We acknowledge Paul J. L. Webster for the 3D rendering of optical data with Amira. Phil Mu&ntilde;oz and Benjamin Franta provided feedback on the manuscript throughout its development. The research described in this paper was supported by the Air Force Office of Scientific Research under grants FA9550-09-1-0546 and FA9550-10-1-0402.

1. Preparing Metal-ion Doped Polymer Film
<ol>
 <li>Measure 8 ml of water in a beaker.</li>
 <li>Add 206 mg of PVP to water. Mix using magnetic stirrer or vortex mixer until the solution is clear.</li>
 <li>Add 210 mg of AgNO3 to solution. Mix using magnetic stirrer or vortex mixer until solution is clear.</li>
 <li>Coat glass slide with solution through drop casting.</li>
 <li>Place glass slide in an oven set at 100 &deg;C. Bake sample for 30 min.</li>
 <li>Remove sample from oven and let cool for 30 min.</li>
</ol>
2. Fabrication of Disconnected Silver Structures
<ol>
 <li>Align setup depicted in Figure 1 on optical table with vibration isolators.</li>
 <li>Adjust compressor to obtain 50-fsec pulses after microscope objective.</li>
 <li>Adjust neutral density filters to obtain 3-nJ pulses after the objective.</li>
 <li>Ensure laser spot size is larger than back aperture of microscope objective.</li>
 <li>Set acousto-optic modulator to produce 10-&mu;sec exposure windows during which the sample is irradiated.</li>
 <li>Block laser beam before it reaches the microscope and place sample onto 3-axis translation stage. The beam path of the femtosecond laser pulses should pass through the imaging microscope objective and into the sample.</li>
 <li>Turn on microscope illumination source to observe the sample in-situ using CCD camera.</li>
 <li>Translate z-axis of stage to find interface between glass substrate and polymer film. Then, refocus microscope to the desired depth inside polymer for patterning bottom-most layer. Z-translation during patterning must be in the direction away from the glass-polymer interface to avoid scattering with fabricated structures.</li>
 <li>Unblock laser-beam and set motion-controller software to translate sample in x-, y- and z- directions with speed of 100 &mu;m/sec. Irradiate single voxels for 10 &mu;sec and separate neighboring voxels by at least several micrometers for clear in-situ imaging. Setting acousto-optic modulator repetition rate to 25 Hz will produce 4-&mu;m spacing. Laser exposed areas will contain silver structures.</li>
</ol>

<ol>
	<li>von Freymann, G., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Three-Dimensional+Nanostructures+for+Photonics.">Three-Dimensional Nanostructures for Photonics.</a> Advanced Functional Materials. 20, 1038-1052 (2010).</li><li>LaFratta, C. N., Fourkas, J. T., Baldacchini, T., Farrer, R. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Multiphoton+Fabrication.">Multiphoton Fabrication.</a> Angewandte Chemie International Edition. 46, 6238-6258 (2007).</li><li>Gattass, R. R., Mazur, E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Femtosecond+laser+micromachining+in+transparent+materials.">Femtosecond laser micromachining in transparent materials.</a> Nat. Photon. 2, 219-225 (2008).</li><li>Li, L., Gattass, R. R., Gershgoren, E., Hwang, H., Fourkas, J. T. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Achieving+&#955;/20+Resolution+by+One-Color+Initiation+and+Deactivation+of+Polymerization.">Achieving &#955;/20 Resolution by One-Color Initiation and Deactivation of Polymerization.</a> Science. 324, 910-913 (2009).</li><li>Haske, W., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=65+nm+feature+sizes+using+visible+wavelength+3-D+multiphoton+lithography.">65 nm feature sizes using visible wavelength 3-D multiphoton lithography.</a> Opt. Express. 15, 3426-3436 (2007).</li><li>Xing, J. F., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Improving+spatial+resolution+of+two-photon+microfabrication+by+using+photoinitiator+with+high+initiating+efficiency.">Improving spatial resolution of two-photon microfabrication by using photoinitiator with high initiating efficiency.</a> Appl. Phys. Lett. 90, 131106 (2007).</li><li>Tan, D., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Reduction+in+feature+size+of+two-photon+polymerization+using+SCR500.">Reduction in feature size of two-photon polymerization using SCR500.</a> Appl. Phys. Lett. 90, 071106 (2007).</li><li>Vora, K., Kang, S., Shukla, S., Mazur, E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Fabrication+of+disconnected+three-dimensional+silver+nanostructures+in+a+polymer+matrix.">Fabrication of disconnected three-dimensional silver nanostructures in a polymer matrix.</a> Appl. Phys. Lett. 100, 063120 (2012).</li><li>G&#252;ney, D. &. #. 2. 1. 4. ;., Koschny, T., Soukoulis, C. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Intra-connected+three-dimensionally+isotropic+bulk+negative+index+photonic+metamaterial.">Intra-connected three-dimensionally isotropic bulk negative index photonic metamaterial.</a> Opt. Express. 18, 12348-12353 (2010).</li><li>Grigorenko, A. N., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Nanofabricated+media+with+negative+permeability+at+visible+frequencies.">Nanofabricated media with negative permeability at visible frequencies.</a> Nat. Photon. 438, 335-338 (2005).</li><li>Grigorenko, A. N. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Negative+refractive+index+in+artificial+metamaterials.">Negative refractive index in artificial metamaterials.</a> Opt. Lett. 31, 2483-2485 (2006).</li><li>Shalaev, V. M., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Negative+index+of+refraction+in+optical+metamaterials.">Negative index of refraction in optical metamaterials.</a> Opt. Lett. 30, 3356-3358 (2005).</li><li>Ishikawa, A., Tanaka, T., Kawata, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Magnetic+excitation+of+magnetic+resonance+in+metamaterials+at+far-infrared+frequencies.">Magnetic excitation of magnetic resonance in metamaterials at far-infrared frequencies.</a> Appl. Phys. Lett. 91, 113118 (2007).</li><li>Tanaka, T., Ishikawa, A., Kawata, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Two-photon-induced+reduction+of+metal+ions+for+fabricating+three-dimensional+electrically+conductive+metallic+microstructure.">Two-photon-induced reduction of metal ions for fabricating three-dimensional electrically conductive metallic microstructure.</a> Appl. Phys. Lett. 88, 081107 (2006).</li><li>Ishikawa, A., Tanaka, T., Kawata, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Improvement+in+the+reduction+of+silver+ions+in+aqueous+solution+using+two-photon+sensitive+dye.">Improvement in the reduction of silver ions in aqueous solution using two-photon sensitive dye.</a> Appl. Phys. Lett. 89, 113102 (2006).</li><li>Cao, Y. -. Y., Takeyasu, N., Tanaka, T., Duan, X. -. M., Kawata, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=3D+Metallic+Nanostructure+Fabrication+by+Surfactant-Assisted+Multiphoton-Induced+Reduction.">3D Metallic Nanostructure Fabrication by Surfactant-Assisted Multiphoton-Induced Reduction.</a> Small. 5, 1144-1148 (2009).</li></ol>

No conflicts of interest declared.

The key to the process is obtaining a doped dielectric matrix that allows high resolution fabrication, but does not degrade soon after preparation. A simple mixture of PVP, AgNO3 and H2O allows the creation of high-resolution silver nanostructures that are embedded inside a support matrix. Varying the PVP to AgNO3 ratio will change the laser energy needed for fabrication, and potentially other properties such as feature resolution. A low ratio leads to faster degradation of the die...

a method to fabricate disconnected silver nanostructures in 3d

The standard nanofabrication toolkit includes techniques primarily aimed at creating 2D patterns in dielectric media. Creating metal patterns on a submicron scale requires a combination of nanofabrication tools and several material processing steps. For example, steps to create planar metal structures using ultraviolet photolithography and electron-beam lithography can include sample exposure, sample development, metal deposition, and metal liftoff. To create 3D metal structures, the sequence is repeated multiple times. The complexity and difficulty of stacking and aligning multiple layers limits practical implementations of 3D metal structuring using standard nanofabrication tools. Femtosecond-laser direct-writing has emerged as a pre-eminent technique for 3D nanofabrication.1,2 Femtosecond lasers are frequently used to create 3D patterns in polymers and glasses.3-7 However, 3D metal direct-writing remains a challenge. Here, we describe a method to fabricate silver nanostructures embedded inside a polymer matrix using a femtosecond laser centered at 800 nm. The method enables the fabrication of patterns not feasible using other techniques, such as 3D arrays of disconnected silver voxels.8 Disconnected 3D metal patterns are useful for metamaterials where unit cells are not in contact with each other,9 such as coupled metal dot10,11or coupled metal rod12,13 resonators. Potential applications include negative index metamaterials, invisibility cloaks, and perfect lenses.
In femtosecond-laser direct-writing, the laser wavelength is chosen such that photons are not linearly absorbed in the target medium. When the laser pulse duration is compressed to the femtosecond time scale and the radiation is tightly focused inside the target, the extremely high intensity induces nonlinear absorption. Multiple photons are absorbed simultaneously to cause electronic transitions that lead to material modification within the focused region. Using this approach, one can form structures in the bulk of a material rather than on its surface.
Most work on 3D direct metal writing has focused on creating self-supported metal structures.14-16 The method described here yields sub-micrometer silver structures that do not need to be self-supported because they are embedded inside a matrix. A doped polymer matrix is prepared using a mixture of silver nitrate (AgNO3), polyvinylpyrrolidone (PVP) and water (H2O). Samples are then patterned by irradiation with an 11-MHz femtosecond laser producing 50-fs pulses. During irradiation, photoreduction of silver ions is induced through nonlinear absorption, creating an aggregate of silver nanoparticles in the focal region. Using this approach we create silver patterns embedded in a doped PVP matrix. Adding 3D translation of the sample extends the patterning to three dimensions.

The acousto-optic modulator and neutral density filters (Figure 1) allow one to control the amount of energy deposited into the sample. Using an exposure of 110 pulses per voxel and 3 nJ per pulse, with the stage translating at 100 &mu;m/sec, the resulting silver structures are readily visible through the in-situ optical microscope. Lower laser exposure levels (by reducing pulse energy and/or pulse number) lead to smaller silver features; we have observed features as small as 300 nm.8...

Watch this Scientific Journal Video about A Method to Fabricate Disconnected Silver Nanostructures in 3D at JoVE.com

A Method to Fabricate Disconnected Silver Nanostructures in 3D

Femtosecond-laser direct-writing is frequently used to create three-dimensional (3D) patterns in polymers and glasses. However, patterning metals in 3D remains a challenge. We describe a method for fabricating silver nanostructures embedded inside a polymer matrix using a femtosecond laser centered at 800 nm.

The standard nanofabrication toolkit includes  techniques primarily aimed at creating 2D patterns in dielectric media. Creating  metal patterns on a ...

a-method-to-fabricate-disconnected-silver-nanostructures-in-3d

Research

JoVE Journal

Engineering

13.7K Views.  Harvard University. Фемтосекундного лазера прямого написания часто используется для создания трехмерных (3D) моделей в полимерах и стеклах. Тем не менее, структурирование металлов в 3D остается проблемой. Мы опишем способ изготовления серебряных наноструктур внедренные в полиме?...

Video: A Method to Fabricate Disconnected Silver Nanostructures in 3D

High-resolution, High-speed, Three-dimensional Video Imaging with Digital Fringe Projection Techniques

Digital fringe projection (DFP) techniques provide dense 3D measurements of dynamically changing surfaces.&#160;Like the human eyes and brain, DFP uses triangulation between matching points in two views of the same scene at different angles to compute depth.&#160;However, unlike a stereo-based method, DFP uses a digital video projector to replace one of the cameras1. The projector rapidly projects a known sinusoidal pattern onto the subject, and the surface of the subject distorts these patterns in the camera&#8217;s field of view. Three distorted patterns (fringe images) from the camera can be used to compute the depth using triangulation.
Unlike other 3D measurement methods, DFP techniques lead to systems that tend to be faster, lower in equipment cost, more flexible, and easier to develop.&#160;DFP systems can also achieve the same measurement resolution as the camera.&#160;For this reason, DFP and other digital structured light techniques have recently been the focus of intense research (as summarized in1-5). Taking advantage of DFP, the graphics processing unit, and optimized algorithms, we have developed a system capable of 30&#160;Hz 3D video data acquisition, reconstruction, and display for over 300,000 measurement points per frame6,7.&#160;Binary defocusing DFP methods can achieve even greater speeds8.
Diverse applications can benefit from DFP techniques. Our collaborators have used our systems for facial function analysis9, facial animation10, cardiac mechanics studies11, and fluid surface measurements, but many other potential applications exist.&#160;This video will teach the fundamentals of DFP techniques and illustrate the design and operation of a binary defocusing DFP system.

This video describes the fundamentals of digital fringe projection techniques, which provide dense 3D measurements of dynamically changing surfaces.&#160;It also demonstrates the design and operation of a high-speed binary defocusing system based on these techniques.

Digital fringe projection (DFP) techniques provide dense 3D measurements of dynamically changing surfaces.&#160;Like the human eyes and brain, DFP uses ...

Evaluating Plasmonic Transport in Current-carrying Silver Nanowires

Plasmonics is an emerging technology capable of simultaneously transporting a plasmonic signal and an electronic signal on the same information support1,2,3. In this context, metal nanowires are especially desirable for realizing dense routing networks4. A prerequisite to operate such shared nanowire-based platform relies on our ability to electrically contact individual metal nanowires and efficiently excite surface plasmon polaritons5 in this information support. In this article, we describe a protocol to bring electrical terminals to chemically-synthesized silver nanowires6 randomly distributed on a glass substrate7. The positions of the nanowire ends with respect to predefined landmarks are precisely located using standard optical transmission microscopy before encapsulation in an electron-sensitive resist. Trenches representing the electrode layout are subsequently designed by electron-beam lithography. Metal electrodes are then fabricated by thermally evaporating a Cr/Au layer followed by a chemical lift-off. The contacted silver nanowires are finally transferred to a leakage radiation microscope for surface plasmon excitation and characterization8,9. Surface plasmons are launched in the nanowires by focusing a near infrared laser beam on a diffraction-limited spot overlapping one nanowire extremity5,9. For sufficiently large nanowires, the surface plasmon mode leaks into the glass substrate9,10. This leakage radiation is readily detected, imaged, and analyzed in the different conjugate planes in leakage radiation microscopy9,11. The electrical terminals do not affect the plasmon propagation. However, a current-induced morphological deterioration of the nanowire drastically degrades the flow of surface plasmons. The combination of surface plasmon leakage radiation microscopy with a simultaneous analysis of the nanowire electrical transport characteristics reveals the intrinsic limitations of such plasmonic circuitry.

Silver nanowires can simultaneously transport electrons and optical information in the form of surface plasmons. A procedure is described here to realize such a shared circuitry and the limitations at propagating both information carriers are evaluated.

Plasmonics is an emerging technology capable of simultaneously transporting a plasmonic signal and an electronic signal on the same information ...

Ohmic Contact Fabrication Using a Focused-ion Beam Technique and Electrical Characterization for Layer Semiconductor Nanostructures

Layer semiconductors with easily processed two-dimensional (2D) structures exhibit indirect-to-direct bandgap transitions and superior transistor performance, which suggest a new direction for the development of next-generation ultrathin and flexible photonic and electronic devices. Enhanced luminescence quantum efficiency has been widely observed in these atomically thin 2D crystals. However, dimension effects beyond quantum confinement thicknesses or even at the micrometer scale are not expected and have rarely been observed. In this study, molybdenum diselenide (MoSe2) layer crystals with a thickness range of 6-2,700 nm were fabricated as two- or four-terminal devices. Ohmic contact formation was successfully achieved by the focused-ion beam (FIB) deposition method using platinum (Pt) as a contact metal. Layer crystals with various thicknesses were prepared through simple mechanical exfoliation by using dicing tape. Current-voltage curve measurements were performed to determine the conductivity value of the layer nanocrystals. In addition, high-resolution transmission electron microscopy, selected-area electron diffractometry, and energy-dispersive X-ray spectroscopy were used to characterize the interface of the metal&#8211;semiconductor contact of the FIB-fabricated MoSe2 devices. After applying the approaches, the substantial thickness-dependent electrical conductivity in a wide thickness range for the MoSe2-layer semiconductor was observed. The conductivity increased by over two orders of magnitude from 4.6 to 1,500 &#937;&#8722;1 cm&#8722;1, with a decrease in the thickness from 2,700 to 6 nm. In addition, the temperature-dependent conductivity indicated that the thin MoSe2 multilayers exhibited considerably weak semiconducting behavior with activation energies of 3.5-8.5 meV, which are considerably smaller than those (36-38 meV) of the bulk. Probable surface-dominant transport properties and the presence of a high surface electron concentration in MoSe2 are proposed. Similar results can be obtained for other layer semiconductor materials such as MoS2 and WS2.

We describe the approaches for the device fabrication and electrical characterization of molybdenum diselenide (MoSe2) layer semiconductor nanostructures with different thicknesses. In addition, the fabrication of ohmic contacts for MoSe2-layer nanocrystals by the focused-ion beam deposition method using platinum (Pt) as a contact metal is described.

Layer semiconductors with easily processed two-dimensional (2D) structures exhibit indirect-to-direct bandgap transitions and superior transistor ...

Integration of Light Trapping Silver Nanostructures in Hydrogenated Microcrystalline Silicon Solar Cells by Transfer Printing

One of the potential applications of metal nanostructures is light trapping in solar cells, where unique optical properties of nanosized metals, commonly known as plasmonic effects, play an important role. Research in this field has, however, been impeded owing to the difficulty of fabricating devices containing the desired functional metal nanostructures. In order to provide a viable strategy to this issue, we herein show a transfer printing-based approach that allows the quick and low-cost integration of designed metal nanostructures with a variety of device architectures, including solar cells. Nanopillar poly(dimethylsiloxane) (PDMS) stamps were fabricated from a commercially available nanohole plastic film as a master mold. On this nanopatterned PDMS stamps, Ag films were deposited, which were then transfer-printed onto block copolymer (binding layer)-coated hydrogenated microcrystalline Si (&#181;c-Si:H) surface to afford ordered Ag nanodisk structures. It was confirmed that the resulting Ag nanodisk-incorporated &#181;c-Si:H solar cells show higher performances compared to a cell without the transfer-printed Ag nanodisks, thanks to plasmonic light trapping effect derived from the Ag nanodisks. Because of the simplicity and versatility, further device application would also be feasible thorough this approach.

A viable transfer printing-based methodology to introduce plasmonic metal nanostructures in solar cells is described. Using nanopillar poly(dimethylsiloxane) stamps, an Ag-based ordered nanodisk array was integrated with standard hydrogenated microcrystalline Si solar cells, which led to improved device performances due to plasmonic light trapping.

One of the potential applications of metal nanostructures is light trapping in solar cells, where unique optical properties of nanosized metals, commonly ...

A Fabrication Method for Highly Stretchable Conductors with Silver Nanowires

Stretchable electronics are identified as a key technology for electronic applications in the next generation. One of the challenges in fabrication of stretchable electronic devices is the preparation of stretchable conductors with great mechanical stability. In this study, we developed a simple fabrication method to chemically solder the contact points between silver nanowire (AgNW) networks. AgNW nanomesh was first deposited on a glass slide via spray coating method. A reactive ink composed of silver nanoparticle (AgNPs) precursors was applied over the spray coated AgNW thin films. After heating for 40 min, AgNPs were preferentially generated over the nanowire junctions to solder the AgNW nanomesh, and reinforced the conducting network. The chemically modified AgNW thin film was then transferred to polyurethane (PU) substrates by casting method. The soldered AgNW thin films on PU exhibited no obvious change in electrical conductivity under stretching or rolling process with elongation strains up to 120%.

A simple synthesis method is used to chemically solder silver nanowire thin film to fabricate highly stretchable and conductive metal conductors.

Stretchable electronics are identified as a key technology for electronic applications in the next generation. One of the challenges in fabrication of ...

Challenges in Rheological Characterization of Highly Concentrated Suspensions &#8212; A Case Study for Screen-printing Silver Pastes

A comprehensive rheological characterization of highly concentrated suspensions or pastes is mandatory for a targeted product development meeting the manifold requirements during processing and application of such complex fluids. In this investigation, measuring protocols for a conclusive assessment of different process relevant rheological parameters have been evaluated. This includes the determination of yield stress, viscosity, wall slip velocity, structural recovery after large deformation and elongation at break as well as tensile force during filament stretching.
The importance of concomitant video recordings during parallel-plate rotational rheometry for a significant determination of rheological quantities is demonstrated. The deformation profile and flow field at the sample edge can be determined using appropriate markers. Thus, measurement parameter settings and plate roughness values can be identified for which yield stress and viscosity measurements are possible. Slip velocity can be measured directly and measuring conditions at which plug flow, shear banding or sample spillover occur can be identified clearly. 
Video recordings further confirm that the change in shear moduli observed during three stage oscillatory shear tests with small deformation amplitude in stage I and III but large oscillation amplitude in stage II can be directly attributed to structural break down and recovery. For the pastes investigated here, the degree of irreversible, shear-induced structural change increases with increasing deformation amplitude in stage II until a saturation is reached at deformations corresponding to the crossover of G' and G'', but the irreversible damage is independent of the duration of large amplitude shear. 
A capillary breakup elongational rheometer and a tensile tester have been used to characterize deformation and breakup behavior of highly filled pastes in uniaxial elongation. Significant differences were observed in all experiments described above for two commercial screen-printing silver pastes used for front side metallization of Si-solar cells.

Challenges in Rheological Characterization of Highly Concentrated Suspensions &amp;#8212; A Case Study for Screen-printing Silver Pastes

A protocol for a robust and application relevant rheological characterization of highly concentrated suspensions is presented. Silver pastes used for screen-printing application in solar cell production are employed as model systems.

A comprehensive rheological characterization of highly concentrated suspensions or pastes is mandatory for a targeted product development meeting the ...

A Standard and Reliable Method to Fabricate Two-Dimensional Nanoelectronics

Two-dimensional (2D) materials have attracted huge attention due to their unique properties and potential applications. Since wafer scale synthesis of 2D materials is still in nascent stages, scientists cannot fully rely on traditional semiconductor techniques for related research. Delicate processes from locating the materials to electrode definition need to be well controlled. In this article, a universal fabrication protocol required in manufacturing nanoscale electronics, such as 2D quasi-heterojunction bipolar transistors (Q-HBT), and 2D back-gated transistors are demonstrated. This protocol includes the determination of material position, electron beam lithography (EBL), metal electrode definition, et al. A step by step narrative of the fabrication procedures for these devices are also presented. Furthermore, results show that each of the fabricated devices has achieved high performance with high repeatability. This work reveals a comprehensive description of process flow for preparing 2D nano-electronics, enables the research groups to access this information, and pave the way toward future electronics.

The article aims to introduce a standard and reliable fabrication procedure for the development of future low dimensional nanoelectronics.

Two-dimensional (2D) materials have attracted huge attention due to their unique properties and potential applications. Since wafer scale synthesis of 2D ...

Fabrication of Robust Nanoscale Contact between a Silver Nanowire Electrode and CdS Buffer Layer in Cu(In,Ga)Se2 Thin-film Solar Cells

Silver nanowire transparent electrodes have been employed as window layers for Cu(In,Ga)Se2 thin-film solar cells. Bare silver nanowire electrodes normally result in very poor cell performance. Embedding or sandwiching silver nanowires using moderately conductive transparent materials, such as indium tin oxide or zinc oxide, can improve cell performance. However, the solution-processed matrix layers can cause a significant number of interfacial defects between transparent electrodes and the CdS buffer, which can eventually result in low cell performance. This manuscript describes how to fabricate robust electrical contact between a silver nanowire electrode and the underlying CdS buffer layer in a Cu(In,Ga)Se2 solar cell, enabling high cell performance using matrix-free silver nanowire transparent electrodes. The matrix-free silver nanowire electrode fabricated by our method proves that the charge-carrier collection capability of silver nanowire electrode-based cells is as good as that of standard cells with sputtered ZnO:Al/i-ZnO as long as the silver nanowires and CdS have high-quality electrical contact. The high-quality electrical contact was achieved by depositing an additional CdS layer as thin as 10 nm onto the silver nanowire surface.

Fabrication of Robust Nanoscale Contact between a Silver Nanowire Electrode and CdS Buffer Layer in CuIn,GaSe2 Thin-film Solar Cells

In this protocol, we describe the detailed experimental procedure for the fabrication of a robust nanoscale contact between a silver nanowire network and CdS buffer layer in a CIGS thin-film solar cell.

Silver nanowire transparent electrodes have been employed as window layers for Cu(In,Ga)Se2 thin-film solar cells. Bare silver nanowire electrodes ...

Spectral and Angle-Resolved Magneto-Optical Characterization of Photonic Nanostructures

Photonic crystals are periodic nanostructures that can support a variety of confined electromagnetic modes. Such confined modes are usually accompanied by local enhancement of electric field intensity that strengthens light-matter interactions, enabling applications such as surface-enhanced Raman scattering (SERS) and surface plasmon enhanced sensing. In the presence of magneto-optically active materials, the local field enhancement gives rise to anomalous magneto-optical activity. Typically, the confined modes of a given photonic crystal depend strongly on the wavelength and incidence angle of the incident electromagnetic radiation. Thus, spectral and angular-resolved measurements are needed to fully identify them as well as to establish their relationship with the magneto-optical activity of the crystal. In this article, we describe how to use a Fourier-plane (back focal plane) microscope to characterize magneto-optically active samples. As a model system, here we use a plasmonic grating built out of magneto-optically active Au/Co/Au multilayer. In the experiments, we apply a magnetic field on the grating in situ and measure its reciprocal space response, obtaining the magneto-optical response of the grating over a range of wavelengths and incident angles. This information enables us to build a complete map of the plasmonic band structure of the grating and the angle and wavelength dependent magneto-optical activity. These two images allow us to pinpoint the effect that the plasmon resonances have on the magneto-optical response of the grating. The relatively small magnitude of magneto-optical effects requires a careful treatment of the acquired optical signals. To this end, an image processing protocol for obtaining magneto-optical response from the acquired raw data is laid out.

Photonic band structure enables understanding how confined electromagnetic modes propagate within a photonic crystal. In photonic crystals that incorporate magnetic elements, such confined and resonant optical modes are accompanied by enhanced and modified magneto-optical activity. We describe a measurement procedure to extract the magneto-optical band structure by Fourier space microscopy.

Photonic crystals are periodic nanostructures that can support a variety of confined electromagnetic modes. Such confined modes are usually accompanied by ...

Macro-Rheology Characterization of Gill Raker Mucus in the Silver Carp, Hypophthalmichthys molitrix

The silver carp, Hypophthalmichthys molitrix, is an invasive planktivorous filter feeder fish that infested the natural waterways of the upper Mississippi River basin due to its highly efficient filter feeding mechanism. The characteristic organs called gill rakers (GRs), found in many such filter feeders, facilitate the efficient filtration of food particles such as phytoplankton that are of a few microns in size.
The motivation to investigate the rheology of the GR mucus stems from our desire to understand its role in aiding the filter feeding process in the silver carp. The mucus-rich fluid, in a &#8216;thick and sticky&#8217; state may facilitate the adhesion of food particulates. The permeation and transport through the GR membrane are&#160;facilitated by the action of external shear forces that induce varying shear strain rates. Therefore, mucus rheology can provide a vital clue to the tremendous outcompeting nature of the silver carp within the pool of filter feeding fish. Based on this it was posited that GR mucus may provide an adhesive function to food particles and act as a transport vehicle to assist in the filter feeding process.
The main objective of the protocol is to determine the yield stress of the mucus, attributed to the minimum shear stress required to initiate flow at which irreversible plastic deformation is first observed across a structured viscoelastic material. Accordingly, rheological properties of the GR mucus, i.e., viscosity, storage, and loss moduli, were investigated for its non-Newtonian, shear-thinning nature using a rotational rheometer. &#160;
A protocol presented here is employed to analyze the rheological properties of mucus extracted from the gill rakers of a silver carp, fished at Hart Creek location of the Missouri River. The protocol aims to develop an effective strategy for rheological testing and material characterization of mucus assumed to be a structured viscoelastic material.

Macro-Rheology Characterization of Gill Raker Mucus in the Silver Carp, Hypophthalmichthys molitrix

This protocol presents a method to perform rheology characterization of mucus that resides on gill rakers (GRs) of the silver carp. Viscoelastic characteristics of GR-mucus, obtained by measuring viscosity, storage and loss moduli, are evaluated for the apparent yield stress to understand the filter feeding mechanism in GRs.

The silver carp, Hypophthalmichthys molitrix, is an invasive planktivorous filter feeder fish that infested the natural waterways of the upper Mississippi ...