowing cells to proliferate and migrate; 2) allows patterning onto any substrate, including tissue-culture polystyrene, glass, matrigel, and even feeder cell layers; and 3) is compatible with traditional microcontact printing, allowing the creation of extracellular matrix islands with cells placed inside those islands. In this video, we demonstrate the patterning of mouse embryonic stem cells onto tissue-culture polystyrene using the BFC.

We demonstrate a simple method for placing cells at desired locations on a substrate. This method patterns cells by flipping a silicone chip containing microwells filled with cells onto the substrate. This method provides a new way to modulate diffusible and juxtacrine signaling between cells.

Cell-cell interactions consisting of diffusible signaling and cell-cell contact (juxtacrine signaling) are important in numerous biological processes such ...

Making Patch-pipettes and Sharp Electrodes with a Programmable Puller

Glass microelectrodes (also called pipettes) have been a workhorse of electrophysiology for decades. Today, such pipettes are made from glass capillaries using a programmable puller. Such instruments heat the capillary using either a metal filament or a laser and draw out the glass using gravity, a motor or both. Pipettes for patch-clamp recording are formed using only heat and gravity, while sharp electrodes for intracellular recording use a combination of heat, gravity, and a motor. The procedure used to make intracellular recording pipettes is similar to that used to make injection needles for a variety of applications, including cRNA injection into Xenopus oocytes. In general, capillary glass &lt;1.2 mm in diameter is used to make pipettes for patch clamp recording, while narrower glass is used for intracellular recording (outer diameter = 1.0 mm). For each tool, the puller is programmed slightly differently. This video shows how to make both kinds of recording pipettes using pre-established puller programs.

This video shows how to use a programmable puller to make patch pipettes and sharp electrodes for electrophysiology. The same procedure can be used to make a variety of glass tools, including injection needles.

Glass microelectrodes (also called pipettes) have been a workhorse of electrophysiology for decades.  Today, such pipettes are made from glass capillaries ...

Fabrication of Amperometric Electrodes

Carbon fiber electrodes are crucial for the detection of catecholamine release from vesicles in single cells for amperometry measurements.  Here, we describe the techniques needed to generate low noise (&lt;0.5 pA) electrodes.  The techniques have been modified from published descriptions by previous researchers (1,2).  Electrodes are made by preparing carbon fibers and threading them individually into each capillary tube by using a vacuum with a filter to aspirate the fiber.  Next, the capillary tube with fiber is pulled by an electrode puller, creating two halves, each with a fine-pointed tip.  The electrodes are dipped in hot, liquid epoxy mixed with hardener to create an epoxy-glass seal.  Lastly, the electrodes are placed in an oven to cure the epoxy.  Careful handling of the electrodes is critical to ensure that they are made consistently and without damage.  This protocol shows how to fabricate and cut amperometric electrodes for recording from single cells.

This protocol describes how to generate carbon fiber electrodes. The electrodes are subsequently used to detect catecholamine release from vesicles with carbon fiber amperometry.

Carbon fiber electrodes are crucial for the detection of catecholamine release from vesicles in single cells for amperometry measurements.  Here, we ...

Antifouling Self-assembled Monolayers on Microelectrodes for Patterning Biomolecules

We present a procedure for forming a poly(ethylene glycol) (PEG) trimethoxysilane self-assembled monolayer (SAM) on a silicon substrate with gold microelectrodes. The PEG-SAM is formed in a single assembly step and prevents biofouling on silicon and gold surfaces. The SAM is used to coat microelectrodes patterned with standard, positive-tone lithography. Using the microtubule as an example, we apply a DC voltage to induce electrophoretic migration to the SAM-coated electrode in a reversible manner. A flow chamber is used for imaging the electrophoretic migration and microtubule patterning in situ using epifluorescence microscopy. This method is generally applicable to biomolecule patterning, as it employs electrophoresis to immobilize target molecules and thus does not require specific molecular interactions. Further, it avoids problems encountered when attempting to pattern the SAM molecules directly using lithographic techniques. The compatibility with electron beam lithography allows this method to be used to pattern biomolecules at the nanoscale.

We present a procedure for forming a poly(ethylene glycol) self-assembled monolayer (PEG-SAM) on a silicon substrate with gold microelectrodes. The PEG-SAM is formed in a single step and prevents biofouling on silicon and gold surfaces. Electrophoresis is then used for patterning biomolecules down to the nanoscale.

We present a procedure for forming a poly(ethylene glycol) (PEG) trimethoxysilane self-assembled monolayer (SAM) on a silicon substrate with gold ...

Analyzing the Function of Small GTPases by Microinjection of Plasmids into Polarized Epithelial Cells

Epithelial cells polarize their plasma membrane into biochemically and functionally distinct apical and basolateral domains where the apical domain faces the 'free' surfaces and the basolateral membrane is in contact with the substrate and neighboring cells. Both membrane domains are separated by tight junctions, which form a diffusion barrier. Apical-basolateral polarization can be recapitulated successfully in culture when epithelial cells such as Madin-Darby Canine Kidney (MDCK) cells are seeded at high density on polycarbonate filters and cultured for several days 1 2. Establishment and maintenance of cell polarity is regulated by an array of small GTPases of the Ras superfamily such as RalA, Cdc42, Rab8, Rab10 and Rab13 3 4 5 6 7. Like all GTPases these proteins cycle between an inactive GDP-bound state and an active GTP-bound state. Specific mutations in the nucleotide binding regions interfere with this cycling 8. For example, Rab13T22N is permanently locked in the GDP-form and thus dubbed 'dominant negative', whereas Rab13Q67L can no longer hydrolyze GTP and is thus locked in a 'dominant active' state 7. To analyze their function in cells both dominant negative and dominant active alleles of GTPases are typically expressed at high levels to interfere with the function of the endogenous proteins 9. An elegant way to achieve high levels of overexpression in a short amount of time is to introduce the plasmids encoding the relevant proteins directly into the nuclei of polarized cells grown on filter supports using microinjection technique. This is often combined with the co-injection of reporter plasmids that encode plasma membrane receptors that are specifically sorted to the apical or basolateral domain. A cargo frequently used to analyze cargo sorting to the basolateral domain is a temperature sensitive allele of the vesicular stomatitis virus glycoprotein (VSVGts045) 10. This protein cannot fold properly at 39&deg;C and will thus be retained in the endoplasmic reticulum (ER) while the regulatory protein of interest is assembled in the cytosol. A shift to 31&deg;C will then allow VSVGts045 to fold properly, leave the ER and travel to the plasma membrane 11. This chase is typically performed in the presence of cycloheximide to prevent further protein synthesis leading to cleaner results. Here we describe in detail the procedure of microinjecting plasmids into polarized cells and subsequent incubations including temperature shifts that allow a comprehensive analysis of regulatory proteins involved in basolateral sorting.

This article details the procedures involved in overexpression and analysis of small GTPases in polarized epithelial cells using microinjection technique.

Epithelial cells polarize their plasma membrane into biochemically and functionally distinct apical and basolateral domains where the apical domain faces ...

Detection of Nitric Oxide and Superoxide Radical Anion by Electron Paramagnetic Resonance Spectroscopy from Cells using Spin Traps

Reactive nitrogen/oxygen species (ROS/RNS) at low concentrations play an important role in regulating cell function, signaling, and immune response but in unregulated concentrations are detrimental to cell viability1, 2. While living systems have evolved with endogenous and dietary antioxidant defense mechanisms to regulate ROS generation, ROS are produced continuously as natural by-products of normal metabolism of oxygen and can cause oxidative damage to biomolecules resulting in loss of protein function, DNA cleavage, or lipid peroxidation3, and ultimately to oxidative stress leading to cell injury or death4. 
Superoxide radical anion (O2&bull;-) is the major precursor of some of the most highly oxidizing species known to exist in biological systems such as peroxynitrite and hydroxyl radical. The generation of O2&bull;- signals the first sign of oxidative burst, and therefore, its detection and/or sequestration in biological systems is important. In this demonstration, O2&bull;- was generated from polymorphonuclear neutrophils (PMNs). Through chemotactic stimulation with phorbol-12-myristate-13-acetate (PMA), PMN generates O2&bull;- via activation of nicotinamide adenine dinucleotide phosphate (NADPH) oxidase5. 
Nitric oxide (NO) synthase which comes in three isoforms, as inducible-, neuronal- and endothelial-NOS, or iNOS, nNOS or eNOS, respectively, catalyzes the conversion of L- arginine to L-citrulline, using NADPH to produce NO6. Here, we generated NO from endothelial cells. Under oxidative stress conditions, eNOS for example can switch from producing NO to O2&bull;- in a process called uncoupling, which is believed to be caused by oxidation of heme7 or the co-factor, tetrahydrobiopterin (BH4)8.
There are only few reliable methods for the detection of free radicals in biological systems but are limited by specificity and sensitivity. Spin trapping is commonly used for the identification of free radicals and involves the addition reaction of a radical to a spin trap forming a persistent spin adduct which can be detected by electron paramagnetic resonance (EPR) spectroscopy. The various radical adducts exhibit distinctive spectrum which can be used to identify the radicals being generated and can provide a wealth of information about the nature and kinetics of radical production9.
The cyclic nitrones, 5,5-dimethyl-pyrroline-N-oxide, DMPO10, the phosphoryl-substituted DEPMPO11, and the ester-substituted, EMPO12 and BMPO13, have been widely employed as spin traps--the latter spin traps exhibiting longer half-lives for O2&bull;- adduct. Iron (II)-N-methyl-D-glucamine dithiocarbamate, Fe(MGD)2 is commonly used to trap NO due to high rate of adduct formation and the high stability of the spin adduct14.

Electron paramagnetic resonance (EPR) spectroscopy was employed to detect nitric oxide from bovine aortic endothelial cells and superoxide radical anion from human neutrophils using iron (II)-N-methyl-D-glucamine dithiocarbamate, Fe(MGD)2 and 5,5-dimethyl-1-pyroroline-N-oxide, DMPO, respectively.

Reactive nitrogen/oxygen species (ROS/RNS) at low concentrations play an important role in regulating cell function, signaling, and immune response but in ...

Visualization of Mitochondrial Respiratory Function using Cytochrome C Oxidase / Succinate Dehydrogenase (COX/SDH) Double-labeling Histochemistry

Mitochondrial DNA (mtDNA) defects are an important cause of disease and may underlie aging and aging-related alterations 1,2. The mitochondrial theory of aging suggests a role for mtDNA mutations, which can alter bioenergetics homeostasis and cellular function, in the aging process 3. A wealth of evidence has been compiled in support of this theory 1,4, an example being the mtDNA mutator mouse 5; however, the precise role of mtDNA damage in aging is not entirely understood 6,7.
Observing the activity of respiratory enzymes is a straightforward approach for investigating mitochondrial dysfunction. Complex IV, or cytochrome c oxidase (COX), is essential for mitochondrial function. The catalytic subunits of COX are encoded by mtDNA and are essential for assembly of the complex (Figure 1). Thus, proper synthesis and function are largely based on mtDNA integrity 2. Although other respiratory complexes could be investigated, Complexes IV and II are the most amenable to histochemical examination 8,9. Complex II, or succinate dehydrogenase (SDH), is entirely encoded by nuclear DNA (Figure 1), and its activity is typically not affected by impaired mtDNA, although an increase might indicate mitochondrial biogenesis 10-12. The impaired mtDNA observed in mitochondrial diseases, aging, and age-related diseases often leads to the presence of cells with low or absent COX activity 2,12-14. Although COX and SDH activities can be investigated individually, the sequential double-labeling method 15,16 has proved to be advantageous in locating cells with mitochondrial dysfunction 12,17-21.
Many of the optimal constitutions of the assay have been determined, such as substrate concentration, electron acceptors/donors, intermediate electron carriers, influence of pH, and reaction time 9,22,23. 3,3'-diaminobenzidine (DAB) is an effective and reliable electron donor 22. In cells with functioning COX, the brown indamine polymer product will localize in mitochondrial cristae and saturate cells 22. Those cells with dysfunctional COX will therefore not be saturated by the DAB product, allowing for the visualization of SDH activity by reduction of nitroblue tetrazolium (NBT), an electron acceptor, to a blue formazan end product 9,24. Cytochrome c and sodium succinate substrates are added to normalize endogenous levels between control and diseased/mutant tissues 9. Catalase is added as a precaution to avoid possible contaminating reactions from peroxidase activity 9,22. Phenazine methosulfate (PMS), an intermediate electron carrier, is used in conjunction with sodium azide, a respiratory chain inhibitor, to increase the formation of the final reaction products 9,25. Despite this information, some critical details affecting the result of this seemly straightforward assay, in addition to specificity controls and advances in the technique, have not yet been presented.

Visualization of Mitochondrial Respiratory Function using Cytochrome C Oxidase / Succinate Dehydrogenase COX/SDH Double-labeling Histochemistry

The cytochrome c oxidase/sodium dehydrogenase (COX/SDH) double-labeling method allows for direct visualization of mitochondrial respiratory enzyme deficiencies in fresh-frozen tissue sections. This is a straightforward histochemical technique and is useful in investigating mitochondrial diseases, aging, and aging-related disorders.

Mitochondrial DNA (mtDNA) defects are an important cause of disease and may underlie aging and aging-related alterations 1,2. The mitochondrial theory of ...

Induction and Analysis of Epithelial to Mesenchymal Transition

Epithelial to mesenchymal transition (EMT) is essential for proper morphogenesis during development. Misregulation of this process has been implicated as a key event in fibrosis and the progression of carcinomas to a metastatic state. Understanding the processes that underlie EMT is imperative for the early diagnosis and clinical control of these disease states. Reliable induction of EMT in vitro is a useful tool for drug discovery as well as to identify common gene expression signatures for diagnostic purposes. Here we demonstrate a straightforward method for the induction of EMT in a variety of cell types. Methods for the analysis of cells pre- and post-EMT induction by immunocytochemistry are also included. Additionally, we demonstrate the effectiveness of this method through antibody-based array analysis and migration/invasion assays.

A straightforward method is described for the induction of epithelial to mesenchymal transition (EMT) in a variety of cell types. Methods for the analysis of cells in EMT states by immunocytochemistry are included.

Epithelial  to mesenchymal transition (EMT) is essential for proper morphogenesis during  development. Misregulation of this  process has been implicated ...

A Functional Assay for Gap Junctional Examination; Electroporation of Adherent Cells on Indium-Tin Oxide

In this technique, cells are cultured on a glass slide that is partly coated with indium-tin oxide (ITO), a transparent, electrically conductive material. A variety of molecules, such as peptides or oligonucleotides can be introduced into essentially 100% of the cells in a non-traumatic manner.&#160; Here, we describe how it can be used to study intercellular, gap junctional communication. Lucifer yellow penetrates into the cells when an electric pulse, applied to the conductive surface on which they are growing, causes pores to form through the cell membrane. This is electroporation. Cells growing on the nonconductive&#160;glass surface immediately adjacent to the electroporated region do not take up Lucifer yellow by electroporation but do acquire the fluorescent dye as it is passed to them via gap junctions that link them to the electroporated cells. The results of the transfer of dye from cell to cell can be observed microscopically under fluorescence illumination. This technique allows for precise quantitation of gap junctional communication. In addition, it can be used for the introduction of peptides or other non-permeant molecules, and the transfer of small electroporated peptides via gap junctions to inhibit the signal in the adjacent, non-electroporated cells is a powerful demonstration of signal inhibition.

This presentation demonstrates a method whereby electroporation of adherent, cultured cells is used for the study of intercellular, junctional communication, while the cells grow on a slide coated with conductive and transparent indium-tin oxide.

In this technique, cells are cultured on a glass slide that is partly coated with indium-tin oxide (ITO), a transparent, electrically conductive material. ...

Application of Genetically Encoded Fluorescent Nitric Oxide (NO&#8226;) Probes, the geNOps, for Real-time Imaging of NO&#8226; Signals in Single Cells

Nitric Oxide (NO&#8226;) is a small radical, which mediates multiple important cellular functions in mammals, bacteria and plants. Despite the existence of a large number of methods for detecting NO&#8226; in vivo and in vitro, the real-time monitoring of NO&#8226; at the single-cell level is very challenging. The physiological or pathological effects of NO&#8226; are determined by the actual concentration and dwell time of this radical. Accordingly, methods that allow the single-cell detection of NO&#8226; are highly desirable. Recently, we expanded the pallet of NO&#8226; indicators by introducing single fluorescent protein-based genetically encoded nitric oxide (NO&#8226;) probes (geNOps) that directly respond to cellular NO&#8226; fluctuations and, hence, addresses this need. Here we demonstrate the usage of geNOps to assess intracellular NO&#8226; signals in response to two different chemical NO&#8226;-liberating molecules. Our results also confirm that freshly prepared 3-(2-hydroxy-1-methyl-2-nitrosohydrazino)-N-methyl-1-propanamine (NOC-7) has a much higher potential to evoke change in intracellular NO&#8226; levels as compared with the inorganic NO&#8226; donor sodium nitroprusside (SNP). Furthermore, dual-color live-cell imaging using the green geNOps (G-geNOp) and the chemical Ca2+ indicator fura-2 was performed to visualize the tight regulation of Ca2+-dependent NO&#8226; formation in single endothelial cells. These representative experiments demonstrate that geNOps are suitable tools to investigate the real-time generation and degradation of single-cell NO&#8226; signals in diverse experimental setups.

Application of Genetically Encoded Fluorescent Nitric Oxide (NO&amp;#8226;) Probes, the geNOps, for Real-time Imaging of NO&amp;#8226; Signals in Single Cells

This manuscript presents protocols for the application of novel genetically encoded nitric oxide (NO&#8226;) probes (geNOps) to monitor single cell NO&#8226; fluctuations in real-time using fluorescence microscopy. The Ca2+-triggered NO&#8226; formation on the level of individual endothelial cells was visualized by combining geNOps with a chemical Ca2+ sensor.

Nitric Oxide (NO&#8226;) is a small radical, which mediates multiple important cellular functions in mammals, bacteria and plants. Despite the existence ...