radio frequency magnetron sputtering of bi2te3 and sb2te3 thermoelectric thin films on glass substrates

Deposition of Bi&lt;sub&gt;2&lt;/sub&gt;Te&lt;sub&gt;3&lt;/sub&gt; and Sb&lt;sub&gt;2&lt;/sub&gt;Te&lt;sub&gt;3&lt;/sub&gt; Thin Films on Glass Substrates via RF Sputtering

Thermoelectric (TE) materials have been attracting a considerable amount of research interest regarding their ability to convert thermal energy into electricity via the Seebeck effect1 and refrigeration via Peltier cooling2. The conversion efficiency of TE material is determined by the temperature difference between the hot end of the TE leg and the cold end. Generally, the higher the temperature difference, the higher the TE figure of merit and the higher its efficiency3. TE works with no requirement for additional mechanical parts involving gas or liquid in its process, producing no waste or pollution, making it environmentally safe and considered a green energy harvesting system.
Bismuth telluride, Bi2Te3, and its alloys remain the most important class of TE material. Even in thermoelectric power generation, such as the recovery of waste heat, Bi2Te3 alloys are most commonly used due to their superior efficiency up to 200 &#176;C4 and remain an excellent TE material at ambient temperature despite the zT value of more than 2 in various TE materials5. Several published papers have studied the TE properties of this material, which shows that the stoichiometric Bi2Te3 has a negative Seebeck coefficient6,7,8, indicating n-type properties. However, this compound can be adjusted to p- and n-type by alloying with antimony telluride (Sb2Te3) and bismuth selenide (Bi2Se3), respectively, which can increase their bandgap and reduce bipolar effects9.
Antimony telluride, Sb2Te3 is another well-established TE material with high figure of merit at low temperature. While stoichiometric Bi2Te3 is a great TE with n-type properties, Sb2Te3 has p-type properties. In some cases, the properties of TE materials often depend on the atomic composition of the material such as the n-type Te-rich Bi2Te3, but a p-type Bi-rich Bi2Te3 due to BiTe antisite acceptor defects4. However, Sb2Te3 is always p-type due to comparatively low formation energy of SbTe antisite defects, even in Te-rich Sb2Te34. Thus, these two materials become suitable candidates to fabricate p-n module of thermoelectric generator for various applications.
The current conventional TEGs are made of diced ingots of n-type and p-type semiconductors connected vertically in series10. They have only been used in niche fields due to their low efficiency and bulky, rigid nature. Over time, researchers have started to explore thin film structures for better performance and application. It is reported that thin film TE have advantages over their bulky counterpart such as higher zT due to their low thermal conductivity11,12, less amount of material and easier integration with integrated circuit12. As a result, niche TE research on thin film thermoelectric devices has been on the rise benefitting from the advantages of nanomaterial structure13,14.
Microfabrication of thin film is important to attain high performance TE materials. Various deposition approaches have been researched and developed including chemical vapor deposition15, atomic layer deposition16,17, pulsed laser deposition18,19,20, screen printing8,21, and molecular beam epitaxy22 to serve this purpose. However, the majority of these techniques suffer from high operation cost, complex growth process or complicated material preparation. On the contrary, magnetron sputtering is a cost-effective approach for producing high-quality thin films that are denser, exhibit smaller grain size, have better adhesion, and high uniformity23,24,25.
Magnetron sputtering is one of the plasma-based physical vapor deposition (PVD) processes which is widely used in various industrial applications. Sputtering process works when sufficient voltage is applied to a target (cathode), ions from the glow discharge plasma bombards the target and release not only secondary electrons, but also atoms of the cathode materials which eventually impact the surface of the substrate and condense as a thin film. Sputtering process was first commercialized in 1930s and improved in 1960s, gaining significant interest due to its ability to deposit wide range of materials using direct current (DC) and RF sputtering26,27. The magnetron sputtering overcomes low deposition rate and high substrate heating impact by utilizing magnetic field. The strong magnet confines the electrons in the plasma at or near the surface of the target and prevent damage to the formed thin film. This configuration preserves the stoichiometry and thickness uniformity of the deposited thin film28.
The preparation of Bi2Te3 and Sb2Te3 thermoelectric thin films using magnetron sputtering method has also been extensively studied, incorporating technique such as doping4,29,30 and annealing31 in the procedures, leading to different performance and quality. Study by Zheng et al.32 uses thermally induced diffusion method to diffuse Ag-doped Bi and Te layer which were sputtered separately. This method enables precise control on the composition of the thin films and the diffusion of Te by thermal induction protects the Te from being volatilized. The properties of the thin films can also be enhanced by pre-coating process33 before sputtering which results in better electrical conductivity due to high carrier mobility, consequently enhancing the power factor. Other than that, study by Chen et al.34 improved the thermoelectric performance of sputtered Bi2Te3 by doping Se via post-selenization diffusion reaction method. During the process, Se vaporizes and diffuses into the Bi-Te thin films to form Bi-Te-Se films, which results in 8-fold higher power factor than undoped Bi2Te3.
This paper describes our experimental setup and procedure for the RF magnetron sputtering technique to deposit Bi2Te3 and Sb2Te3 thin films on glass substrates. Sputtering was performed in a top-down configuration as shown in the schematic diagram in Figure 1, cathode was mounted at an angle to the substrate normal, leading to a more concentrated and convergent plasma to the substrate. The films were systematically characterized using FESEM, EDX, Hall effect and Seebeck coefficient measurement to study their surface morphology, thickness, composition, and thermoelectric properties.
<img alt="Figure 1" class="xfigimg" src="/files/ftp_upload/66248/66248fig01.jpg" /> 
Figure 1: A schematic of the top-down configuration sputter. The diagram was designed according, but not to scale, to the actual sputtering configuration available for this study including the arrangement of glass substrates to be sputtered viewed from the top. <a href="https://www.jove.com/files/ftp_upload/66248/66248fig01large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>

Author Spotlight: Advancements in High-Performance Thermoelectric Thin Films Through Radio Frequency Magnetron Sputtering

Fabrication of Bi2Te3 and Sb2Te3 Thermoelectric Thin Films using Radio Frequency Magnetron Sputtering Technique

Our research focuses on fabricating high-quality thin films for thermoelectric generators to recover waste heat and turn it into electricity. Various thin film deposition technique have been researched and developed, including radio frequency magnetron sputtering that is able to produce high-density, robust thin films with better adhesion and high uniformity. This method does not require melting and evaporation of the target materials, enabling most of materials to be deposited regardless of their melting temperature, making it superior than other physical vapor deposition technologies.

Radio Frequency Magnetron Sputtering of Bi2Te3 and Sb2Te3 Thermoelectric Thin Films on Glass Substrates

radio-frequency-magnetron-sputtering-bi2te3-sb2te3-thermoelectric

Research

JoVE Journal

Engineering

494 次观看.  Universiti Kebangsaan Malaysia. 首先，从喷枪上取下铝制护罩并将目标材料放在盖子的中心。牢固地拧紧磁控管支架上的盖子并重新安装铝制屏蔽罩。用铝箔包裹腔体、喷枪和样品架。使用万用表检查腔体、腔体和枪以及腔体和目标之间的分类电路。然后关上门，在腔室中开始吸尘过程 15 到 30 分钟。在吸尘开始时，用力将门和机身压在一起，以确保紧密密封。监控压力表以确认压力下降。现在?...

视频: 玻璃基板上Bi2te3 和Sb2te3 热电薄膜的射频磁控溅射

Through various studies on thermoelectric (TE) materials, thin film configuration gives superior advantages over conventional bulk TEs, including adaptability to curved and flexible substrates. Several different thin film deposition methods have been explored, yet magnetron sputtering is still favorable due to its high deposition efficiency and scalability. Therefore, this study aims to fabricate a bismuth telluride (Bi2Te3) and antimony telluride (Sb2Te3) thin film via the radio frequency (RF) magnetron sputtering method. The thin films were deposited on soda lime glass substrates at ambient temperature. The substrates were first washed using water and soap, ultrasonically cleaned with methanol, acetone, ethanol, and deionized water for 10 min, dried with nitrogen gas and hot plate, and finally treated under UV ozone for 10 min to remove residues before the coating process. A sputter target of Bi2Te3 and Sb2Te3 with Argon gas was used, and pre-sputtering was done to clean the target&#39;s surface. Then, a few clean substrates were loaded into the sputtering chamber, and the chamber was vacuumed until the pressure reached 2 x 10-5 Torr. The thin films were deposited for 60 min with Argon flow of 4 sccm and RF power at 75 W and 30 W for Bi2Te3 and Sb2Te3, respectively. This method resulted in highly uniform n-type Bi2Te3 and p-type Sb2Te3 thin films.

The manuscript describes a protocol for radio frequency magnetron sputtering of Bi2Te3 and Sb2Te3 thermoelectric thin films on glass substrates, which represents a reliable deposition method that provides a wide range of applications with the potential for further development.