We thank Mrs. Rebecca Alvarado for the support in the protocol video production and Mr. Stephen Casale for constructive criticism on the manuscript. We thank the colleagues from the Department of Cellular Biophysics, Max Planck Institute for Medical Research for the helpful discussions. The financial support from the Max-Planck-Gesellschaft to E.A.C.-A. and the Deutsche Forschungsgemeinschaft (DFG SFB1129, Projektnummer 240245660, P15 to E.A.C.-A. and P4 to U.S.S.; DFG EXC 2082/1-390761711 to U.S.S.) is also greatly acknowledged. J.B. thanks the Carl Zeiss Foundation for financial support. E.A.C.-A., C.S. and U.S.S. acknowledge funding through the Max Planck School Matter to Life supported by the German Federal Ministry of Education and Research (BMBF). C.S. is supported by the European Research Council (Consolidator Grant PHOTOMECH, no.101001797).

1. Preparation of methacrylated coverslips
NOTE: Glass coverslips are methacrylated to covalently link PA hydrogels and therefore prevent their detachment during the incubation with cells. Microscope glass coverslips are used to achieve high image quality.
<ol>
	<li>To prepare a 300 mL solution, take a clean 400 mL glass beaker and place it inside a fume hood.</li>
	<li>Add 10 mL of double distilled water (ddH2O) into the beaker. Add 18.75 mL of acetic acid (&#8805;99.8% pro analysis, p.a.), 18.75 mL of 3-(Trimethoxysilyl)propyl methacrylate and 252.5 mL of ethanol (&#8805;99.8% p.a.) using a serological pipette. Pour the solution into a crystallizing dish.</li>
	<li>Clean 24 mm round glass coverslips with precision wipes. Place the coverslips in a custom-made polytetrafluorethylene rack.</li>
	<li>Immerse the rack into the solution and incubate for 15 min at room temperature (RT).</li>
	<li>Take the rack and rinse all coverslips with ethanol (99.8% p.a.). Dry the coverslips under air flow. 
	NOTE: Methacrylated coverslips can be stored for up to 1 month at RT.</li>
</ol>
2. Micropatterning of extracellular matrix proteins on glass coverslips
NOTE: Glass coverslips are first coated with a layer of molecules, comprising of protein and cell repellent. This layer is then removed using a photopatterning technique, to allow the subsequent deposition of extracellular matrix proteins in micropatterned regions.
<ol>
	<li>Take a 15 mm round glass coverslip and place it on a Petri dish. Use a diamond pen to mark the upper side of the coverslip. Then, proceed to cleaning via oxygen plasma treatment at 0.4 mbar and 200 W for 2 min.</li>
	<li>Pipette 100 &#181;L of 0.01% poly-L-lysine solution on the surface of each coverslip. Incubate for 30 min at RT. Wash the coverslips with 10 mM 4-(2-hydroxyethyl)-1-piperazineethanesulfonic acid (HEPES) pH 8.5. Remove any excess liquid but keep the surface wet.</li>
	<li>Pipette 100 &#181;L of 50 mg/mL poly(ethylene glycol) methyl ether succinimidyl valeric acid (mPEG-SVA) in 10 mM HEPES pH 8.5 on the surface of each coverslip. Incubate for 1 h at RT. Rinse the coverslips with 10 mM HEPES pH 8.5 and dry off under air flow.</li>
	<li>Add 2 &#181;L of UV-sensitive photoinitiator (e.g., PLPP-gel) followed by 40 &#181;L of ethanol (&#8805;99.8% p.a.) onto the surface. To obtain a homogeneous distribution of the gel and ethanol on the surface, gently tilt the Petri dish back and forth. Wait for 5 min for the solution to polymerize.</li>
	<li>Place a single coverslip inside a 35 mm Petri dish with a 20 mm hole at the bottom. This allows the laser beam coming from underneath to directly reach the glass surface.</li>
	<li>Turn on the microscope and a light patterning module (working with this device is only permitted after a safety introduction from the laser safety officers). Calibrate the UV-A laser on the 20x air objective. Put the sample with the photoinitiator on the stage. Adjust the focus on the surface of the glass and turn on the focus control. Load and lock the pre-drawn pattern.
	<ol>
		<li>Prepare the pattern using a graphics software like Inkscape. Ensure that the pattern file does not exceed the DMD dimensions (1824 x 1140 px, which corresponds to 552 x 325 &#181;m on 20 x lens (0.28 &#181;m/px)). 
		NOTE: It is recommended to use the DMD size (1824 x 1140 pixels) as the pattern file size, as this will ensure no error during the patterning. For example, do not produce a pattern file with 1830 x 1130 pixels dimension.</li>
		<li>For the purpose of pattern transfer to polyacrylamide, ensure that the patterning is done only up to 60%-70 % of the radius from the center of the glass to the edge.</li>
		<li>For patterning a single cell, use a diameter of 50-100 &#181;m with the distance of 100 &#181;m between patterns and a diameter of 150-300 &#181;m for a cell group. The appropriate pattern size highly depends on the typical cell size, and it has to be sufficiently large to allow cells to adhere.</li>
	</ol>
	</li>
	<li>Start the patterning by UV dose of 30 mJ/mm2. The patterning duration depends on the number of patterns. Making a single pattern takes approximately 1 s.</li>
	<li>After completing the patterning step, rinse the surface with phosphate-buffered saline (PBS) three times. Incubate the sample with 100 &#181;L of 25 &#181;g/mL fibronectin dissolved in 1x PBS and 25 &#181;g/mL fibrinogen Alexa488 conjugate in PBS for 1 h at RT. For other ECM proteins, find the optimal concentrations completely covering the patterned regions.</li>
	<li>Rinse the surface with 1x PBS three times. Ensure that the patterned glass is immediately used for glass-PA transfer. Store the patterned glass in PBS at RT during the hydrogel preparation.</li>
</ol>
3. Fabrication of patterned polyacrylamide hydrogels
NOTE: Polyacrylamide hydrogels are prepared, including oxidized N-hydroxyethyl acrylamide (HEA) to present reactive aldehyde groups for the covalent binding of matrix proteins on the surface. Additionally, a dual-layer approach to embed fluorescent beads only on the top layer of the hydrogel is used to improve the recording of bead displacement during traction force microscopy experiments.
<ol>
	<li>Put the methacrylated glass coverslips into a Petri dish.</li>
	<li>To prepare fresh oxidized HEA solution, add 9.55 mL of double-distilled water into a 15 mL centrifuge tube. Then, add 0.5 mL of HEA, and 42 mg of sodium(meta)periodate to get 10 mL of the solution. Continuously stir the solution in the dark for 4 h.</li>
	<li>Mix acrylamide, bis-acrylamide, and double-distilled water according to Table 1, to get 10 mL of stock solution hydrogel (do it under the fume hood, monomers are neurotoxic). Degas and close the lid to an airtight seal. 
	NOTE: The stock solution can be kept in aliquots for up to 1 year at 4 &#176;C. Always characterize the Young&#39;s modulus of the hydrogel prior to use.</li>
	<li>Prepare a dual-layered PA hydrogel (do it under the fume hood, monomers are neurotoxic).
	<ol>
		<li>Start with the bottom layer by gently mixing 99.3 &#181;L of stock solution, 0.5 &#181;L of 1% ammonium persulfate (APS), and 0.2 &#181;L of tetramethylethylenediamine (TEMED) in a 1.5 mL tube. Take 10 &#181;L from the solution and pipette it dropwise on the center of the methacrylated coverslip.</li>
		<li>Carefully place a 15 mm round coverslip on the droplet and wait for 45 min for polymerization. Gently detach the top coverslip with a scalpel.</li>
		<li>For the top layer, gently mix 93.3 &#181;Lof stock solution with 1 &#181;L of fresh oxidized HEA solution, 5 &#181;L of fluorescent beads (corresponding to three beads per square micron for beads of 200 nm sized beads), 0.5 &#181;L of 1% APS, and 0.2 &#181;L of TEMED in a 1.5 mL tube. Take 5 &#181;L from the solution and pipette it dropwise on the center of the already polymerized bottom layer.</li>
		<li>Gently place the micropatterned coverslip on the droplet. Wait for 45 min at RT for the droplet to polymerize. Make sure the patterned side touches the droplet. Gently detach the coverslip with a scalpel.</li>
	</ol>
	</li>
	<li>Glue the 24 mm coverslips to the bottom of custom-drilled 6-well plates using two-component silicone-glue. After 5 min, add PBS to the wells.</li>
	<li>Characterize the Young&#39;s modulus of the polyacrylamide hydrogel samples by atomic force microscopy (AFM).
	<ol>
		<li>Mount a spherical tip cantilever on the AFM holder.</li>
		<li>Calibrate each cantilever by acquiring a force-distance curve (3-4 V setpoint) on a hard substrate (e.g., glass or mica), extrapolate the cantilever sensitivity, retract from the surface, and perform a thermal tune to get their spring constant.</li>
		<li>Place the calibrated cantilevers over the hydrogel sample and acquire force curves in PBS buffer, using the following parameters: 20-30 nN force setpoint, 5 or 10 &#181;m/s approach and retraction speed, 5 &#181;m ramp size. 
		NOTE: An inverted optical microscope, equipped with an air 40x objective and a green fluorescent protein (GFP) filter was used to visualize and target ECM-micropatterned areas within the PA hydrogel samples.</li>
		<li>Plot the acquired force versus distance curves with the AFM analysis software.</li>
		<li>Find the contact point and convert force versus distance curves into force versus indentation curves.</li>
		<li>Fit the indentation part of the curve with Hertz model (or a suitable mechanics model in function of the tip geometry), using a Poisson ratio between 0.2 and 0.5.</li>
	</ol>
	</li>
</ol>
4. Local release of cell traction forces by UV-A laser illumination (LUVI-TFM)
NOTE: UV-A laser is applied to release traction forces in cells localized in defined regions of the hydrogels. The UV-A laser (i.e., &#955; = 375 nm solid-state laser, &#60;15 mW) is a class 3B laser. The unshielded laser beam is dangerous to the eyes and often for the skin. Reflected and scattered light and radiation can be dangerous. Moreover, UV radiation may cause skin cancer. Working with devices is only permitted after safety introduction from the laser safety officers.
<ol>
	<li>Aspirate the PBS from the wells.</li>
	<li>Seed 3 x 106 cells per 6-well plate in growth medium. For fibroblasts, use high glucose Dulbecco&#39;s Modified Eagle Medium (DMEM) containing L-glutamine and supplemented with 10% Foetal Bovine Serum (FBS) and 1% penicillin/streptomycin. Incubate the cells overnight at 37 &#176;C/5% CO2. Wash samples to remove floating cells before starting microscopy.</li>
	<li>Turn on the microscope incubation chamber and gas supply to obtain a temperature of 37 &#176;C and 5% CO2 atmosphere.</li>
	<li>Turn on the microscope and the laser patterning module. If necessary, re-calibrate the UV-A laser on the 20x air objective using the Leonardo software. Place the custom-made 6-well plate with the samples on the stage. Adjust focus on the surface of the PA.</li>
	<li>Setup the illumination pattern and mark the cells of interest. Refocus on the surface of the hydrogel. Acquire the image of the cells in the brightfield channel. Switch to the Cy5 channel (far-red filter, 650 nm excitation, 670 nm emission) and take an image of beads in the deformed state.</li>
	<li>Shift to the laser channel. Turn on the laser for 3 min. In our particular setup, this corresponded to a light dose of 6,000 mJ/mm2.</li>
	<li>Switch to the Cy5 channel and acquire an image of the beads in the undeformed state. 
	NOTE: For experiment using mouse embryonic fibroblasts, wait for 15 min post-exposure to record the reference/undeformed image (See the Representative Results section). It might be different for other type of cells. Repeat steps 4.5-4.7 again for another cell(s) of interest.</li>
	<li>To measure the elevated oxidative stress after UV-A illumination, use the commercially available reagent (CellRox). CellRox is non-fluorescent in the reduced state and, when oxidized by reactive oxygen species, fluoresces with an emission maximum of ~665 nm.</li>
	<li>According to the provided protocol, add 5 &#181;M reagent into the imaging media and incubate for 30 min at 37 &#176;C/5% CO2. Then, wash the cells 3x with warm 1x PBS and replace the imaging media. Record the Cy5 signal by fluorescence imaging before and after UV-A illumination using a similar light exposure.</li>
</ol>
5. Image processing, particle image velocimetry and calculation of traction forces
NOTE: Cell traction forces are recorded by analyzing displacement of fluorescent beads and calculated using image analysis tools based on particle image velocimetry.
<ol>
	<li>Open fluorescent beads images, before (i.e., deformed) and after laser (i.e., undeformed) using Fiji. Merge two images as one stack (Image | Stacks | Images to Stack).</li>
	<li>Correct lateral drift between the two images using StackReg plugin (P. Th&#233;venaz, Swiss Federal Institute of Technology Lausanne). Change images to 8 bit (Image | Type | 8 bit) and re-scale to 1024 x 1024 pix (Image | Scale). Save as an Image Sequence (TIFF format) with the reference image always at the beginning.</li>
	<li>Acquire the displacement vector field using a cross-correlation technique19 from the PIV-field as implemented in the OpenPIV project.
	<ol>
		<li>Ensure that the relaxed (undeformed) image and the deformed image are covered with search windows of size wR and wD in pixels. For each search window, define a cross-correlation function using the following formula: 
		<img alt="Equation 1" src="/files/ftp_upload/63121/63121eq01.jpg" /> 
		Here, R(i,j) and D(i,j) describe the intensity fields of the two images truncated to the selected search window and subsequently mirror padded. <img alt="Equation 2" src="/files/ftp_upload/63121/63121eq02.jpg" /> and <img alt="Equation 3" src="/files/ftp_upload/63121/63121eq03.jpg" /> describe their mean value. The window sizes are chosen to be wR = 32 and wD = 32 and an overlap of 70% is used between the neighboring search windows.</li>
		<li>For each search window determine a displacement vector <img alt="Equation 4" src="/files/ftp_upload/63121/63121eq04.jpg" /> that optimizes the cross-correlation function and assign to the center position of the search window. Subpixel accuracy is obtained using a Gaussian fit around the maxima region as described20.</li>
		<li>Find and remove ambiguous displacement vectors. Displacement vectors corresponding to search windows where the ratio between two highest local maxima of the cross-correlation function below a threshold of 1.5 are considered as ambiguous21.</li>
		<li>Discard displacement vectors that fail the normalized median test for a residual threshold of 1.522.</li>
		<li>(Optional) Correct the remaining lateral drift by subtracting a fixed vector <img alt="Equation 5" src="/files/ftp_upload/63121/63121eq05.jpg" /> from all displacements. This is done because the displacement in a selected area far away from the cell vanishes.</li>
		<li>Interpolate the resulting displacement vector field to a regular grid with spacing of 4 px of the input images using a cubic polynomial interpolation. Missing datapoints are filled using a smooth bivariate spline extrapolation. A displacement vector in pixels is related to a local deformation by the pixel ratio of the image (0.33 &#181;m/px for 20x air lens).</li>
		<li>(Optional) Mirror pad the image to reduce ringing artifacts in the subsequent analysis.</li>
		<li>Multiply the deformation field by a Tukey window function to eliminate the edge effect due to the drift correction, with a parameter of 0.2-0.3. In this experiment, the micropatterned area which is in the center of FOV is of interest.</li>
	</ol>
	</li>
	<li>Reconstruct the traction using regularized Fourier Transform Traction Cytometry (FTTC)18. As regularization we use the simplest reasonable choice, namely, 0th order Tikhonov (L2) regularization23,24,25. An optimal regularization parameter &#955; is chosen such that it minimizes the Generalized Cross Validation (GCV) function defined by26: 
	<img alt="Equation 6" src="/files/ftp_upload/63121/63121eq06.jpg" /> 
	Here&#160;&#964;&#955; is a stacked vector containing the x and y components of the reconstructed traction field for the given value of &#955; for all Fourier sampling modes and G is the linear operator mapping traction fields to their corresponding displacement field, as defined for FTTC. The sum is running over vector components. ui are the x and y components of the displacement field for all Fourier sampling modes. GCV is widely used in the field of ill-posed inverse problems and is a good alternative to the L-curve criterion often used in TFM. A Lanzcos filter is used to reduce artifacts introduces due to the limited frequency space and the displacement field upsampling. The traction calculation depends on the Young&#39;s modulus of the PA (e.g., 11.3 kPa) and Poisson&#39;s ratio (e.g., for PA in the range between 0.2 and 0.5 depending on crosslinker concentration).</li>
</ol>

<ol>
	<li>Geiger, B., Bershadsky, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Exploring+the+neighborhood:+adhesion-coupled+cell+mechanosensors.">Exploring the neighborhood: adhesion-coupled cell mechanosensors.</a> Cell. 110 (2), 139-142 (2002).</li><li>Beningo, K. A., Hamao, K., Dembo, M., Wang, Y. -. l., Hosoya, H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Traction+forces+of+fibroblasts+are+regulated+by+the+Rho-dependent+kinase+but+not+by+the+myosin+light+chain+kinase.">Traction forces of fibroblasts are regulated by the Rho-dependent kinase but not by the myosin light chain kinase.</a> Archives of Biochemistry and Biophysics. 456 (2), 7 (2006).</li><li>Rape, A. D., Guo, W. H., Wang, Y. L. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=The+regulation+of+traction+force+in+relation+to+cell+shape+and+focal+adhesions.">The regulation of traction force in relation to cell shape and focal adhesions.</a> Biomaterials. 32 (8), 2043-2051 (2011).</li><li>Kumar, R., Saha, S., Sinha, B. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Cell+spread+area+and+traction+forces+determine+myosin-II-based+cortex+thickness+regulation.">Cell spread area and traction forces determine myosin-II-based cortex thickness regulation.</a> Biochimica Biophysica Acta. Molecular Cell Research. 1866 (12), 118516 (2019).</li><li>Chen, C. S., Mrksich, M., Huang, S., Whitesides, G. M., Ingber, D. E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Geometric+control+of+cell+life+and+death.">Geometric control of cell life and death.</a> Science. 276 (5317), 1425-1428 (1997).</li><li>Thery, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Micropatterning+as+a+tool+to+decipher+cell+morphogenesis+and+functions.">Micropatterning as a tool to decipher cell morphogenesis and functions.</a> Journal of Cell Science. 123, 4201-4213 (2010).</li><li>Strale, P. O., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Multiprotein+printing+by+light-induced+molecular+adsorption.">Multiprotein printing by light-induced molecular adsorption.</a> Advanced Materials. 28 (10), 2024-2029 (2016).</li><li>Azioune, A., Carpi, N., Tseng, Q., Th&#233;ry, M., Piel, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=.">.</a> Microtubules: in vivo Methods in Cell Biology. , 133-146 (2010).</li><li>Tseng, Q., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=A+new+micropatterning+method+of+soft+substrates+reveals+that+different+tumorigenic+signals+can+promote+or+reduce+cell+contraction+levels.">A new micropatterning method of soft substrates reveals that different tumorigenic signals can promote or reduce cell contraction levels.</a> Lab on a Chip. 11 (13), 2231-2240 (2011).</li><li>Vignaud, T., Ennomani, H., Thery, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Polyacrylamide+hydrogel+micropatterning.">Polyacrylamide hydrogel micropatterning.</a> Methods Cell Biology. 120, 93-116 (2014).</li><li>Munevar, S., Wang, Y., Dembo, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Traction+force+microscopy+of+migrating+normal+and+H-ras+transformed+3T3+fibroblasts.">Traction force microscopy of migrating normal and H-ras transformed 3T3 fibroblasts.</a> Biophysical Journal. 80 (4), 1744-1757 (2001).</li><li>Style, R. W., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Traction+force+microscopy+in+physics+and+biology.">Traction force microscopy in physics and biology.</a> Soft Matter. 10 (23), 4047-4055 (2014).</li><li>Polacheck, W. J., Chen, C. S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Measuring+cell-generated+forces:+a+guide+to+the+available+tools.">Measuring cell-generated forces: a guide to the available tools.</a> Nature Methods. 13 (5), 415-423 (2016).</li><li>Schwarz, U. S., Soine, J. R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Traction+force+microscopy+on+soft+elastic+substrates:+A+guide+to+recent+computational+advances.">Traction force microscopy on soft elastic substrates: A guide to recent computational advances.</a> Biochimica Biophysica Acta. 1853, 3095-3104 (2015).</li><li>Roca-Cusachs, P., Conte, V., Trepat, X. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Quantifying+forces+in+cell+biology.">Quantifying forces in cell biology.</a> Nature Cell Biology. 19 (7), 742-751 (2017).</li><li>Hanke, J., Probst, D., Zemel, A., Schwarz, U. S., Koster, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Dynamics+of+force+generation+by+spreading+platelets.">Dynamics of force generation by spreading platelets.</a> Soft Matter. 14 (31), 6571-6581 (2018).</li><li>Butler, J. P., Tolic-Norrelykke, I. M., Fabry, B., Fredberg, J. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Traction+fields,+moments,+and+strain+energy+that+cells+exert+on+their+surroundings.">Traction fields, moments, and strain energy that cells exert on their surroundings.</a> American Journal of Physiology. Cell Physiology. 282 (3), 595-605 (2002).</li><li>Sabass, B., Gardel, M. L., Waterman, C. M., Schwarz, U. S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=High+resolution+traction+force+microscopy+based+on+experimental+and+computational+advances.">High resolution traction force microscopy based on experimental and computational advances.</a> Biophysical Journal. 94 (1), 207-220 (2008).</li><li>Willert, C. E., Gharib, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Digital+particle+image+velocimetry.">Digital particle image velocimetry.</a> Experiments in Fluids. 10, 181-193 (1991).</li><li>Lourenco, L., Krothapalli, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=On+the+accuracy+of+velocity+and+corticity+measurements+with+PIV.">On the accuracy of velocity and corticity measurements with PIV.</a> Experiments in Fluids. 18, 421-428 (1995).</li><li>Adrian, R. J., Westerweel, J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=.">.</a> Particle Image Velocimetry. , (2011).</li><li>Westerweel, J., Scarano, F. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Universal+outlier+detection+for+PIV+data.">Universal outlier detection for PIV data.</a> Experiments in Fluids. 39 (6), 1096-1100 (2005).</li><li>Dembo, M., Wang, Y. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Stresses+at+the+cell-to-substrate+interface+during+locomotion+of+fibroblasts.">Stresses at the cell-to-substrate interface during locomotion of fibroblasts.</a> Biophysical Journal. 76 (4), 2307-2316 (1999).</li><li>Schwarz, U. S., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Calculation+of+forces+at+focal+adhesions+from+elastic+substrate+data:+the+effect+of+localized+force+and+the+need+for+regularization.">Calculation of forces at focal adhesions from elastic substrate data: the effect of localized force and the need for regularization.</a> Biophysical Journal. 83 (3), 1380-1394 (2002).</li><li>Huang, Y., Gompper, G., Sabass, B. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=A+Bayesian+traction+force+microscopy+method+with+automated+denoising+in+a+user-friendly+software+package.">A Bayesian traction force microscopy method with automated denoising in a user-friendly software package.</a> Computer Physics Communications. 256, 107313 (2020).</li><li>Vedadghavami, A., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Manufacturing+of+hydrogel+biomaterials+with+controlled+mechanical+properties+for+tissue+engineering+applications.">Manufacturing of hydrogel biomaterials with controlled mechanical properties for tissue engineering applications.</a> Acta Biomaterialia. 62, 42-63 (2017).</li><li>Huth, S., Sindt, S., Selhuber-Unkel, C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Automated+analysis+of+soft+hydrogel+microindentation:+Impact+of+various+indentation+parameters+on+the+measurement+of+Young's+modulus.">Automated analysis of soft hydrogel microindentation: Impact of various indentation parameters on the measurement of Young's modulus.</a> PLoS One. 14 (8), 0220281 (2019).</li><li>Oria, R., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Force+loading+explains+spatial+sensing+of+ligands+by+cells.">Force loading explains spatial sensing of ligands by cells.</a> Nature. 552 (7684), 219-224 (2017).</li><li>Buxboim, A., Rajagopal, K., Brown, A. E., Discher, D. E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=How+deeply+cells+feel:+methods+for+thin+gels.">How deeply cells feel: methods for thin gels.</a> Journal of Physics. Condensed Matter. 22 (19), 194116 (2010).</li><li>Sen, S., Engler, A. J., Discher, D. E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Matrix+strains+induced+by+cells:+Computing+how+far+cells+can+feel.">Matrix strains induced by cells: Computing how far cells can feel.</a> Cell and Molecular Bioengineering. 2 (1), 39-48 (2009).</li><li>Arnold, M., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Induction+of+cell+polarization+and+migration+by+a+gradient+of+nanoscale+variations+in+adhesive+ligand+spacing.">Induction of cell polarization and migration by a gradient of nanoscale variations in adhesive ligand spacing.</a> Nano Letters. 8 (7), 2063-2069 (2008).</li><li>Galluzzi, M., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Atomic+force+microscopy+methodology+and+AFMech+Suite+software+for+nanomechanics+on+heterogeneous+soft+materials.">Atomic force microscopy methodology and AFMech Suite software for nanomechanics on heterogeneous soft materials.</a> Nat Communications. 9 (1), 3584 (2018).</li></ol>

The authors have nothing to disclose.

In this protocol, we describe the preparation of micropatterned PA hydrogels containing fluorescent beads, which are used as fiducial markers for TFM studies. Our approach is based on three steps: 1) preparation of dual-layered PA hydrogels; 2) micropatterning of ECM proteins and their transfer onto the hydrogel surface; 3) use of patterned near-UV light for TFM. The experimental setup to analyze cell tractions to the substrate requires the use of linear elastic materials with known stiffness values to calculate the forces related to displacement of the fluorescent beads26. PA hydrogels are easy to prepare, the stiffness can be easily tuned, and they are commonly used for rigidity sensing and TFM18,28. However, to obtain reproducible polymerization times and homogeneous polymerization of the entire hydrogel, attention should be paid to storing conditions and time for the reagents, e.g., APS should be kept in a desiccator to avoid losing its activity; TEMED should be protected from direct light. The use of oxidized HEA allows the covalent binding of matrix proteins on the hydrogel surface, which might be advantageous to achieve the formation of a full and stable protein layer. The oxidized HEA solution should be prepared fresh every time PA hydrogels are fabricated. The dual-layered PA hydrogel offers three main advantages: 1) it provides an alternative way to reproducibly get a homogenous distribution of fiducial beads near the hydrogel surface, without the need for making the gel extremely thin (i.e., &lt;20 &#181;m). Control over hydrogel thickness is crucial for obtaining accurate measurements with TFM. When the elastic substrate is too thin, strong adherent cells such as fibroblasts may sense and mechanically respond to the underlying rigid glass substrate29,30. Thick hydrogels make the image acquisition for the force reconstruction more challenging. Moreover, many microscopes will not have sufficient space to accommodate them, considering the additional thickness of the glass substrate used to attach the hydrogel, unless ultrathin microscopy slides are used. 2) In the dual-layered PA hydrogel, the homogenous distribution of fiducial beads near the surface of the PA hydrogel is achieved without using a centrifuge, but rather with a simple incubation of precise amounts of hydrogel solutions and fluorescent beads. High bead density is of significant advantage when performing the PIV analysis because it increases the resolution of the traction forces and the signal-to-noise ratio without the need for confocal microscopy. 3) Confining beads in a thin layer close to the cell-material interface enables imaging of traction forces with epifluorescence microscopes as well as confocal microscopes. When preparing the hydrogel, the user should make sure that it firmly adheres to the bottom glass before proceeding with the subsequent steps of the protocol. We recommend following the incubation time indicated for the polymerization of the hydrogel layers, as it might be difficult to remove the glass on top of the surface without damaging the hydrogel surface.
The most well-known techniques to measure elastic properties are AFM, nanoindentation, tensile tests, and rheometry. However, nanoindentation induces very high strains on the materials that can affect the determination of elastic properties. Tensile tests and rheometry on the other hand are macroscopic measurement techniques, whereas cells interact on a microscopic scale31,32. AFM allows measurements at the microscale with reduced strains under physiological conditions. The reliability of AFM measurements can be adversely affected if experimental details are missing (e.g., indentation force and speed) or insufficient data is recorded27. Huth et al. describes an algorithm to extract Young's moduli from AFM data, which emphasizes keeping measurement details constant27. This algorithm offers a precise and reliable determination of Young's moduli and was used for our experiments. Additionally, we measured many curves on samples fabricated on different days and gained very similar results (variation of mean values of ca. 1-2 kPa). This shows that the stiffness of our gels can be reliably predicted.
In this protocol, we use a photopatterning module to create micropatterned regions on glass, which are then transferred to the hydrogel surfaces. The micropatterning shown in this protocol is based on DMD (digital micro-mirror device)-based maskless near-UV lithography (&#955; = 375 nm)7. A DMD consists of a large number of micromirrors on a chip. A single pixel corresponds to a single micro-mirror. The pixelated pattern image file from a computer is projected through DMD and focused on the surface using an objective lens. For micropatterning of proteins, the focused laser light is used to cleave repellent polymer brushes with the help of a photoinitiator. Afterwards, the exposed regions are filled with ECM proteins. This maskless ablation method offers great flexibility in designing new patterns, as it does not rely on the use of a photomask. Designing and applying a pattern is very easy as it only takes several minutes using a freeware like Inkscape. However, the number of patterns and sample produced in a short amount of time is a major drawback, as this method can only be used to pattern a single substrate each time. The photopatterning module uses a near UV solid-state laser source that emits several milliwatts. The unshielded laser beam is dangerous to the eyes and skin. Reflected and scattered light and radiation can also be dangerous. Handling must be accompanied by a safety instruction from laser officers. The most critical step in the protocol when using a photopatterning module is to ensure that during the micropatterning and the ablation the laser is properly focused on the surface. A consistent illumination dose (intensity multiplied by time) of UV-light during patterning is dependent on how the laser is focused on the surface. A weak intensity on the surface due to poor focus may result in the failure of ECM transfer to the hydrogel surface resulting in no cells becoming attached to the hydrogel.
In TFM experiments, after the initial imaging of adherent cells and the fiducial markers, cells are released from the PA hydrogel by trypsin treatment to record their relaxed state. A drawback in performing this step is handling the sample on the microscopy stage. Without a perfusion chamber, opening the lid of the dish, aspirating the medium, rinsing, and pipetting trypsin solution represent a challenge for beginners and experienced users. In fact, these procedures are a major source of the drift in xyz axes, resulting in loss of position and focus. Our local-UV illumination protocol makes TFM a more accessible technique for beginners. It should be noted that we used a commercially available microscopy-based maskless photopatterning module, but in principle any UV-A lighting system could be used, eventually in combination with a mask to protect regions of the substrates, where cell traction forces should not be recorded. Exposing cells with a significant dose of low wavelength visible light (e.g., the violet light that excites DAPI emission) will lead to increasing oxidative stress, which can result in phototoxicity and cell death. Therefore, this technique can be applied even in an epifluorescence microscope without a UV laser module. However, as the intensity is much weaker, it will be much easier to accomplish TFM with the enzymatic treatment in this case.
With LUVI-TFM it is possible to use the same sample for several measurements because of the local detachment of single cells or small groups of cells. However, attention should be paid to the selection of cells to detach, to avoid recording forces from neighboring cells. Thus, for single cell measurements in absence of micropatterns, crowded regions should be avoided; for measurements on single micropatterned cells, the patterns should be designed such that the distance between single structures is at least twice the diameter of the patterned area. We also recommend not using cells from adjacent patterns in sequence, but rather sampling them from distant regions on the substrate. Our measurement is well conducted on an epifluorescence microscope equipped with a focus control feature and a 40 x air NA = 0.9 lens, where the working distance of the lens is sufficiently long and the rapid movement from one well to another is highly tunable. The targeted detachment of cells for TFM applications is effective for measuring cellular force of a single cell or of an entire small cell cluster (e.g., up to 300 &#181;m in diameter). Using our setup, we observed cell rounding and detachment for UV treatment of single cells (Figure 3A), whereas detachment seldom occurred for small cell clusters. This might lead to an underestimation of cell traction forces. For larger cell clusters, enzymatic detachment is recommended, since the users should use a 20x air objective to image the entire cluster and a focus control feature is needed. As the depth of focus of the 20x air lens is much longer, the handling will not be as critical as the higher magnification objective. The user should ensure that the focus is correctly set for the ablation of cells, since the illumination dose is dependent on the laser focus on the surface. While we are aware of the possible limitations in using LUVI-TFM in cell collectives because of possible mechanical interactions with neighboring untreated cells, this aspect could actually turn out to be useful for studies on the mechanics of targeted cell extrusion, e.g., from epithelial monolayers.
In conclusion, with our TFM approach combined with light induced release of micropatterned cells, we provide a robust and high-throughput protocol to measure cell adhesion forces. The versatility of this method could be further exploited using microscopy and imaging setup aimed at improving resolution and sensitivity.

When interacting with their extracellular environment, adherent cells exert forces that are mainly mediated by integrin-based focal adhesions connecting the extracellular matrix (ECM) to the actin cytoskeleton. Focal adhesions are multiprotein assemblies that are centered around the binding of integrins to ECM-proteins like fibronectin and collagen. Integrin clustering and growth of focal adhesions is crucial not only for the establishment of a mechanically stable connection, but also for recruitment of other focal adhesion proteins, including those that activate the RhoA pathway for the regulation of cellular contractility1. The RhoA-dependent contractility of the actin cytoskeleton allows cells to spread and migrate on the underlying ECM, and also to sense its stiffness2. The distribution of traction forces strongly depends on cells&#39; spread area and shape, both of which rely on matrix properties and therefore impact cytoskeletal organization, eventually forming a closed feedback loop between matrix mechanics and cytoskeletal organization3,4.
Surface micropatterning techniques allow a defined control of cell shape by creating micron-sized regions presenting ECM adhesive proteins; according to the size of these regions, single cells, or groups of cells that adhere to the micropattern5. ECM proteins can be patterned on glass substrates by different approaches such as microcontact printing, photo-patterning or laser-patterning6. The use of UV light (&#955; = 185 or 375 nm) combined with surface antifouling strategies offers the flexibility for designing different shapes and sizes and immobilization of multiple protein types with a high precision near surface edges7,8. The regions coated with protein repellent chemicals such as polyethylene glycol (PEG) are protected with either a chromium photomask or a digital mirror device (DMD)-based maskless lithography system. The patterns in the masks allow the exposure to UV light of regions that will then be patterned with ECM proteins. The patterning of hydrogel surfaces with ECM proteins requires a transfer step to remove proteins from the glass surface and crosslink them to the patterns. Alternatively, patterning on soft materials can be achieved by first coating the photomask with a repellent protein, followed by burning the unmasked regions using deep UV illumination. Since deep UV generates ozone and makes the surface reactive for protein binding, the unmasked regions are coated with ECM proteins and finally the gel is polymerized directly on top of the unmasked regions9,10.
The patterned hydrogels can be used to perform TFM, a technique that measures cell forces at the cell-material interface11. In 2D-TFM, one uses the flat surface of a thick polymer film, in which marker beads have been embedded to track deformations12,13,14,15. In order to extract displacement vectors, it is essential to combine two images, one of the deformed state and one reference image without deformations. The two images are then mapped onto each other with image processing. At high marker density, this is usually done with Particle Image Velocimetry (PIV), which is a well-established method to reconstruct hydrodynamic flow. At low marker density and in 3D-TFM, this is usually done with Particle Tracking Velocimetry (PTV), which includes specific features of the experimental data set. An example of a computationally cheaper alternative is optical flow, such as the Kanade-Lucas-Tomasi (KLT) algorithm16. In the case of hydrogel substrates, fluorescent beads are usually embedded at high density during the material polymerization, and images are recorded before and after cell release upon enzymatic detachment. Enzymatic detachment of adherent cells, e.g., by trypsinization, leads to simultaneous release of cellular tractions from all cells on the hydrogels, making it difficult to obtain a detailed analysis from a high number of cells.
Here we present a protocol to prepare micropatterned hydrogels to control cell shape and localization and a method to efficiently measure traction forces in sequence using UV to detach individual cells from the substrate. For traction force measurements, we present a technique to produce dual-layered PA hydrogels, where fluorescent beads are embedded only in the top layer, which increases their density and reduces their vertical spread. Combining UV-mediated release of cellular traction forces with micropatterning makes it possible to obtain spatial control over cell detachment (e.g., of single cells without affecting the adhesion of other cells in the region of interest), provided there is a sufficient distance between patterned cells. Cellular traction is then reconstructed using the most efficient and reliable method for 2D-TFM, namely, Fourier Transform Traction Cytometry (FTTC) with regularization17,18.

<table border="1" fo:keep-together.within-page="1" fo:keep-with-next.within-page="always">
	<tbody>
		<tr>
			<td>3-(Trimethoxysilyl)propyl methacrylate</td>
			<td>#440159</td>
			<td>Sigma Aldrich</td>
			<td></td>
		</tr>
		<tr>
			<td>Acetic acid</td>
			<td>#33209</td>
			<td>Honeywell</td>
			<td></td>
		</tr>
		<tr>
			<td>Acrylamide 40 %</td>
			<td>#1610140</td>
			<td>Bio-Rad</td>
			<td>CAUTION : toxic, work under a fume hood</td>
		</tr>
		<tr>
			<td>AFM cantilever</td>
			<td>#CP-CONT-BSG-A-G</td>
			<td>NanoAndMore</td>
			<td>5 &#956;m spherical tip</td>
		</tr>
		<tr>
			<td>AFM system</td>
			<td>#NanoWizard3</td>
			<td>JPK</td>
			<td>Coupled to optical microscope equipped with 40x air objective and GFP filter</td>
		</tr>
		<tr>
			<td>Ammonium persulfate</td>
			<td>#A3678</td>
			<td>Sigma</td>
			<td></td>
		</tr>
		<tr>
			<td>Bis-acrylamide 2 %</td>
			<td>#1610142</td>
			<td>Bio-Rad</td>
			<td>CAUTION : toxic, work under a fume hood</td>
		</tr>
		<tr>
			<td>Camera sCMOS</td>
			<td>#C11440-42U30</td>
			<td>Hamamatsu</td>
			<td></td>
		</tr>
		<tr>
			<td>Camera sCMOS</td>
			<td>#ANDORZYLA4.2</td>
			<td>Oxford Instrument</td>
			<td></td>
		</tr>
		<tr>
			<td>CellRox</td>
			<td>#C10422</td>
			<td>Thermo Fisher</td>
			<td></td>
		</tr>
		<tr>
			<td>Custom incubator chamber</td>
			<td></td>
			<td>EMBLEM</td>
			<td></td>
		</tr>
		<tr>
			<td>Dental glue</td>
			<td>#1300 100</td>
			<td>Picodent</td>
			<td></td>
		</tr>
		<tr>
			<td>DMEM</td>
			<td>#41965</td>
			<td>Thermo Fisher</td>
			<td></td>
		</tr>
		<tr>
			<td>Epifluorescence microscope</td>
			<td>#Eclipse Ti2E</td>
			<td>Nikon</td>
			<td></td>
		</tr>
		<tr>
			<td>Epifluorescence microscope</td>
			<td>#Axiovert200</td>
			<td>Zeiss</td>
			<td></td>
		</tr>
		<tr>
			<td>Ethanol</td>
			<td>#9065.3</td>
			<td>Carl Roth</td>
			<td></td>
		</tr>
		<tr>
			<td>FBS South America</td>
			<td>#S181T</td>
			<td>Thermo Fisher</td>
			<td></td>
		</tr>
		<tr>
			<td>Fibrinogen</td>
			<td>#F13191</td>
			<td>Invitrogen</td>
			<td>Alexa488 conjugate</td>
		</tr>
		<tr>
			<td>Fibronectin</td>
			<td>#F1141</td>
			<td>Sigma</td>
			<td></td>
		</tr>
		<tr>
			<td>Fluorescent beads 200 nm</td>
			<td>#F8805</td>
			<td>Invitrogen</td>
			<td>Carboxylated (365/415)</td>
		</tr>
		<tr>
			<td>Fluorescent beads 200 nm</td>
			<td>#F8848</td>
			<td>Invitrogen</td>
			<td>Carboxylated (505/515)</td>
		</tr>
		<tr>
			<td>Fluorescent beads 200 nm</td>
			<td>#F8810</td>
			<td>Invitrogen</td>
			<td>Carboxylated (580/605)</td>
		</tr>
		<tr>
			<td>Fluorescent beads 200 nm</td>
			<td>#F8807</td>
			<td>Invitrogen</td>
			<td>Carboxylated (660/680)</td>
		</tr>
		<tr>
			<td>Glass coverslip 15 mm round</td>
			<td>#41001115</td>
			<td>Assistent</td>
			<td></td>
		</tr>
		<tr>
			<td>Glass coverslip 24 mm round</td>
			<td>#41001124</td>
			<td>Assistent</td>
			<td></td>
		</tr>
		<tr>
			<td>Microscope Objective</td>
			<td>#MRH08230</td>
			<td>Nikon</td>
			<td>20x air NA 0.45</td>
		</tr>
		<tr>
			<td>Mouse Embryonic Fibroblasts</td>
			<td>#CRL-2991</td>
			<td>ATCC</td>
			<td></td>
		</tr>
		<tr>
			<td>mPEG-SVA</td>
			<td>#MPEG-SVA-5000</td>
			<td>Laysan Bio</td>
			<td></td>
		</tr>
		<tr>
			<td>N-Hydroxyethyl acrylamide</td>
			<td>#697931</td>
			<td>Aldrich</td>
			<td></td>
		</tr>
		<tr>
			<td>Plasma cleaner</td>
			<td>#100-E</td>
			<td>TePla</td>
			<td></td>
		</tr>
		<tr>
			<td>PLPP gel</td>
			<td>#PLPPgel</td>
			<td>Alveole</td>
			<td></td>
		</tr>
		<tr>
			<td>Poly-L-lysine</td>
			<td>#P4823</td>
			<td>Sigma Aldrich</td>
			<td></td>
		</tr>
		<tr>
			<td>Poly(L-lysine)-graft-poly(ethylene glycol)</td>
			<td>#PLL(20-g[3.5]-PEG(2)</td>
			<td>SuSoS</td>
			<td></td>
		</tr>
		<tr>
			<td>Sodium(meta) periodate</td>
			<td>#S1878</td>
			<td>Sigma Aldrich</td>
			<td></td>
		</tr>
		<tr>
			<td>TEMED</td>
			<td>#17919</td>
			<td>Thermo Scientific</td>
			<td></td>
		</tr>
		<tr>
			<td>UV Pattening module</td>
			<td>#PRIMO</td>
			<td>Alveole</td>
			<td></td>
		</tr>
		<tr>
			<td>UVO cleaner</td>
			<td>#342-220</td>
			<td>Jelight</td>
			<td></td>
		</tr>
	</tbody>
</table>

control of cell adhesion using hydrogel patterning techniques for applications in traction force microscopy

Traction force microscopy (TFM) is the main method used in mechanobiology to measure cell forces. Commonly this is being used for cells adhering to flat soft substrates that deform under cell traction (2D-TFM). TFM relies on the use of linear elastic materials, such as polydimethylsiloxane (PDMS) or polyacrylamide (PA). For 2D-TFM on PA, the difficulty in achieving high throughput results mainly from the large variability of cell shapes and tractions, calling for standardization. We present a protocol to rapidly and efficiently fabricate micropatterned PA hydrogels for 2D-TFM studies. The micropatterns are first created by maskless photolithography using near-UV light where extracellular matrix proteins bind only to the micropatterned regions, while the rest of the surface remains non-adhesive for cells. The micropatterning of extracellular matrix proteins is due to the presence of active aldehyde groups, resulting in adhesive regions of different shapes to accommodate either single cells or groups of cells. For TFM measurements, we use PA hydrogels of different elasticity by varying the amounts of acrylamide and bis-acrylamide and tracking the displacement of embedded fluorescent beads to reconstruct cell traction fields with regularized Fourier Transform Traction Cytometry (FTTC).
To further achieve precise recording of cell forces, we describe the use of a controlled dose of patterned light to release cell tractions in defined regions for single cells or groups of cells. We call this method local UV illumination traction force microscopy (LUVI-TFM). With enzymatic treatment, all cells are detached from the sample simultaneously, whereas with LUVI-TFM traction forces of cells in different regions of the sample can be recorded in sequence. We demonstrate the applicability of this protocol (i) to study cell traction forces as a function of controlled adhesion to the substrate, and (ii) to achieve a greater number of experimental observations from the same sample.

The PA hydrogels were polymerized on methacrylated glass coverslips, which present reactive groups for the covalent linkage of the PA. In this way, when placing the hydrogels in an aqueous solution, their detachment from the substrate was prevented (Figure 1A-D). To obtain a high density of fiducial markers near the hydrogel surface, we developed the preparation of a dual-layered PA hydrogel. The bottom layer, without any fluorescent beads, was polymerized on the methacrylated coverslip. Subsequently, another layer containing beads was polymerized on top of the bottom layer (Figure 1E-H), replacing the need for sedimentation, which is often used to achieve bead distribution in a single focal plane and increase bead density. To achieve control over cell shape during TFM measurements, we produced micropatterned PA hydrogels via direct transfer of fibronectin-patterned microstructures from a glass coverslip to the pre-polymerized PA (Figure 1F-F&#39;). The addition of 1% non-conventional crosslinker (oxidized HEA) in the top hydrogel layer solution provides aldehyde groups that covalently bind to amine groups of fibronectin.
We prepared PA hydrogels, which are approximately 60 &#181;m in thickness and confined fluorescent beads in the upper layer close to the hydrogel surface. This type of hydrogel is a suitable substrate for imaging cellular tractions with inverted microscopes and thick enough (minimum thickness to perform TFM has been reported to be 20-30 &#181;m)18 to prevent any impact of the glass substrate. Localization of the fluorescent beads was imaged by confocal microscopy (Figure 1I). To visualize protein transfer on the hydrogel, we used fluorescently labeled ECM proteins and imaged them by epifluorescence microscopy (Figure 1J). We prepared micropatterned circles of fibronectin with a diameter of 100 &#181;m (left side) and 50 &#181;m (right side) to allow adhesion of groups of cells or single cells, as shown in the overlay of bright field images of adherent cells, and fluorescently labeled fiducial beads and fibronectin micropatterns. On a different sample, the adhesion response of single cells to micropatterned fibronectin was validated by indirect immunofluorescence microscopy to image the localization of focal adhesion proteins such as paxillin (Figure 1K).
Both ECM protein coating and hydrogel stiffness are crucial parameters for cell adhesion26. To characterize the mechanical properties of our PA hydrogels, we performed nanoindentation experiments by AFM27, coupled with an epifluorescence microscope. Hydrogel substrates of three different stiffnesses were prepared and tested with our setup (Figure 2 and Table 1). Sphere-shaped AFM cantilevers were cyclically approached and retracted from unpatterned PA hydrogels and fibrinogen conjugated to Alexa488-micropatterned areas, while recording force-distance curves. Subsequently, contact point evaluation and application of Hertz model allowed us to estimate the Young&#39;s modulus (E) of each sample. ECM micropatterning did not alter the Young&#39;s modulus, which remained comparable to each of the unpatterned PA hydrogels.
To measure traction forces exerted by adherent cells on the substrate, we developed an experimental setup for reference based TFM carried out on a widefield epifluorescence microscope equipped with near UV laser module (UV-A 6000 mJ/mm2) to release cell tractions (Figure 3A). As the laser beam illumination can be spatio-temporally controlled, not only is it possible to selectively expose a single cell or a cell cluster with a high laser dose, but also and more importantly, the disruptive intermediate step of cell removal from the entire sample using a digestive enzyme like trypsin is no longer necessary.Illuminating cells with such a high laser dose induced an elevated oxidative stress leading to cell death (Figure 3B). Cell death yielded the release of tractions from the substrate, as indicated by the bead displacement (illustrated in Figure 3A). We combined the UV-A illumination with a light patterning module to selectively illuminate micron-sized regions of the PA hydrogels (Figure 3B-C). In this way it is possible to release the tractions of micropatterned cell clusters (Figure 3C,F) or single cells (Figure 3B). Importantly, at our time scales the mechanical properties of the ECM patterned hydrogels were not significantly affected by UV exposure (Figure 2C). Increase in oxidative stress is shown in Figure 3D,E. The traction forces were reconstructed by using regularized FTTC with a regularization parameter chosen by Generalized Cross Validation (Figure 3B,F). The release of forces for single cells occurred over a period of 15 min, and the result of the LUVI-TFM is comparable to the trypsin-based TFM (Figure 3G-H).
<img alt="Figure 1" class="xfigimg" src="/files/ftp_upload/63121/63121fig01.jpg" /> 
Figure 1: Scheme of patterned fibronectin-substrate preparation for TFM. (A) The solution for the bottom layer is pipetted on a methacrylated surface. (B) A smaller clean coverslip is carefully placed on the droplet. (C) The gelation time is 45 min. (D) The top coverslip is detached. The bottom layer is ready. (E) The solution for the top layer is pipetted on the hydrogel. (F) The patterned coverslip is carefully placed on the droplet. (F&#39;) The micropatterning of adhesive proteins on glass is produced by maskless near UV-lithography, and then transferred from glass to PA hydrogel. The free amine groups of adhesive proteins, e.g., fibronectin, bind covalently to aldehyde groups on the PA surface. (G) The gelation time is 45 min. (H) The top coverslip is detached. The patterned PA hydrogel is ready. (I) A 3D representation of a confocal xyz micrograph showing a high density of fiducial beads near the surface. (J) A micrograph of fluorescently labeled fibronectin (magenta) on the surface of PA with embedded fluorescent beads (green), overlayed with a bright field image of cells. (K) Indirect immunofluorescence microscopy imaging of a single cell adhering to a circle-shaped fibronectin micropattern (100 &#181;m). Nucleus (blue), paxillin (red). <a href="https://www.jove.com/files/ftp_upload/63121/63121fig01large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>
<img alt="Figure 2" class="xfigimg" src="/files/ftp_upload/63121/63121fig02.jpg" /> 
Figure 2: Characterization of sample mechanical properties by AFM. (A) AFM nanoindentation experimental setup. A sphere-shaped cantilever is used to probe ECM micropatterns before or after UV treatment, and the non-patterned regions of dual layered PA (5% Acrylamide, 0.3% Bis-acrylamide) areas. (B) Representative force versus indentation curve for ECM micropattern (black). Hertz fit (red) is used to calculate the Young&#39;s modulus (E) of the sample. (C) Mechanical measurements for non-patterned dual layered PA areas (no ECM), ECM micropattern and ECM micropattern after UV-A exposure. The bars show mean &#177; S.E.M. (Brown-Forsythe and Welch ANOVA test). <a href="https://www.jove.com/files/ftp_upload/63121/63121fig02large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>
<img alt="Figure 3" class="xfigimg" src="/files/ftp_upload/63121/63121fig03.jpg" /> 
Figure 3. Local UV-A illumination TFM (LUVI-TFM) enables local traction force measurements inside a large field of view. (A) Scheme of local UV-A illumination TFM. Cells are treated with a high dose of UV-A laser to get the undeformed (reference) image. (B) The brightfield image of a single cell before UV-A laser illumination. Middle: The brightfield image of a single cell after UV-A laser illumination. Right: Traction force of a single MEF adhering to a fibronectin coated PA hydrogel (E = 5.74 kPa) illuminated with a 50 &#181;m diameter UV-light beam (red dashed line). (C) Left: Recording of traction forces of a cluster of mouse embryonic fibroblasts (MEF) adhering to micropatterned fibronectin (circle, 100 &#181;m diameter). The cluster was illuminated with a 200 &#181;m diameter UV-light beam (red dashed line). Right: Recording of traction forces of a cluster of mouse embryonic fibroblasts (MEF) adhering to micropatterned fibronectin (circle, 300 &#181;m diameter). The cluster was illuminated with a 300 &#181;m diameter UV-light beam (red dashed line). Scale bar = 200 &#181;m. (D,E) An increase in oxidative stress in cells indicated by the increased Cy5 signal intensity after a high UV-A laser dose is detected by fluorescence microscopy. The oxidative stress leads to cell death.&#160;Scale bar = 200 &#181;m. (F) Left: The stress heat map from a cluster of mouse embryonic fibroblasts (MEF) adhering to micropatterned fibronectin (circle, 100 &#181;m diameter). Right: The stress heat map from a cluster of mouse embryonic fibroblasts (MEF) adhering to micropatterned fibronectin (circle, 300 &#181;m diameter). (G)&#160;MEF cells adhering to 100 &#181;m fibronectin micropatterns slowly release their tractions after UV-A exposure. Full release is achieved after 15 min (the reference image was then taken 15 min post exposure). (H) A comparison with the conventional trypsin based-TFM for MEF cells adhering to 300 &#181;m diameter patterned-fibronectin. The result of UV-A illumination (6,000 mJ/mm2) followed by 15 min waiting is non-significantly different from the conventional trypsin treatment (i.e., 0.05% for 20 min). The bars show mean S.E.M. (two-tailed Student&#39;s t-test, ****P &#60; 0.0001, * P &#60; 0.05, ns P &#8804;0.5). <a href="https://www.jove.com/files/ftp_upload/63121/63121fig03large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>
<table border="1" fo:keep-together.within-page="1" fo:keep-with-next.within-page="always">
	<tbody>
		<tr>
			<td>Acrylamide (%)</td>
			<td>Bis-acrylamide (%)</td>
			<td>Acrylamide from 40 % stock solution (ml)</td>
			<td>Bis-acrylamide from 2 % stock solution (ml)</td>
			<td>Water (ml)</td>
			<td>Young&#8217;s modulus (kPa)</td>
		</tr>
		<tr>
			<td>4</td>
			<td>0.1</td>
			<td>1</td>
			<td>0.5</td>
			<td>8.5</td>
			<td>5,74 &#177; 0,53</td>
		</tr>
		<tr>
			<td>5</td>
			<td>0.15</td>
			<td>1.25</td>
			<td>0.75</td>
			<td>8</td>
			<td>9,69 &#177; 0,68</td>
		</tr>
		<tr>
			<td>5</td>
			<td>0.3</td>
			<td>1.25</td>
			<td>1.5</td>
			<td>7.25</td>
			<td>11,33 &#177; 1,06</td>
		</tr>
	</tbody>
</table>
Table 1: Hydrogel stock solution mixtures and resulting elasticity
All data are deposited in the Open Access Data Repository of The Max Planck Society (Edmond) and can be accessed through the following address:&#160;https://edmond.mpdl.mpg.de/imeji/collection/JTu8PlWqpbymN9Qf

Watch this Scientific Journal Video about Control of Cell Adhesion using Hydrogel Patterning Techniques for Applications in Traction Force Microscopy at JoVE.com

Control of Cell Adhesion using Hydrogel Patterning Techniques for Applications in Traction Force Microscopy

Near-UV lithography and traction force microscopy are combined to measure cellular forces on micropatterned hydrogels. The targeted light-induced release of single cells enables a high number of measurements on the same sample.

Traction force microscopy (TFM) is the main method used in mechanobiology to measure cell forces. Commonly this is being used for cells adhering to flat ...

control-cell-adhesion-using-hydrogel-patterning-techniques-for

Research

JoVE Journal

Bioengineering

5.5K visualizações.  Max Planck Institute for Medical Research. O objetivo geral deste procedimento é fabricar hidrogéis de micro-padrão para estudos de microscopia de força de tração 2D. Isso é feito primeiro fazendo um deslizamento de tampa de vidro metacrilatado e formando a primeira camada de um hidrogel de poliacrilamida sobre ele. O segundo passo é criar outra camada de hidrogel contendo contas fluorescentes para microscopia de força de tração.O hidrogel é sanduíche com um deslizamento de cobertura de micro-padrão em cima dele, ...

Vídeo: Control of Cell Adhesion using Hydrogel Patterning Techniques for Applications in Traction Force Microscopy

Visualization of Cortex Organization and Dynamics in Microorganisms, using Total Internal Reflection Fluorescence Microscopy

TIRF microscopy has emerged as a powerful imaging technology to study spatio-temporal dynamics of fluorescent molecules in vitro and in living cells1. The optical phenomenon of total internal reflection occurs when light passes from a medium with high refractive index into a medium with low refractive index at an angle larger than a characteristic critical angle (i.e. closer to being parallel with the boundary). Although all light is reflected back under such conditions, an evanescent wave is created that propagates across and along the boundary, which decays exponentially with distance, and only penetrates sample areas that are 100-200 nm near the interface2. In addition to providing superior axial resolution, the reduced excitation of out of focus fluorophores creates a very high signal to noise ratios and minimizes damaging effects of photobleaching2,3. Being a widefield technique, TIRF also allows faster image acquisition than most scanning based confocal setups.
At first glance, the low penetration depth of TIRF seems to be incompatible with imaging of bacterial and fungal cells, which are often surrounded by thick cell walls. On the contrary, we have found that the cell walls of yeast and bacterial cells actually improve the usability of TIRF and increase the range of observable structures4-8. Many cellular processes can therefore be directly accessed by TIRF in small, single-cell microorganisms, which often offer powerful genetic manipulation techniques. This allows us to perform in vivo biochemistry experiments, where kinetics of protein interactions and activities can be directly assessed in living cells.
We describe here the individual steps required to obtain high quality TIRF images for Saccharomyces cerevisiae or Bacillus subtilis cells. We point out various problems that can affect TIRF visualization of fluorescent probes in cells and illustrate the procedure with several application examples. Finally, we demonstrate how TIRF images can be further improved using established image restoration techniques.

Total Internal Reflection Fluorescence (TIRF) microscopy is a powerful approach to observe structures close to the cell surface at high contrast and temporal resolution. We demonstrate how TIRF can be employed to study protein dynamics at the cortex of cell wall-enclosed bacterial and fungal cells.

TIRF microscopy has emerged as  a powerful imaging technology to study spatio-temporal dynamics of fluorescent molecules  in vitro and in living cells1. ...

Simultaneously Capturing Real-time Images in Two Emission Channels Using a Dual Camera Emission Splitting System: Applications to Cell Adhesion

Multi-color immunofluorescence microscopy to detect specific molecules in the cell membrane can be coupled with parallel plate flow chamber assays to investigate mechanisms governing cell adhesion under dynamic flow conditions. For instance, cancer cells labeled with multiple fluorophores can be perfused over a potentially reactive substrate to model mechanisms of cancer metastasis. However, multi-channel single camera systems and color cameras exhibit shortcomings in image acquisition for real-time live cell analysis. To overcome these limitations, we used a dual camera emission splitting system to simultaneously capture real-time image sequences of fluorescently labeled cells in the flow chamber. Dual camera emission splitting systems filter defined wavelength ranges into two monochrome CCD cameras, thereby simultaneously capturing two spatially identical but fluorophore-specific images. Subsequently, psuedocolored one-channel images are combined into a single real-time merged sequence that can reveal multiple target molecules on cells moving rapidly across a region of interest.

Dual camera emission splitting systems for two-color fluorescence microscopy generate real-time image sequences with exceptional optical and temporal resolution, a requirement of certain live cell assays including parallel plate flow chamber adhesion assays. When software is employed to merge images from simultaneously acquired emission channels, pseudocolored image sequences are produced.

Multi-color immunofluorescence microscopy to detect specific molecules in the cell membrane can be coupled with parallel plate flow chamber assays to ...

A Novel Method for Localizing Reporter Fluorescent Beads Near the Cell Culture Surface for Traction Force Microscopy

PA gels have long been used as a platform to study cell traction forces due to ease of fabrication and the ability to tune their elastic properties. When the substrate is coated with an extracellular matrix protein, cells adhere to the gel and apply forces, causing the gel to deform. The deformation depends on the cell traction and the elastic properties of the gel. If the deformation field of the surface is known, surface traction can be calculated using elasticity theory. Gel deformation is commonly measured by embedding fluorescent marker beads uniformly into the gel. The probes displace as the gel deforms. The probes near the surface of the gel are tracked. The displacements reported by these probes are considered as surface displacements. Their depths from the surface are ignored. This assumption introduces error in traction force evaluations. For precise measurement of cell forces, it is critical for the location of the beads to be known. We have developed a technique that utilizes simple chemistry to confine fluorescent marker beads, 0.1 and 1 &#181;m in diameter, in PA gels, within 1.6 &#956;m of the surface. We coat a coverslip with poly-D-lysine (PDL) and fluorescent beads. PA gel solution is then sandwiched between the coverslip and an adherent surface. The fluorescent beads transfer to the gel solution during curing. After polymerization, the PA gel contains fluorescent beads on a plane close to the gel surface.

Traditional techniques for fabricating polyacrylamide (PA) gels containing fluorescent probes involve sandwiching a gel between an adherent surface and a glass slide. Here, we show that coating this slide with poly-D-lysine (PDL) and fluorescent probes localizes the probes to within 1.6 &#181;m from the gel surface.

PA gels have long been used as a platform to study cell traction forces due to ease of fabrication and the ability to tune their elastic properties. When ...

Using Cell-substrate Impedance and Live Cell Imaging to Measure Real-time Changes in Cellular Adhesion and De-adhesion Induced by Matrix Modification

Cell-matrix adhesion plays a key role in controlling cell morphology and signaling. Stimuli that disrupt cell-matrix adhesion (e.g., myeloperoxidase and other matrix-modifying oxidants/enzymes released during inflammation) are implicated in triggering pathological changes in cellular function, phenotype and viability in a number of diseases. Here, we describe how cell-substrate impedance and live cell imaging approaches can be readily employed to accurately quantify real-time changes in cell adhesion and de-adhesion induced by matrix modification (using endothelial cells and myeloperoxidase as a pathophysiological matrix-modifying stimulus) with high temporal resolution and in a non-invasive manner. The xCELLigence cell-substrate impedance system continuously quantifies the area of cell-matrix adhesion by measuring the electrical impedance at the cell-substrate interface in cells grown on gold microelectrode arrays. Image analysis of time-lapse differential interference contrast movies quantifies changes in the projected area of individual cells over time, representing changes in the area of cell-matrix contact. Both techniques accurately quantify rapid changes to cellular adhesion and de-adhesion processes. Cell-substrate impedance on microelectrode biosensor arrays provides a platform for robust, high-throughput measurements. Live cell imaging analyses provide additional detail regarding the nature and dynamics of the morphological changes quantified by cell-substrate impedance measurements. These complementary approaches provide valuable new insights into how myeloperoxidase-catalyzed oxidative modification of subcellular extracellular matrix components triggers rapid changes in cell adhesion, morphology and signaling in endothelial cells. These approaches are also applicable for studying cellular adhesion dynamics in response to other matrix-modifying stimuli and in related adherent cells (e.g., epithelial cells).

Here, we present a protocol to continuously quantify cell adhesion and de-adhesion processes with high temporal resolution in a non-invasive manner by cell-substrate impedance and live cell imaging analyses. These approaches reveal the dynamics of cell adhesion/de-adhesion processes triggered by matrix modification and their temporal relationship to adhesion-dependent signaling events.

Cell-matrix adhesion plays a key role in controlling cell morphology and signaling. Stimuli that disrupt cell-matrix adhesion (e.g., myeloperoxidase and ...

Light-mediated Formation and Patterning of Hydrogels for Cell Culture Applications

Click chemistries have been investigated for use in numerous biomaterials applications, including drug delivery, tissue engineering, and cell culture. In particular, light-mediated click reactions, such as photoinitiated thiol&#8722;ene and thiol&#8722;yne reactions, afford spatiotemporal control over material properties and allow the design of systems with a high degree of user-directed property control. Fabrication and modification of hydrogel-based biomaterials using the precision afforded by light and the versatility offered by these thiol&#8722;X photoclick chemistries are of growing interest, particularly for the culture of cells within well-defined, biomimetic microenvironments. Here, we describe methods for the photoencapsulation of cells and subsequent photopatterning of biochemical cues within hydrogel matrices using versatile and modular building blocks polymerized by a thiol&#8722;ene photoclick reaction. Specifically, an approach is presented for constructing hydrogels from allyloxycarbonyl (Alloc)-functionalized peptide crosslinks and pendant peptide moieties and thiol-functionalized poly(ethylene glycol) (PEG) that rapidly polymerize in the presence of lithium acylphosphinate photoinitiator and cytocompatible doses of long wavelength ultraviolet (UV) light. Facile techniques to visualize photopatterning and quantify the concentration of peptides added are described. Additionally, methods are established for encapsulating cells, specifically human mesenchymal stem cells, and determining their viability and activity. While the formation and initial patterning of thiol-alloc hydrogels are shown here, these techniques broadly may be applied to a number of other light and radical-initiated material systems (e.g., thiol-norbornene, thiol-acrylate) to generate patterned substrates.

We describe a sequential process for light-mediated formation and subsequent biochemical patterning of synthetic hydrogel matrices for three-dimensional cell culture applications. The construction and modification of hydrogels with cytocompatible photoclick chemistry is demonstrated. Additionally, facile techniques to quantify and observe patterns and determine cell viability within these hydrogels are presented.

Click chemistries have been investigated for use in numerous biomaterials applications, including drug delivery, tissue engineering, and cell culture. In ...

Patterning Bioactive Proteins or Peptides on Hydrogel Using Photochemistry for Biological Applications

There are many biological stimuli that can influence cell behavior and stem cell differentiation. General cell culture approaches rely on soluble factors within the medium to control cell behavior. However, soluble additions cannot mimic certain signaling motifs, such as matrix-bound growth factors, cell-cell signaling, and spatial biochemical cues, which are common influences on cells. Furthermore, biophysical properties of the matrix, such as substrate stiffness, play important roles in cell fate, which is not easily manipulated using conventional cell culturing practices. In this method, we describe a straightforward protocol to provide patterned bioactive proteins on synthetic polyethylene glycol (PEG) hydrogels using photochemistry. This platform allows for the independent control of substrate stiffness and spatial biochemical cues. These hydrogels can achieve a large range of physiologically relevant stiffness values. Additionally, the surfaces of these hydrogels can be photopatterned with bioactive peptides or proteins via thiol-ene click chemistry reactions. These methods have been optimized to retain protein function after surface immobilization. This is a versatile protocol that can be applied to any protein or peptide of interest to create a variety of patterns. Finally, cells seeded onto the surfaces of these bioactive hydrogels can be monitored over time as they respond to spatially specific signals.

In this method, we use photopolymerization and click chemistry techniques to create protein or peptide patterns on the surface of polyethylene glycol (PEG) hydrogels, providing immobilized bioactive signals for the study of cellular responses in vitro.

There are many biological stimuli that can influence cell behavior and stem cell differentiation. General cell culture approaches rely on soluble factors ...

High Throughput Traction Force Microscopy Using PDMS Reveals Dose-Dependent Effects of Transforming Growth Factor-&#946; on the Epithelial-to-Mesenchymal Transition

Cellular contractility is essential in diverse aspects of biology, driving processes that range from motility and division, to tissue contraction and mechanical stability, and represents a core element of multi-cellular animal life. In adherent cells, acto-myosin contraction is seen in traction forces that cells exert on their substrate. Dysregulation of cellular contractility appears in a myriad of pathologies, making contractility a promising target in diverse diagnostic approaches using biophysics as a metric. Moreover, novel therapeutic strategies can be based on correcting the apparent malfunction of cell contractility. These applications,&#160;however, require direct quantification of these forces.
We have developed silicone elastomer-based traction force microscopy (TFM) in a parallelized multi-well format. Our use of a silicone rubber, specifically polydimethylsiloxane (PDMS), rather than the commonly employed hydrogel polyacrylamide (PAA) enables us to make robust and inert substrates with indefinite shelf-lives requiring no specialized storage conditions. Unlike pillar-PDMS based approaches that have a modulus in the GPa range, the PDMS used here is very compliant, ranging from approximately 0.4 kPa to 100 kPa. We create a high-throughput platform for TFM by partitioning these large monolithic substrates spatially into biochemically independent wells, creating a multi-well platform for traction force screening that is compatible with existing multi-well systems.
In this manuscript, we use this multi-well traction force system to examine the Epithelial to Mesenchymal Transition (EMT); we induce EMT in NMuMG cells by exposing them to TGF-&#946;, and to quantify the biophysical changes during EMT. We measure the contractility as a function of concentration and duration of TGF-&#946; exposure. Our findings here demonstrate the utility of parallelized TFM in the context of disease biophysics.

High Throughput Traction Force Microscopy Using PDMS Reveals Dose-Dependent Effects of Transforming Growth Factor-&amp;#946; on the Epithelial-to-Mesenchymal Transition

We present a high throughput traction force assay fabricated with silicone rubber (PDMS). This novel assay is suitable for studying physical changes in cell contractility during various biological and biomedical processes and diseases. We demonstrate this method's utility by measuring a TGF-&#946; dependent increase in contractility during the epithelial-to-mesenchymal transition.

Cellular contractility is essential in diverse aspects of biology, driving processes that range from motility and division, to tissue contraction and ...

Patterning the Geometry of Human Embryonic Stem Cell Colonies on Compliant Substrates to Control Tissue-Level Mechanics

Human embryonic stem cells demonstrate a unique ability to respond to morphogens in vitro by self-organizing patterns of cell fate specification that correspond to primary germ layer formation during embryogenesis. Thus, these cells represent a powerful tool with which to examine the mechanisms that drive early human development. We have developed a method to culture human embryonic stem cells in confined colonies on compliant substrates that provides control over both the geometry of the colonies and their mechanical environment in order to recapitulate the physical parameters that underlie embryogenesis. The key feature of this method is the ability to generate polyacrylamide hydrogels with defined patterns of extracellular matrix ligand at the surface to promote cell attachment. This is achieved by fabricating stencils with the desired geometric patterns, using these stencils to create patterns of extracellular matrix ligand on glass coverslips, and transferring these patterns to polyacrylamide hydrogels during polymerization. This method is also compatible with traction force microscopy, allowing the user to measure and map the distribution of cell-generated forces within the confined colonies. In combination with standard biochemical assays, these measurements can be used to examine the role mechanical cues play in fate specification and morphogenesis during early human development.

Extracellular matrix ligands can be patterned onto polyacrylamide hydrogels to enable the culture of human embryonic stem cells in confined colonies on compliant substrates. This method can be combined with traction force microscopy and biochemical assays to examine the interplay between tissue geometry, cell-generated forces, and fate specification.

Human embryonic stem cells demonstrate a unique ability to respond to morphogens in vitro by self-organizing patterns of cell fate specification that ...

Fabrication and Implementation of a Reference-Free Traction Force Microscopy Platform

Quantifying cell-induced material deformation provides useful information concerning how cells sense and respond to the physical properties of their microenvironment. While many approaches exist for measuring cell-induced material strain, here we provide a methodology for monitoring strain with sub-micron resolution in a reference-free manner. Using a two-photon activated photolithographic patterning process, we demonstrate how to generate mechanically and bio-actively tunable synthetic substrates containing embedded arrays of fluorescent fiducial markers to easily measure three-dimensional (3D) material deformation profiles in response to surface tractions. Using these substrates, cell tension profiles can be mapped using a single 3D image stack of a cell of interest. Our goal with this methodology is to make traction force microscopy a more accessible and easier to implement tool for researchers studying cellular mechanotransduction processes, especially newcomers to the field.

This protocol provides instructions for implementing multiphoton lithography to fabricate three-dimensional arrays of fluorescent fiducial markers embedded in poly(ethylene glycol)-based hydrogels for use as reference-free, traction force microscopy platforms. Using these instructions, measurement of 3D material strain and calculation of cellular tractions is simplified to promote high-throughput traction force measurements.

Quantifying cell-induced material deformation provides useful information concerning how cells sense and respond to the physical properties of their ...

Traction Microscopy Integrated with Microfluidics for Chemotactic Collective Migration

Cells change migration patterns in response to chemical stimuli, including the gradients of the stimuli. Cellular migration in the direction of a chemical gradient, known as chemotaxis, plays an important role in development, the immune response, wound healing, and cancer metastasis. While chemotaxis modulates the migration of single cells as well as collections of cells in vivo, in vitro research focuses on single-cell chemotaxis, partly due to the lack of the proper experimental tools. To fill that gap, described here is a unique experimental system that combines microfluidics and micropatterning to demonstrate the effects of chemical gradients on collective cell migration. Furthermore, traction microscopy and monolayer stress microscopy are incorporated into the system to characterize changes in cellular force on the substrate as well as between neighboring cells. As proof-of-concept, the migration of micropatterned circular islands of Madin-Darby canine kidney (MDCK) cells is tested under a gradient of hepatocyte growth factor (HGF), a known scattering factor. It is found that cells located near the higher concentration of HGF migrate faster than those on the opposite side within a cell island. Within the same island, cellular traction is similar on both sides, but intercellular stress is much lower on the side of higher HGF concentration. This novel experimental system can provide new opportunities to studying the mechanics of chemotactic migration by cellular collectives.

Collective cell migration in development, wound healing, and cancer metastasis is often guided by the gradients of growth factors or signaling molecules. Described here is an experimental system combining traction microscopy with a microfluidic system and a demonstration of how to quantify the mechanics of collective migration under biochemical gradient.

Cells change migration patterns in response to chemical stimuli, including the gradients of the stimuli. Cellular migration in the direction of a chemical ...