This work was supported by the German Science Foundation within the Priority Program (SPP1708) &#34;Material Synthesis near Room Temperature&#34; (projects BE 2243/3-1 and BE 2243/3-2). We further acknowledge Hermann K&#246;hler for experimental assistance as well as Dr. Christian K&#252;bel and Wu Wang for support with electron microscopy studies.

CAUTION: Please consult all relevant material safety data sheets before use. Several of the chemicals used in these syntheses are acutely toxic and carcinogenic. Nanomaterials may have additional hazards compared to their bulk counterpart. Please use all appropriate safety practices when performing a synthetic reaction including the use of engineering controls (fume hood, glove box) and personal protective equipment (safety glasses, gloves, lab coat, full length pants, closed-toe shoes). The following procedures involve standard, air-free handling Schlenk techniques using argon as an inert gas or the use of an anoxic glove box. Assemble all glass-to-glass joints carefully with Teflon ring seals or vacuum grease to avoid contact with air. Inspect all glassware for defects prior to use. Triethylborane is a pyrophoric liquid which burns in contact with air. Please take care of appropriate safety practices and handle in air-free conditions. Please employ all appropriate safety practices for the use of hydrogen and any equipment (autoclaves, gas burettes) under high pressure.
1. Preparation of the Reducing Agent
<ol>
	<li>Preparation of potassium triethylborohydride (K[BEt3H])
	<ol>
		<li>Suspend 34.5 g (0.873 mol) of potassium hydride in 400 mL of anhydrous tetrahydrofurane in a 1000 mL 3-neck round bottom Schlenk flask under argon atmosphere by using the Schlenk line and heat the flask to 50 &#176;C while stirring with a stir bar.</li>
		<li>With a syringe, add the 100 mL (0.71 mol) of triethylborane drop-wise (~1 drop/s) to the stirring suspension of potassium hydride in tetrahydrofurane.</li>
		<li>Cool the reaction mixture to -40 &#176;C and remove any excess of potassium hydride by filtration.</li>
		<li>Receive potassium triethylborohydride as a clear, colorless solution in tetrahydrofurane.</li>
	</ol>
	</li>
	<li>Preparation of methyltrioctylammonium triethylborohydride ([OMA][BEt3H])
	<ol>
		<li>Under argon atmosphere, dissolve 50 g (0.11 mol) of methyltrioctylammonium bromide in 100 mL of anhydrous tetrahydrofurane in a 500 mL 2-neck round bottom flask.</li>
		<li>At room temperature, add 100 mL of K[BEt3H] solution (1.5 M in tetrahydrofurane) to the solution of trioctylmethylammonium bromide in tetrahydrofurane.</li>
		<li>Stir for 3 h at room temperature with a stir bar, then cool to -40 &#176;C overnight.</li>
		<li>Remove potassium bromide via filtration of the cooled solution.</li>
		<li>Receive [OMA][BEt3H] as a clear solution in tetrahydrofurane.</li>
	</ol>
	</li>
</ol>
2. Treatment of Methyltrioctylammonium Bis(trifluoromethylsulfonyl)imide ([OMA][NTf2])
<ol>
	<li>Prior to use, dry and degas the [OMA][NTf2] in vacuum (10-3 mbar) at 70 &#176;C for 3 h and in vacuum (10-4 mbar) at room temperature for another 16 h.</li>
</ol>
3. Synthesis of Pt/Sn-based Nanoparticles
<ol>
	<li>Synthesis of Pt/Sn-based nanocrystals
	<ol>
		<li>In argon atmosphere, combine a total of 0.25 mmol of the two metal salt precursors. Adjust the molar ratio of the Pt2+ and Sn2+ precursors to 1:1 and 3:1 to achieve random alloy nanoparticles with different compositions:
		<ol>
			<li>For the synthesis of Pt/Sn nanoparticles (1:1 molar ratio of Pt:Sn precursor), suspend 33.2 mg of PtCl2 and 29.6 mg of Sn(ac)2 (or 23.7 mg of SnCl2, accordingly) in 4 mL of [OMA][NTf2] in a 100 mL Schlenk flask and stir with a stir bar at 60-80 &#176;C for 2-3 h under the vacuum line.</li>
			<li>For the synthesis of Pt/Sn samples (3:1 molar ratio of Pt:Sn precursor), suspend 49.9 mg of PtCl2 with 14.8 mg of Sn(ac)2 (or 11.9 mg of SnCl2, accordingly) in 4 mL of [OMA][NTf2] in a 100 mL Schlenk flask and stir with a stir bar at 60-80 &#176;C for 2-3 h under the vacuum line.</li>
		</ol>
		</li>
		<li>Place the suspension in an ultrasonic bath at room temperature for 1-2 h.</li>
		<li>At 60-80 &#176;C, rapidly inject 3 mL of [OMA][BEt3H] solution (1.23 M in tetrahydrofurane) with a 3 mL syringe to the metal salt precursors in [OMA][NTf2] whilst vigorously stirring. The rapid injection creates a sharp nucleation event, promoting a small size and narrow size distribution. Let the reaction proceed while stirring at 60-80 &#176;C for 2-3 h.</li>
		<li>Cool to room temperature and remove any volatile compounds in vacuum during a period of 0.5 h.</li>
		<li>Obtain the Pt/Sn-based particles as a highly stable colloidal sol in [OMA][NTf2].</li>
	</ol>
	</li>
	<li>Isolation of Pt/Sn-based nanocrystals
	<ol>
		<li>Precipitation of Pt/Sn-based nanocrystals
		<ol>
			<li>Add 3 mL of anhydrous acetonitrile or tetrahydrofurane to the solution to flocculate the nanocrystals. Transfer the suspension to a vial in the glove box, close the vial with a cap, and centrifuge for 15 min (4226 x g).</li>
			<li>Decant the solution. Discard the supernatant and wash the precipitate with anhydrous acetonitrile or tetrahydrofurane.</li>
			<li>Obtain the particles as a sticky powder containing the Pt/Sn nanoparticles in addition to some residual IL.</li>
			<li>Confirm the crystal structure and composition of the Pt/Sn-based nanocrystals by XRD analysis. A shift of the reflections towards lower Bragg angles indicates alloying of the platinum nanoparticles with tin. Estimate the particle size from XRD patterns with the Scherrer equation according to the following formula 
			<img alt="Equation 1" src="/files/ftp_upload/58058/58058eq1v3.jpg" /> 
			where Lhkl is the diameter (nm) of the Pd/Sn nanocrystal perpendicular to hkl, &#955; the wavelength (nm) (typically Cu K&#945; 0.154 nm), &#946; the peak width at half maximum, and&#160;&#952; the Bragg angle.</li>
			<li>Determine the metal content and the composition by ICP-AES. 
			NOTE: The composition of the particles can be tuned by changing both the nature of the metal precursors and the platinum to tin precursor ratio. Pt/Sn-based nanoparticles synthesized from platinum(II) chloride (PtCl2) and tin(II) acetate (Sn(ac)2) (Pt:Sn precursor ratio of 3:1 or 1:1), yield random alloy-type Pt/Sn nanoparticles. See reference for details [C. Dietrich, D. Schild, W. Wang, C. K&#252;bel, S. Behrens, Z. Anorg. Allg. Chem. 2017, 643, 120-129]25.</li>
		</ol>
		</li>
		<li>Extraction of Pt/Sn-based nanocrystals 
		NOTE: To transfer the nanoparticles from the IL into a conventional organic solvent (i.e., n-hexane), add 2 mL N-oleylsarcosine (10 wt.-% in hexane) and 2 mL of acetonitrile to 1 mL of the nanoparticle sol in the IL.
		<ol>
			<li>Add 2 mL N-oleylesarcosine in n-hexane (10 wt.-%) and 1 mL of anhydrous acetonitrile to the nanoparticle/IL sol to extract the nanocrystals in n-hexane. After shaking, monitor the phase transfer visually by both the decolorization of the IL phase and a black coloring of the n-hexane phase.</li>
			<li>Deposit a drop of the solution on a carbon-covered copper grid and analyze by transmission electron microscopy.</li>
		</ol>
		</li>
	</ol>
	</li>
</ol>
4. Catalytic Testing
NOTE: For catalytic testing, use a semi-continuous autoclave reactor with a reactor equipped with a Teflon liner, a mechanical blowing stirrer (Teflon) and baffles (stainless steel) to achieve intimate mixing between the gas and the liquid phase, a thermocouple and a heating bath.
<ol>
	<li>Selective hydrogenation of &#945;,&#946;-unsaturated aldehydes
	<ol>
		<li>Add 2.2 mg (17 mmol) of cinnaic aldehyde (CAL) in 30 mL of anhydrous tetrahydrofurane under inert gas.</li>
		<li>In the anoxic glove box, combine with 1 mL of the nanoparticle solution.</li>
		<li>Place the reactor in the heating bath and pressurize with hydrogen. During catalytic experiments, keep the hydrogen pressure constant at 10 bar, while hydrogen is continuously supplied to the reactor via a 500 mL gas burette.</li>
		<li>Raise the temperature to 80 &#176;C. At 80&#176;C, start to stir using a blowing stirrer (1200 rpm). Load the reactor with hydrogen to start the reaction.</li>
		<li>Record the hydrogen consumption continuously based on the pressure drop in the gas burette. To determine catalytic activity and selectivity, take aliquots every 30 min.</li>
		<li>Analyze the reaction products by gas chromatography using a column (30m x 0.25mm, 0.25&#181;m film thickness).</li>
		<li>Calculate the turn over frequency (TOF), product selectivity (SCAOL [%]), and cinnamic alcohol (CAOL) yield ([%]) according to the following formulas 
		<img alt="Equation" src="/files/ftp_upload/58058/58058eq3v3.jpg" /> 
		&#160; &#160; 
		<img alt="Equation" src="/files/ftp_upload/58058/58058eq4v2.jpg" /> 
		&#160; &#160; 
		<img alt="Equation" src="/files/ftp_upload/58058/58058eq5v2.jpg" /> 
		where t is the reaction time (h), n0,CAL the initial amount of CAL (mol), nmetal/catalyst the amount of metal catalyst (mol), and Xt,CAL the conversion of CAL at time t (%). [CAOL], [HCAOL] and [HCAL] refer to the concentrations of cinnamic alcohol, hydrocinnamic alcohol and hydrocinnamic aldehyde (see reaction scheme Figure 2), respectively. 
		NOTE: For more details, also see reference 25.</li>
	</ol>
	</li>
</ol>

<ol>
	<li>Dupont, J., Scholten, J. D. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=On+the+structural+and+surface+properties+of+transition-metal+nanoparticles+in+ionic+liquids.">On the structural and surface properties of transition-metal nanoparticles in ionic liquids.</a> Chemical Society Reviews. 39 (5), 1780-1804 (2010).</li><li>Vollmer, C., Janiak, C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Naked+metal+nanoparticles+from+metal+carbonyls+in+ionic+liquids:+Easy+synthesis+and+stabilization.">Naked metal nanoparticles from metal carbonyls in ionic liquids: Easy synthesis and stabilization.</a> Coordination Chemistry Reviews. 255 (17-18), 2039-2057 (2011).</li><li>Behrens, S., Essig, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=A+facile+procedure+for+magnetic+fluids+using+room+temperature+ionic+liquids.">A facile procedure for magnetic fluids using room temperature ionic liquids.</a> Journal of Materials Chemistry. 22 (9), 3811-3816 (2012).</li><li>Essig, S., Behrens, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Ionic+liquids+as+size-+and+shape-regulating+solvents+for+the+synthesis+of+cobalt+nanoparticles.">Ionic liquids as size- and shape-regulating solvents for the synthesis of cobalt nanoparticles.</a> Chemie Ingenieur Technik. 87 (12), 1741-1747 (2015).</li><li>Liu, X., Wang, D., Li, Y. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Synthesis+and+catalytic+properties+of+bimetallic+nanomaterials+with+various+architectures.">Synthesis and catalytic properties of bimetallic nanomaterials with various architectures.</a> Nano Today. 7, 448-466 (2012).</li><li>Armbr&#252;ster, M. K., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Al13Fe4+as+a+low-cost+alternative+for+palladium+in+heterogeneous+hydrogenation.">Al13Fe4 as a low-cost alternative for palladium in heterogeneous hydrogenation.</a> Nature Materials. 11, 690-692 (2012).</li><li>Luo, Y., Alarc&#243;n Villaseca, S., Friedrich, M., Teschner, D., Knop-Gericke, A., Armbr&#252;ster, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Addressing+electronic+effects+in+the+semi-hydrogenation+of+ethyne+by+InPd2+and+intermetallic+Ga-Pd+compounds.">Addressing electronic effects in the semi-hydrogenation of ethyne by InPd2 and intermetallic Ga-Pd compounds.</a> Journal of Catalysis. 338, 265-272 (2016).</li><li>Egeberg, A., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Bimetallic+nickel-iridium+and+nickel-osmium+alloy+nanoparticles+and+their+catalytic+performance+in+hydrogenation+Reactions.">Bimetallic nickel-iridium and nickel-osmium alloy nanoparticles and their catalytic performance in hydrogenation Reactions.</a> ChemCatChem. 9, 3534-3543 (2017).</li><li>Rai, R., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Access+to+highly+active+Ni-Pd+bimetallic+nanoparticle+catalysts+for+C-C+coupling+reactions.">Access to highly active Ni-Pd bimetallic nanoparticle catalysts for C-C coupling reactions.</a> Catalysis Science &amp; Technoly. 6, 5567-5579 (2016).</li><li>Rai, R., Gupta, K., Behrens, S., Li, J., Xu, Q., Singh, S. K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Highly+active+bimetallic+nickel-palladium+alloy+nanoparticle+catalyzed+Suzuki-Miyaura+reactions.">Highly active bimetallic nickel-palladium alloy nanoparticle catalyzed Suzuki-Miyaura reactions.</a> ChemCatChem. 7, 1806-1812 (2015).</li><li>Singh, S. K., Yadav, M., Behrens, S., Roesky, P. W. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Au-based+bimetallic+nanoparticles+for+the+intramolecular+aminoalkene+hydroamination.">Au-based bimetallic nanoparticles for the intramolecular aminoalkene hydroamination.</a> Dalton Transactions. 42, 10404-10408 (2013).</li><li>Arquilli&#232;re, P., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Bimetallic+Ru-Cu+nanoparticles+synthesized+in+ionic+liquids:+Kinetically+controlled+size+and+structure.">Bimetallic Ru-Cu nanoparticles synthesized in ionic liquids: Kinetically controlled size and structure.</a> Topics in Catalysis. 56, 1-7 (2013).</li><li>Helgadottir, I., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Ru-core/Cu-shell+bimetallic+nanoparticles+with+controlled+size+formed+in+one-pot+synthesis.">Ru-core/Cu-shell bimetallic nanoparticles with controlled size formed in one-pot synthesis.</a> Nanoscale. 6, 14856-14862 (2014).</li><li>Dash, P., Miller, S. M., Scott, R. W. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Stabilizing+nanoparticle+catalysts+in+imidazolium-based+ionic+liquids:+A+comparative+study.">Stabilizing nanoparticle catalysts in imidazolium-based ionic liquids: A comparative study.</a> Journal of Molecular Catalysis A. 329, 86-95 (2010).</li><li>Schutte, K., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Colloidal+nickel/gallium+nanoalloys+obtained+from+organometallic+precursors+in+conventional+organic+solvents+and+in+ionic+liquids:+noble-metal-free+alkyne+semihydrogenation+catalysts.">Colloidal nickel/gallium nanoalloys obtained from organometallic precursors in conventional organic solvents and in ionic liquids: noble-metal-free alkyne semihydrogenation catalysts.</a> Nanoscale. 6, 5532-5544 (2014).</li><li>Schutte, K., Meyer, H., Gemel, C., Barthel, J., Fischer, R. A., Janiak, C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Synthesis+of+Cu,+Zn+and+Cu/Zn+brass+alloy+nanoparticles+from+metal+amidinate+precursors+in+ionic+liquids+or+propylene+carbonate+with+relevance+to+methanol+synthesis.">Synthesis of Cu, Zn and Cu/Zn brass alloy nanoparticles from metal amidinate precursors in ionic liquids or propylene carbonate with relevance to methanol synthesis.</a> Nanoscale. 6, 3116-3126 (2014).</li><li>Wang, X., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Pt/Sn+Intermetallic,+Core/Shell+and+Alloy+Nanoparticles:+Colloidal+Synthesis+and+Structural+Control.">Pt/Sn Intermetallic, Core/Shell and Alloy Nanoparticles: Colloidal Synthesis and Structural Control.</a> Chemistry of Materials. 25, 1400-1407 (2013).</li><li>Marcos Esteban, R., Janiak, C., Prechtl, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Synthesis+and+application+of+metal+nanoparticle+catalysts+in+ionic+liquid+media+using+metal+carbonyl+complexes+as+precursors.">Synthesis and application of metal nanoparticle catalysts in ionic liquid media using metal carbonyl complexes as precursors.</a> Nanocatalysis in Ionic Liquids. , (2016).</li><li>Redel, E., Kr&#228;mer, J., Thomann, R., Janiak, C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Synthesis+of+Co,+Rh+and+Ir+nanoparticles+from+metal+carbonyls+in+ionic+liquids+and+their+use+as+biphasic+liquid-liquid+hydrogenation+nanocatalysts+for+cyclohexene.">Synthesis of Co, Rh and Ir nanoparticles from metal carbonyls in ionic liquids and their use as biphasic liquid-liquid hydrogenation nanocatalysts for cyclohexene.</a> Journal of Organometallic Chemistry. 694, 1069-1075 (2009).</li><li>Venkatesan, R., Prechtl, M. H. G., Scholten, J. D., Pezzi, R. P., Machado, G., Dupont, J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Palladium+nanoparticle+catalysts+in+ionic+liquids:+synthesis,+characterisation+and+selective+partial+hydrogenation+of+alkynes+to+Z-alkenes.">Palladium nanoparticle catalysts in ionic liquids: synthesis, characterisation and selective partial hydrogenation of alkynes to Z-alkenes.</a> Journal of Materials Chemistry. 21, 3030-3036 (2011).</li><li>Konnerth, H., Prechtl, M. H. G. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Selective+partial+hydrogenation+of+alkynes+to+(Z)-alkenes+with+ionic+liquid-doped+nickel+nanocatalysts+at+near+ambient+conditions.">Selective partial hydrogenation of alkynes to (Z)-alkenes with ionic liquid-doped nickel nanocatalysts at near ambient conditions.</a> Chemical Communications. 52, 9129-9132 (2016).</li><li>Gieshoff, T. N., Welther, A., Kessler, M. T., Prechtl, M. H. G. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Stereoselective+iron-catalyzed+alkyne+hydrogenation+in+ionic+liquids.">Stereoselective iron-catalyzed alkyne hydrogenation in ionic liquids.</a> Chem. Comm. 50, 2261-2264 (2014).</li><li>Konnerth, H., Prechtl, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Selective+hydrogenation+of+N-heterocyclic+compounds+using+Ru+nanocatalysts+in+ionic+liquids.">Selective hydrogenation of N-heterocyclic compounds using Ru nanocatalysts in ionic liquids.</a> Green Chemistry. 19, 2762-2767 (2017).</li><li>Beier, M. J., Andanson, J. -. M., Mallat, T., Krumeich, F., Baiker, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Ionic+liquid-supported+Pt+nanoparticles+as+catalysts+for+enantioselective+hydrogenation.">Ionic liquid-supported Pt nanoparticles as catalysts for enantioselective hydrogenation.</a> ACS Catalysis. 2, 337-340 (2012).</li><li>Dietrich, C., Schild, D., Wang, W., K&#252;bel, C., Behrens, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Bimetallic+Pt/Sn-based+nanoparticles+in+ionic+liquids+as+nanocatalysts+for+the+selective+hydrogenation+of+cinnamaldehyde.">Bimetallic Pt/Sn-based nanoparticles in ionic liquids as nanocatalysts for the selective hydrogenation of cinnamaldehyde.</a> Journal of Inorganic and General Chemistry (ZAAC). 643, 120-129 (2017).</li><li>Zhou, W., Liu, L., Li, B., Wu, P., Song, Q. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Structural,+elastic+and+electronic+properties+of+intermetallics+in+the+Pt-Sn+system:+A+density+functional+investigation.">Structural, elastic and electronic properties of intermetallics in the Pt-Sn system: A density functional investigation.</a> Computational Materials Science. 46, 921-931 (2009).</li><li>Gallezot, P., Richard, D. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Selective+hydrogenation+of+&#945;,&#946;-unsaturated+aldehydes.">Selective hydrogenation of &#945;,&#946;-unsaturated aldehydes.</a> Catalysis Reviews Science and Engineering. 40, 81-126 (1998).</li><li>Samant, P., Pereira, M., Figueiredo, J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Mesoporous+carbon+supported+Pt+and+Pt-Sn+catalysts+for+hydrogenation+of+cinnamaldehyde.">Mesoporous carbon supported Pt and Pt-Sn catalysts for hydrogenation of cinnamaldehyde.</a> Catal. Today. 102, 183-188 (2005).</li><li>Rong, H., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Structure+evolution+and+associated+catalytic+properties+of+Pt-Sn+bimetallic+nanoparticles.">Structure evolution and associated catalytic properties of Pt-Sn bimetallic nanoparticles.</a> Chemistry European Journal. 21, 12034-12041 (2015).</li></ol>

We have nothing to disclose.

The metal salt precursors are carefully dissolved in [OMA][NTf2] by stirring the reaction mixture over night, followed by ultrasonication. This is an important step to achieve Pt/Sn nanoparticles of homogeneous composition and sizes. [OMA][BEt3H] (as a solution in tetrahydrofurane) is then rapidly injected with a syringe whilst vigorously stirring the viscous solution. Rapid injection and mixing of the two components is a prerequisite to achieve monodisperse and homogeneous nanoparticles and may limit the scale-up of the procedure. Successful nanoparticle formation may be monitored by the change in color from a yellowish to black solution. During this step, H2 is generated as a side product, and thus, the reduction step has to be performed in an argon stream to avoid pressurization of the reaction vessel. Contact with air and moisture has to be prevented during all steps of nanoparticle synthesis. The Pt/Sn nanoparticles are formed in the IL after the injection of the reducing agent, where IL cation and IL anion control both nucleation and growth processes25. As a result, very small nanoparticles are obtained which form an extraordinarily stable, colloidal sol in [OMA][NTf2]. This synthetic approach does not require the use of additional, strongly coordinating ligands and may be further employed to achieve small nanoparticles of various mono- and bimetallic compositions.
The sols in which the nanoparticles are immobilized in the IL are highly interesting in view of quasi-homogeneous catalytic applications. However, the isolation of the nanoparticles (e.g., for particle characterization) turns out to be quite challenging due to the high colloidal stability in the IL. The particles are isolated as a sticky powder by precipitation with tetrahydrofurane and successive centrifugation. This is a useful step with respect to nanoparticle characterization, e.g., by TEM or XRD analysis. Alternatively, the nanoparticles can be additionally functionalized and extracted to a conventional solvent, after adding a coordinating ligand (i.e., N-oleylsarcosine) in n-hexane and acetonitrile to the IL-based nanoparticle sol. The samples are then further treated like a conventional nanoparticle sol. In general, specific surface properties are typically required with respect to a certain biomedical or technical application of the nanoparticles. Due to the weak coordination of the particles to the surface, ILs can be replaced by other ligands easily. As a consequence, it&#39;s possible to engineer the surface properties based on the specific requirements of the application using the present synthetic procedure. Magnetic fluids based on small, superparamagnetic cobalt nanoparticles, e.g., are prepared in diverse aliphatic or aromatic carrier media (i.e., kerosene, AP201, or Edwards L9) following a similar procedure3,4. After nanoparticle extraction, the IL may be recycled and reused for nanoparticle synthesis.
TEM analysis of the particles is carried out by depositing a thin film of the nanoparticle sol on the TEM grid. Here, the decomposition of the IL in the electron beam and successive contamination of the TEM sample may represent a real challenge to image the small nanoparticles. Alternatively, the precipitated nanoparticles are deposited on the TEM grid and investigated by TEM analysis. In this case, the particles typically form highly aggregated structures. Figure 1a-d displays TEM images of the nanoparticles in the IL showing very small and regular nanoparticles of 2-3 nm diameter. For all samples, TEM-EDX analysis confirms the presence of both tin and platinum in the particles (Figure 1e).
In order to show the alloyed character and the random alloy-type structure of the nanoparticles, X-ray diffraction patterns are collected for the nanoparticle powders. The XRD patterns confirm the face centered cubic (fcc) and random alloy-type structure of the particles (Figure 1f). The random alloy structure is one of the most conventional forms in bimetallic nanoparticles, where the two elements are randomly (or nearly randomly) dispersed in the nanoparticles. For the Pt-Sn system, also the formation of some intermetallic compounds is known (i.e., PtSn, PtSn4, PtSn2, Pt2Sn3, and Pt3Sn)17,26. Ordered intermetallic and disordered random alloy structures may be distinguished by the presence and absence of additional diffraction patterns derived from superlattice structures. The fcc platinum phase has reflections at 40&#176;, 45&#176;, 68&#176;, and 82&#176; (2) corresponding to the (111), (200), (220), and (311) planes. For all Pt/Sn-based nanoparticles, the XRD pattern shows the four characteristic reflections of the fcc platinum phase. As compared to the positions of the reflections of the pure platinum reference, however, the reflections of the Pt/Sn-based nanoparticles are shifted to smaller Bragg angles. This shift to smaller Bragg angles indicates an increase of the lattice parameters by the insertion of the tin atoms into the fcc platinum lattice. In the XRD patterns, the reflections which are characteristic of the atomic ordering in the intermetallic phase (i.e., Pt3Sn) are not observed. This suggests the formation of an alloyed nanoparticle core with a random distribution of platinum and tin. The decrease of the PdCl2 to Sn(ac)2 precursor ratio from 3:1 to 1:1 additionally leads to small SnO2 nanoparticles in close contact to the random alloy-type Pt/Sn nanoparticles. SnO2 is formed by decomposition of the Sn(ac)2 precursor. If Sn(ac)2 is reacted with [OMA][BEt3H] under the same reaction conditions in the absence of the platinum precursor, SnO and SnO2 are obtained as major reaction products. If the Sn(ac)2 is replaced by tin(II)chloride (SnCl2) and reacted with [OMA][BEt3H] in the presence of the platinum precursor (PtCl2), exclusively amorphous particles are formed and no SnO2 is detected. The tin content in the nanoparticle core can be further analyzed if the lattice constants are determined via Rietveld analysis. According to Vegard&#39;s law, the lattice parameters increase linearly between the lattice parameters of the pure Pt nanoparticles (3.914 &#197;) and the Pt3Sn phase (4.004 &#197;). Following this approach, the tin in the crystalline nanoparticle core is calculated to 11% (i.e., for a PtCl2 / Sn(ac)2 precursor ratio of 3:1) and increases to 18 % (i.e., for a PtCl2 / Sn(ac)2 precursor ratio of 1:1). The overall tin content of 21% and 55%, respectively, is determined by ICP-AES analysis and thus, exceeds the amount of tin in the nanoparticle core. The higher overall tin content can be assigned to the additional formation of SnO2 (i.e., approximately 26%) and to some segregation of tin atoms on the nanoparticle surface. X-ray photoelectron spectra further confirm the presence of Pt0/Sn0 (i.e., for a PtCl2 to Sn(ac)2 precursor ratio of 3:1) and Pt0/Sn0 in combination with 20% SnO2 (i.e., for a PtCl2 to Sn(ac)2 precursor ratio of 1:1) in the Pt/Sn-based nanoparticles, which is consistent with the results of XRD analysis25. The peak broadening arises from Scherrer broadening due to finite crystal size. The size of the nanoparticles is calculated using the Scherrer equation for the Pt/Sn-based nanoparticles to 2.4 nm (i.e., Pt:Sn 1:1), 2.5 nm (i.e., Pt:Sn 3:1) and, for the Pt nanoparticle reference, to 2.7 nm, respectively, which is consistent with the results of TEM analysis.
The transformation of &#945;,&#946;-unsaturated aldehydes to unsaturated alcohols via selective hydrogenation is fundamental in catalytic chemistry and a critical step in the production of various fine chemicals25,27. Although thermodynamics favors the formation of the saturated aldehydes, the selectivity towards the formation of the unsaturated alcohols can be significantly increased on bimetallic Pt-based catalysts by tailoring their size, composition and their support material. The incorporation of an electropositive metal (e.g., Sn) into the platinum leads to the electronic modification of the Pt d band which lowers the binding energy for the C=C bond of the unsaturated aldehyde27. The electron-deficient Sn atoms may further act as Lewis acid adsorption sites for the carbonyl group28. Moreover, vacant oxygen sites in SnO2-x patches in close contact to Pt are also demonstrated to promote carbonyl adsorption and its subsequent hydrogenation by atomic hydrogen which is supplied via the nearby platinum sites29. Overall, these examples show that the catalytic performance of bimetallic Pt-based catalysts is governed by a complex set of factors. In this protocol, we use the hydrogenation of cinnamic aldehyde as a model reaction not only to probe the overall catalytic performance of the IL-stabilized nanoparticles but further to elucidate the effect of tin alloying on the activity and selectivity of the Pt nanoparticles. Figure 2 displays possible pathways and major reaction products in the hydrogenation of CAL. At first, the catalytic properties of the Pt reference nanoparticles are tested in the hydrogenation of CAL. In this case, the saturated aldehyde (i.e., HCAL) is obtained as the only reaction product after 3 h of reaction, and the CAL conversion XCAL is 5% (3 h) and 9% (22 h), accordingly. After alloying the Pt with Sn in the bimetallic nanoparticles, the product selectivity is clearly shifted towards the unsaturated alcohol (i.e., CAOL) (Figure 3). The selectivity SCAOL is 100 % (i.e., for particles synthesized by a molar PtCl2/Sn(ac)2 ratio of 1:1), 80 % (i.e., for particles synthesized by a molar PtCl2 / Sn(ac)2 ratio of 3:1), and 83 % (i.e., for particles synthesized by a molar PtCl2 / SnCl2 ratio of 1:1) after 3 h of reaction and thus, further influenced by the actual nanoparticle composition. The TOF decrease from 28 h-1 to 8 h-1 for the particles synthesized by a molar PtCl2 / Sn(ac)2 ratio of 3:1 and 1:1, respectively, and to 7 h-1 for the nanoparticles obtained using SnCl2 instead of Sn(ac)2 with a molar PtCl2/SnCl2 ratio of 1:1, accordingly. The CAL conversion XCAL is 25% (3h) and 84% (22h) for Pt/Sn-based nanoparticles (i.e., molar PtCl2 / Sn(ac)2 ratio 3:1) which leads to the highest yield in CAOL (YCAOL 20% (3 h)) among the nanoparticles investigated in this study. In order to evaluate the overall catalytic performance of the system, both aspects, i.e., catalytic selectivity and activity, need to be taken into account and thus, Pt/Sn nanoparticles prepared with an initial molar PtCl2/Sn(ac)2 ratio of 3:1 clearly outperformed all other Pt- and Pt/Sn-based particles investigated in our study in terms of cinnamic alcohol yield. Thus, the excellent catalytic performance in this case appears to be a consequence of the Sn doping of the Pt nanoparticles balancing activity and selectivity to cinnamic alcohol in the system. It has to be noted that the blank experiment using the same reaction conditions but without nanoparticle catalyst did not show any conversion of cinnamic aldehyde after 22 h of reaction.
We have demonstrated a synthetic procedure for controlling the preparation of small, Pt/Sn-based nanoparticles of random alloy-type structure by exploiting the beneficial physico-chemical properties of ILs. Similar co-precipitation approaches have already been applied to a wide range of bimetallic nanoparticles in conventional solvents, and we expect that the types of both random alloy and intermetallic nanoparticles that can be obtained by this approach will continue to expand. The nanoparticles reveal interesting catalytic properties in the catalytic hydrogenation of cinnamic aldehyde, and a significantly higher selectivity to the &#945;,&#946;-unsaturated cinnamic alcohol is achieved for the Pt/Sn-based nanoparticles.

ILs represent room-temperature molten salts of large organic cations with asymmetric substitution patterns. They are well known for their unusual physico-chemical properties. The IL properties can be tuned by different combinations of IL cations and anions, and by now, a plethora of ILs is commercially available. Recently, scientists started using ILs as reaction media for the synthesis of nanoparticle due to their modular and excellent solvent properties, low vapor pressure, high polarity and a wide electrochemical stability window1,2,3,4.
During the past decade, bimetallic nanoparticles have attracted considerable attention because they show multiple functionalities and prominent catalytic activity, selectivity as well as thermal and/or chemical stability over their monometallic counterparts5,6,7,8,9,10. Due to synergistic effects, modified electronic and/or geometric surface structures, high catalytic activities and selectivities may be achieved for chemical transformations even if one of the constituents is less or even inactive11. Although the controllable synthesis of nanoparticles has developed rapidly over the recent years, there is still a need for more accurate control over nucleation and growth stages for the synthesis of bimetallic nanocrystals. Since different metals are involved in bimetallic nanocrystals, the atomic distribution not only influences the final nanoparticle architecture but also the catalytic properties. The catalytic performance is highly sensitive to the nature of atomic ordering (i.e., random alloys vs intermetallic compound) even if the composition and stoichiometry are exactly identical. It is surprising, that, so far, the attractive properties of ILs are less explored for the controlled synthesis of bimetallic nanocatalysts12,13,14,15,16.
In this protocol, we will show how to exploit the unusual properties of ILs for the synthesis of bimetallic, random alloy-type nanoparticles. Here, very small nanoparticles with uniform sizes can be synthesized without the addition of auxiliary ligands at moderate reaction temperatures. Nucleation and growth processes are directly controlled by IL-inherent, weak cation/anion interactions. Several methods for Pt/Sn-based nanoparticles are known, however, these synthetic protocols typically involve either supports and/or stabilizing agents (i.e., rather strongly coordinating surfactants or ligands)17. Ligands/surfactants adsorbed on the nanoparticle surface may modify or even inhibit catalytic performance and often need to be successively removed (e.g., via thermal treatment) for catalytic application. This protocol yields IL-based nanoparticle sols of extraordinary high colloidal stability without the addition of such strongly coordinating ligands. Nanoparticles stabilized in ILs have revealed interesting properties as quasi-homogenous catalysts in a broad range of catalytic reactions18,19,20,21,22,23,24. In this protocol, the selective hydrogenation of an &#945;,&#946;-unsaturated aldehyde (i.e., cinnamic aldehyde) is described as a model reaction to probe the catalytic performance of the IL-stabilized nanoparticles and the influence of tin alloying on the catalytic activity and selectivity25.
This protocol is intended to elucidate the details of the experimental synthetic procedures and to help new practitioners in the field to avoid many common pitfalls associated with the synthesis of nanoparticles in ILs. The details of materials characterization is included in previous publication25.

<table>
	<tbody>
		<tr>
			<td>Platinum(II) acetate (PtCl2)</td>
			<td>Acros</td>
			<td>ACRO369670010</td>
			<td>99%, anhydrous, toxic</td>
		</tr>
		<tr>
			<td>Tin(II) acetate (Sn(ac)2)</td>
			<td>Strem</td>
			<td>50-1975</td>
			<td>99%</td>
		</tr>
		<tr>
			<td>Tin(II) chloride (SnCl2)</td>
			<td>Sigma Aldrich</td>
			<td>452335</td>
			<td>98%; harmful</td>
		</tr>
		<tr>
			<td>Methyltrioctylammonium 
			bis(trifluoromethylsulfonyl) imide ([OMA][NTf2])</td>
			<td>IoLitec</td>
			<td>IL-0017-HP</td>
			<td>99 %; n.a.; H2O &#60; 100 ppm; halides &#60; 100 ppm</td>
		</tr>
		<tr>
			<td>Tetrahydrofurane</td>
			<td>Sigma Aldrich</td>
			<td>186562</td>
			<td>99.9 %; anhydrous; carcinogenic</td>
		</tr>
		<tr>
			<td>Acetonitrile</td>
			<td>Sigma Aldrich</td>
			<td>271004</td>
			<td>99.8%; anhydrous; harmful</td>
		</tr>
		<tr>
			<td>n-Hexane</td>
			<td>Sigma Aldrich</td>
			<td></td>
			<td>95%, flammable, carcinogenic, toxic</td>
		</tr>
		<tr>
			<td>(Trans)-cinnamaldehyde</td>
			<td>Sigma Aldrich</td>
			<td>14371-10-9</td>
			<td>99%; irritant</td>
		</tr>
		<tr>
			<td>Methyltrioctylammonium bromide</td>
			<td>Sigma Aldrich</td>
			<td>365718</td>
			<td>97%; irritant</td>
		</tr>
		<tr>
			<td>Potassium hydride (KH)</td>
			<td>Sigma Aldrich</td>
			<td>215813</td>
			<td>30 wt.-% dispersion in mineral oil; corrosive</td>
		</tr>
		<tr>
			<td>Triethylborane (B(Et)3)</td>
			<td>Witco</td>
			<td>257192</td>
			<td>95%; toxic, pyrophoric</td>
		</tr>
		<tr>
			<td>N-oleylsarcosine (Korantin-SH)</td>
			<td>BASF</td>
			<td></td>
			<td></td>
		</tr>
		<tr>
			<td>H2</td>
			<td>Air Liquide</td>
			<td></td>
			<td>99.9 %, flammable</td>
		</tr>
	</tbody>
</table>

synthesis of bimetallic pt/sn-based nanoparticles in ionic liquids

We demonstrate a method for the synthesis of bimetallic nanoparticles consisting of Pt and Sn. A synthesis strategy is used in which the particular physico-chemical properties of ionic liquids (ILs) are exploited to control both nucleation and growth processes. The nanoparticles form colloidal sols of very high colloidal stability in the IL, which is particularly interesting in view of their use as quasi-homogeneous catalysts. Procedures for both nanoparticle extraction in conventional solvents and for nanoparticle precipitation are presented. The size, structure and composition of the synthesized nanocrystals are confirmed using inductively coupled plasma atomic emission spectroscopy (ICP-AES), X-ray diffraction analysis (XRD) and transmission electron microscopy (TEM) with energy-dispersive X-ray spectroscopy (EDX). By this, we show that the nanocrystals are random-type alloy and of small (2-3 nm) size. The catalytic activity and selectivity in the hydrogenation of &#945;,&#946;-unsaturated aldehydes is tested in a semi-continuous batch-type reactor. In this context, the bimetallic Pt/Sn-based nanoparticles reveal a high selectivity towards the unsaturated alcohol.

XRD patterns and transmission electron microscopy (TEM) images are collected for the alloyed nanoparticles (Figure 1) and used to identify the size, phase and morphology of the nanostructures. Energy-dispersive X-ray spectroscopy (EDX) and ICP-AES are used to determine the elemental composition of the nanoparticles.
<img alt="Figure 1" class="xfigimg" src="/files/ftp_upload/58058/58058fig1.jpg" /> 
Figure 1. Representative TEM images with particle size distribution of random alloy-type Pt/Sn nanoparticles. The nanoparticles were prepared using platinum(II) chloride and tin(II) acetate precursors (a) in a molar Pt:Sn precursor ratio of 3:1 and (b,c) in a molar Pt:Sn precursor ratio of 1:1 and (d) using platinum(II) chloride and tin(II) chloride precursors in a molar Pt:Sn ratio of 1:1. (e) Representative energy-dispersive X-ray spectrum of the bimetallic Pt/Sn-based particles confirming the presence of both Sn and Pt. (Cu signals originate from the supporting Cu grid). (f) XRD patterns of Pt/Sn-based nanoparticles compared to Pt nanoparticle reference. <a href="https://www.jove.com/files/ftp_upload/58058/58058fig1large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>
<img alt="Figure 2" class="xfigimg" src="/files/ftp_upload/58058/58058fig2.jpg" /> 
Figure 2. Schematic representation of the reaction pathways and major reaction products (i.e., cinnamic alcohol (CAOL), hydrocinnamic aldehyde (HCAL), and hydrocinnamic alcohol (HCAOL)) in the hydrogenation of cinnamic aldehyde (CAL). The selective hydrogenation of the carbonyl bond to the unsaturated alcohol is a critical step in the synthesis of various fine chemicals. By alloying Pt with Sn in Pt/Sn-based nanoparticles, the carbonyl bond may be selectively hydrogenated to yield the unsaturated alcohol (i.e., CAOL) as the main reaction product. <a href="https://www.jove.com/files/ftp_upload/58058/58058fig2large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>
<img alt="Figure 3" class="xfigimg" src="/files/ftp_upload/58058/58058fig3.jpg" /> 
Figure 3. Time course of the conversion and selectivity in the catalytic hydrogenation of cinnamaldehyde (CAL) for the random alloy-type Pt/Sn nanoparticles which are prepared from platinum(II) chloride and tin(II) acetate in a Pt:Sn precursor ratio of (a) 1:1 and (b) 3:1 (reaction conditions: 80 &#176;C, 10 bar H2). Although the CAOL selectivity is lower for nanoparticles with a Pt:Sn precursor ratio of 3:1 (b), the enhanced CAL conversion results in a higher yield in CAOL. <a href="https://www.jove.com/files/ftp_upload/58058/58058fig3large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>

Watch this Scientific Journal Video about Synthesis of Bimetallic Pt/Sn-based Nanoparticles in Ionic Liquids at JoVE.com

Synthesis of Bimetallic Pt/Sn-based Nanoparticles in Ionic Liquids

A protocol for the synthesis of bimetallic nanoparticles in ionic liquids and the procedure of their catalytic testing in the selective hydrogenation of unsaturated aldehydes are described.

We demonstrate a method for the synthesis of bimetallic nanoparticles consisting of Pt and Sn. A synthesis strategy is used in which the particular ...

This method can be used to prepare various mono-and bimetallic nanoparticles with controlled size and shape in a simple, one-part synthesis step in ionic liquids.The main advantage of this technique is that weakly coordinating anions and cations of the ionic liquid directly control nanoparticle nucleation and cross-processes and further provide electrosteric stabilization of the as-formed nanoparticles.Generally, individuals new to this method will struggle, because the experiment has to be experienced in working under air-free conditions.Demonstrating the procedure, will be Yannick Tr

synthesis-of-bimetallic-ptsn-based-nanoparticles-in-ionic-liquids

Research

Education

JoVE Journal

JoVE Core

Chemistry

Molecules, Compounds, and Chemical Equations

SCIENTISTS IN ACTION

8.9K visualizações.  Karlsruhe Institute of Technology (KIT). This method can be used to prepare various mono-and bimetallic nanoparticles with controlled size and shape in a simple, one-part synthesis step in ionic liquids.The main advantage of this technique is that weakly coordinating anions and cations of the ionic liquid directly control nanoparticle nucleation and cross-processes and further provide electrosteric stabilization of the as-formed nanoparticles.Generally, individuals new to this method will struggle, because the experiment has to be e...

Vídeo: Synthesis of Bimetallic Pt/Sn-based Nanoparticles in Ionic Liquids

Reverse Microemulsion-mediated Synthesis of Monometallic and Bimetallic Early Transition Metal Carbide and Nitride Nanoparticles

A reverse microemulsion is used to encapsulate monometallic or bimetallic early transition metal oxide nanoparticles in microporous silica shells. The silica-encapsulated metal oxide nanoparticles are then carburized in a methane/hydrogen atmosphere at temperatures over 800 &#176;C to form silica-encapsulated early transition metal carbide nanoparticles. During the carburization process, the silica shells prevent the sintering of adjacent carbide nanoparticles while also preventing the deposition of excess surface carbon. Alternatively, the silica-encapsulated metal oxide nanoparticles can be nitridized in an ammonia atmosphere at temperatures over 800 &#176;C to form silica-encapsulated early transition metal nitride nanoparticles. By adjusting the reverse microemulsion parameters, the thickness of the silica shells, and the carburization/nitridation conditions, the transition metal carbide or nitride nanoparticles can be tuned to various sizes, compositions, and crystal phases. After carburization or nitridation, the silica shells are then removed using either a room-temperature aqueous ammonium bifluoride solution or a 0.1 to 0.5 M NaOH solution at 40-60 &#176;C. While the silica shells are dissolving, a high surface area support, such as carbon black, can be added to these solutions to obtain supported early transition metal carbide or nitride nanoparticles. If no high surface area support is added, then the nanoparticles can be stored as a nanodispersion or centrifuged to obtain a nanopowder.

A &#8220;removable ceramic coating method&#8221; is presented in visual format for the synthesis of non-sintered and metal-terminated monometallic and bimetallic early transition metal carbide and nitride nanoparticles with tunable sizes and crystal structures.

A reverse microemulsion is used to encapsulate monometallic or bimetallic early transition metal oxide nanoparticles in microporous silica shells. The ...

Highly Stereoselective Synthesis of 1,6-Ketoesters Mediated by Ionic Liquids: A Three-component Reaction Enabling Rapid Access to a New Class of Low Molecular Weight Gelators

In organic chemistry ionic liquids (ILs) have emerged as safe and recyclable reaction solvents. In the presence of a base ILs can be deprotonated to form catalytically active N-Heterocyclic Carbenes (NHCs). Here we have used ILs as precatalysts in the addition of &#945;,&#946;-unsaturated aldehydes to chalcones to form 1,6-ketoesters, incorporating an anti-diphenyl moiety in a highly stereoselective fashion. The reaction has a broad substrate scope and several functional groups and heteroaromatics can be integrated into the ketoester backbone in generally good yields with maintained stereoselectivity. The reaction protocol is robust and scalable. The starting materials are inexpensive and the products can be obtained after simple filtration, avoiding solvent-demanding chromatography. Furthermore, the IL can be recycled up to 5 times without any loss of reactivity. Moreover, the 1,6-ketoester end product is a potent gelator in several hydrocarbon based solvents. The method enables rapid access to and evaluation of a new class of low molecular weight gelators (LMWGs) from recyclable and inexpensive starting materials.

Ionic liquids (ILs) mediate fast, simple and cheap access to 1,6-ketoesters in high diastereoselectivities and good yields. The reaction protocol is robust and the 1,6-ketoesters can be obtained in gram scale after a simple filtration protocol. Moreover, the 1,6-ketoesters are potent gelators in hydrocarbon solvents.

In organic chemistry ionic liquids (ILs) have emerged as safe and recyclable reaction solvents. In the presence of a base ILs can be deprotonated to form ...

Synthesis, Characterization, and Functionalization of Hybrid Au/CdS and Au/ZnS Core/Shell Nanoparticles

Plasmonic nanoparticles are an attractive material for light harvesting applications due to their easily modified surface, high surface area and large extinction coefficients which can be tuned across the visible spectrum. Research into the plasmonic enhancement of optical transitions has become popular, due to the possibility of altering and in some cases improving photo-absorption or emission properties of nearby chromophores such as molecular dyes or quantum dots. The electric field of the plasmon can couple with the excitation dipole of a chromophore, perturbing the electronic states involved in the transition and leading to increased absorption and emission rates. These enhancements can also be negated at close distances by energy transfer mechanism, making the spatial arrangement of the two species critical. Ultimately, enhancement of light harvesting efficiency in plasmonic solar cells could lead to thinner and, therefore, lower cost devices. The development of hybrid core/shell particles could offer a solution to this issue. The addition of a dielectric spacer between a gold nanoparticles and a chromophore is the proposed method to control the exciton plasmon coupling strength and thereby balance losses with the plasmonic gains. A detailed procedure for the coating of gold nanoparticles with CdS and ZnS semiconductor shells is presented. The nanoparticles show high uniformity with size control in both the core gold particles and shell species allowing for a more accurate investigation into the plasmonic enhancement of external chromophores.

The synthesis of uniform gold nanoparticles coated with semiconductor shells of CdS or ZnS is performed. The semiconductor coating is conducted by first depositing a silver sulfide shell and exchanging the silver cations for zinc or cadmium cations.

Plasmonic nanoparticles are an attractive material for light harvesting applications due to their easily modified surface, high surface area and large ...

Synthesis of Ligand-free CdS Nanoparticles within a Sulfur Copolymer Matrix

Aliphatic ligands are typically used during the synthesis of nanoparticles to help mediate their growth in addition to operating as high-temperature solvents. These coordinating ligands help solubilize and stabilize the nanoparticles while in solution, and can influence the resulting size and reactivity of the nanoparticles during their formation. Despite the ubiquity of using ligands during synthesis, the presence of aliphatic ligands on the nanoparticle surface can result in a number of problems during the end use of the nanoparticles, necessitating further ligand stripping or ligand exchange procedures. We have developed a way to synthesize cadmium sulfide (CdS) nanoparticles using a unique sulfur copolymer. This sulfur copolymer is primarily composed of elemental sulfur, which is a cheap and abundant material. The sulfur copolymer has the advantages of operating both as a high temperature solvent and as a sulfur source, which can react with a cadmium precursor during nanoparticle synthesis, resulting in the generation of ligand free CdS. During the reaction, only some of the copolymer is consumed to produce CdS, while the rest remains in the polymeric state, thereby producing a nanocomposite material. Once the reaction is finished, the copolymer stabilizes the nanoparticles within a solid polymeric matrix. The copolymer can then be removed before the nanoparticles are used, which produces nanoparticles that do not have organic coordinating ligands. This nascent synthesis technique presents a method to produce metal-sulfide nanoparticles for a wide variety of applications where the presence of organic ligands is not desired.

Herein we present a method to synthesize ligand-free cadmium sulfide (CdS) nanoparticles based on a unique sulfur copolymer. The sulfur copolymer operates as a high temperature solvent and a sulfur source during the nanoparticle synthesis and stabilizes the nanoparticles after the reaction.

Aliphatic ligands are typically used during the synthesis of nanoparticles to help mediate their growth in addition to operating as high-temperature ...

Molten-Salt Synthesis of Complex Metal Oxide Nanoparticles

The development of feasible synthesis methods is critical for the successful exploration of novel properties and potential applications of nanomaterials. Here, we introduce the molten-salt synthesis (MSS) method for making metal oxide nanomaterials. Advantages over other methods include its simplicity, greenness, reliability, scalability, and generalizability. Using pyrochlore lanthanum hafnium oxide (La2Hf2O7) as a representative, we describe the MSS protocol for the successful synthesis of complex metal oxide nanoparticles (NPs). Furthermore, this method has the unique ability to produce NPs with different material features by changing various synthesis parameters such as pH, temperature, duration, and post-annealing. By fine-tuning these parameters, we are able to synthesize highly uniform, non-agglomerated, and highly crystalline NPs. As a specific example, we vary the particle size of the La2Hf2O7&#160;NPs by changing the concentration of the ammonium hydroxide solution used in the MSS process, which allows us to further explore the effect of particle size on various properties. It is expected that the MSS method will become a more popular synthesis method for nanomaterials and more widely employed in the nanoscience and nanotechnology community in the upcoming years.

Here, we demonstrate a unique, relatively low-temperature, molten-salt synthesis method for preparing uniform complex metal oxide lanthanum hafnate nanoparticles.

The development of feasible synthesis methods is critical for the successful exploration of novel properties and potential applications of nanomaterials. ...

Synthesis and Characterization of Amphiphilic Gold Nanoparticles

Gold nanoparticles covered with a mixture of 1-octanethiol (OT) and 11-mercapto-1-undecane sulfonic acid (MUS) have been extensively studied because of their interactions with cell membranes, lipid bilayers, and viruses. The hydrophilic ligands make these particles colloidally stable in aqueous solutions and the combination with hydrophobic ligands creates an amphiphilic particle that can be loaded with hydrophobic drugs, fuse with the lipid membranes, and resist nonspecific protein adsorption. Many of these properties depend on nanoparticle size and the composition of the ligand shell. It is, therefore, crucial to have a reproducible synthetic method and reliable characterization techniques that allow the determination of nanoparticle properties and the ligand shell composition. Here, a one-phase chemical reduction, followed by a thorough purification to synthesize these nanoparticles with diameters below 5 nm, is presented. The ratio between the two ligands on the surface of the nanoparticle can be tuned through their stoichiometric ratio used during synthesis. We demonstrate how various routine techniques, such as transmission electron microscopy (TEM), nuclear magnetic resonance (NMR), thermogravimetric analysis (TGA), and ultraviolet-visible (UV-Vis) spectrometry, are combined to comprehensively characterize the physicochemical parameters of the nanoparticles.

Amphiphilic gold nanoparticles can be used in many biological applications. A protocol to synthesize gold nanoparticles coated by a binary mixture of ligands and a detailed characterization of these particles is presented.

Gold nanoparticles covered with a mixture of 1-octanethiol (OT) and 11-mercapto-1-undecane sulfonic acid (MUS) have been extensively studied because of ...

Synthesis of Monodisperse Cylindrical Nanoparticles via Crystallization-driven Self-assembly of Biodegradable Block Copolymers

The production of monodisperse cylindrical micelles is a significant challenge in polymer chemistry. Most cylindrical constructs formed from diblock copolymers are produced by one of three techniques: thin film rehydration, solvent switching or polymerization-induced self-assembly, and produce only flexible, polydisperse cylinders. Crystallization-driven self-assembly (CDSA) is a method which can produce cylinders with these properties, by stabilizing structures of a lower curvature due to the formation of a crystalline core. However, the living polymerization techniques by which most core-forming blocks are formed are not trivial processes and the CDSA process may yield unsatisfactory results if carried out incorrectly. Here, the synthesis of cylindrical nanoparticles from simple reagents is shown. The drying and purification of reagents prior to a ring-opening polymerization of &#949;-caprolactone catalyzed by diphenyl phosphate is described. This polymer is then chain extended by methyl methacrylate (MMA) followed by N,N-dimethyl acrylamide (DMA) using reversible addition&#8722;fragmentation chain-transfer (RAFT) polymerization, affording a triblock copolymer that can undergo CDSA in ethanol. The living CDSA process is outlined, the results of which yield cylindrical nanoparticles up to 500 nm in length and a length dispersity as low as 1.05. It is anticipated that these protocols will allow others to produce cylindrical nanostructures and elevate the field of CDSA in the future.

Crystallization-driven self-assembly (CDSA) displays the unique ability to fabricate cylindrical nanostructures of narrow length distributions. The organocatalyzed ring-opening polymerization of &#949;-caprolactone and subsequent chain extensions of methyl methacrylate and N,N-dimethyl acrylamide are demonstrated. A living CDSA protocol that produces monodisperse cylinders up to 500 nm in length is outlined.

The production of monodisperse cylindrical micelles is a significant challenge in polymer chemistry. Most cylindrical constructs formed from diblock ...

Synthesis of Aptamer-PEI-g-PEG Modified Gold Nanoparticles Loaded with Doxorubicin for Targeted Drug Delivery

Due to drug resistance and toxicity in healthy cells, use of doxorubicin (DOX) has been limited in clinical cancer therapy. This protocol describes the designing of poly(ethylenimine) grafted with polyethylene glycol (PEI-g-PEG) copolymer functionalized gold nanoparticles (AuNPs) with loaded aptamer (AS1411) and DOX through amide reactions. AS1411 is specifically bonded with targeted nucleolin receptors on cancer cells so that DOX targets cancer cells instead of healthy cells. First, PEG is carboxylated, then grafted to branched PEI to obtain a PEI-g-PEG copolymer, which is confirmed by 1H NMR analysis. Next, PEI-g-PEG copolymer coated gold nanoparticles (PEI-g-PEG@AuNPs) are synthesized, and DOX and AS1411 are covalently bonded to AuNPs gradually via amide reactions. The diameter of the prepared AS1411-g-DOX-g-PEI-g-PEG@AuNPs is ~39.9 nm, with a zeta potential of -29.3 mV, indicating that the nanoparticles are stable in water and cell medium. Cell cytotoxicity assays show that the newly designed DOX loaded AuNPs are able to kill cancer cells (A549). This synthesis demonstrates the delicate arrangement of PEI-g-PEG copolymers, aptamers, and DOX on AuNPs that are achieved by sequential amide reactions. Such aptamer-PEI-g-PEG functionalized AuNPs provide a promising platform for targeted drug delivery in cancer therapy.

In this protocol, doxorubicin-loaded AS1411-g-PEI-g-PEG modified gold nanoparticles are synthesized via three-step amide reactions. Then, doxorubicin is loaded and delivered to target cancer cells for cancer therapy.

Due to drug resistance and toxicity in healthy cells, use of doxorubicin (DOX) has been limited in clinical cancer therapy. This protocol describes the ...

Construction of Cyclic Cell-Penetrating Peptides for Enhanced Penetration of Biological Barriers

Cancer has been a grand challenge in global health. However, the complex tumor microenvironment generally limits the access of therapeutics to deeper tumor cells, leading to tumor recurrence. To conquer the limited penetration of biological barriers, cell-penetrating peptides (CPPs) have been discovered with excellent membrane translocation ability and have emerged as useful molecular transporters for delivering various cargoes into cells. However, conventional linear CPPs generally show compromised proteolytic stability, which limits their permeability across biological barriers. Thus, the development of novel molecular transporters that can penetrate biological barriers and exhibit enhanced proteolytic stability is highly desired to promote drug delivery efficiency in biomedical applications. We have previously synthesized a panel of short cyclic CPPs with aromatic crosslinks, which exhibited superior permeability in cancer cells and tissues compared to their linear counterparts. Here, a concise protocol is described for the synthesis of the fluorescently labeled cyclic polyarginine R8 peptide and its linear counterpart, as well as key steps for investigating their cell permeability.

This protocol describes the synthesis of cyclic cell-penetrating peptides with aromatic cross-links and the evaluation of their permeability across biological barriers.

Cancer has been a grand challenge in global health. However, the complex tumor microenvironment generally limits the access of therapeutics to deeper ...

Aqueous Synthesis of Plasmonic Gold-Tin Alloy Nanoparticles

This protocol describes the synthesis of Au nanoparticle seeds and the subsequent formation of Au-Sn bimetallic nanoparticles. These nanoparticles have potential applications in catalysis, optoelectronics, imaging, and drug delivery. Previously, methods for producing alloy nanoparticles have been time-consuming, require complex reaction conditions, and can have inconsistent results. The outlined protocol first describes the synthesis of approximately 13 nm Au nanoparticle seeds using the Turkevich method. The protocol next describes the reduction of Sn and its incorporation into the Au seeds to generate Au-Sn alloy nanoparticles. The optical and structural characterization of these nanoparticles is described. Optically, prominent localized surface plasmon resonances (LSPRs) are apparent using UV-visible spectroscopy. Structurally, powder X-ray diffraction (XRD) reflects all particles to be less than 20 nm and shows patterns for Au, Sn, and multiple Au-Sn intermetallic phases. Spherical morphology and size distribution are obtained from transmission electron microscopy (TEM) imaging. TEM reveals that after Sn incorporation, the nanoparticles grow to approximately 15 nm in diameter.

Author Spotlight: Designing Sustainable Nanomaterials for Advancing Synthesis and Element Mixing

Here, the synthesis of gold (Au) seeds is described using the Turkevich method. These seeds are then used to synthesize gold-tin alloy (Au-Sn) nanoparticles with tunable plasmonic properties.

This protocol describes the synthesis of Au nanoparticle seeds and the subsequent formation of Au-Sn bimetallic nanoparticles. These nanoparticles have ...