This work has been financially supported by NSERC, CSEE, nanoBridge and TRLabs.

As mentioned above, the two key steps in the AAO-based fabrication process are (a) synthesis of the empty AAO template on arbitrary (primarily conductive and/or transparent) substrates (schematic description in Figure 1) and (b) growth of small molecular organic nanowires within the nanopores of the AAO template (Figure 2). In this section we provide a detailed description of these processes.
1. Growth of Anodic Aluminum Oxide (AAO) Templates on Conductive Aluminum Substrates
<ol>
	<li>Create nanoporous alumina templates by first polishing aluminum foils and then anodizing (or electrochemically oxidizing) them. Begin by cutting out small (~2 x 2 cm2) sheets of high purity unpolished aluminum (99.997%) with thickness 250 &mu;m.</li>
	<li>In lieu of electropolishing, a simpler chemical polishing process 18 is used. Submerge a small number of 2 x 2 cm2 sheets in nitric-phosphoric acid etchant at 80 &deg;C on a hotplate for 5 min.</li>
</ol>
Note: The nitric-phosphoric acid solution used to pre-treat the aluminum sheets is 15 parts 68% nitric acid and 85 parts 85% phosphoric acid. A polishing step is necessary prior to anodization because surface roughness of as-purchased aluminum is of the order of few microns, which creates a non-uniform electric field at the surface and prevents formation of an ordered pore array. In literature, electropolishing has been used extensively for this purpose 2,3. However, chemical polishing is a cheap and easy alternative, which also yields polished surfaces with comparable (or better) smoothness 18.
<ol start="3">
	<li>After etching, neutralize the foils in 1 M sodium hydroxide for 20 min. These "chemically polished" foils are now ready to be anodized.</li>
	<li>Load the polished aluminum sheets in to flat cells and anodize them for 15 min with 3% oxalic acid at 40 V DC bias.</li>
</ol>
Note: For foil samples a two-step anodization process is performed to improve pore ordering 2,3,19. This first step will create a porous oxide layer on the Al surface and nano-scale dimples at the aluminum/alumina interface, which act as the initiation sites for pore growth during the second step of anodization.
<ol start="5">
	<li>Etch the sample in chromic-phosphoric acid by removing it from the flat cell. Immerse the sample in a beaker of the etchant on a hot plate at 60 &deg;C for ~30 min to remove the initial oxide layer.</li>
	<li>Repeat the anodization process (step 1.4) for 2.5 min while keeping all other parameters unchanged. Try to realign the foil in the flat cell such that the same area anodized in step (1.4) will again be exposed to the electrolyte.</li>
</ol>
Note: The time of the final anodization step determines the thickness of the final oxide layer and can be altered accordingly. Duration of 2.5 min. corresponds to a film thickness (pore length) of ~500 nm. At the end of the second step a well-ordered nanopore array is created in the anodic alumina layer. The anodization and etching cycle can be repeated to further improve pore ordering.
<ol start="7">
	<li>Submerge the template in 5% phosphoric acid at room temperature for 40 min to thin the barrier layer at the bottom of the nanopores and widen the nanopore diameter. Final nanopore diameter after this step is ~60-70 nm.</li>
</ol>
2. Growth of AAO Templates on Transparent Substrates (Glass)
<ol>
	<li>Deposit the following multilayer system sequentially on cleaned glass slides: TiO2 (20 nm, atomic layer deposition), Au (7 nm, sputtering), Al (1 &mu;m, sputtering).</li>
</ol>
Note: The Au layer acts as an electrode, required for anodization, and does not deteriorate transparency 20. The TiO2 acts as a transparent adhesion layer between the Au and glass substrate.
<ol start="2">
	<li>Attach a foil electrode to the surface of the thin film of aluminum to be anodized using a conductive silver epoxy. This will result in a proper connection from power source to sample while improving current distribution.</li>
</ol>
Note: Since there is very little aluminum deposited on the glass substrate, polishing techniques mentioned before are not viable to flatten the aluminum surface. Instead, this protocol modifies the anodization procedure to incorporate another anodization/etching step.
<ol start="3">
	<li>Load the sample in to the flat cell and anodize the aluminum thin film for 4 min using 3% oxalic acid at 30 V DC bias.</li>
	<li>Without removing the sample from the flat cell, rinse the cell out with DI water and etch the template in chromic-phosphoric acid at 60 &deg;C for 1 hr by pouring the hot etchant in to the cell.</li>
</ol>
Note: The temperature of the etchant will immediately start to decrease once it has been poured in to the cell. Therefore, the duration of etching is increased to 1 hr from 30 min for the foil samples to ensure all oxidized film is removed.
<ol start="5">
	<li>Rinse out the cell again and anodize a second time under the same conditions as the first; for 4 min, using 3% oxalic acid at 30 V DC bias.</li>
	<li>Repeat step (2.4). Without removing the sample from the flat cell, rinse the cell out with DI water and etch the template in chromic-phosphoric acid at 60 &deg;C for 1 hr by pouring the hot etchant in to the cell.</li>
	<li>Rinse the cell out for the final time and perform the third (and last) anodization step, using 3% oxalic acid at 30 V DC. Monitor the current of the system to determine when to stop.</li>
</ol>
Note: The current needs to be monitored during the final anodization. After the first few seconds, the current stabilizes at around 1-2 mA. This indicates uniform anodization is taking place. Once the anodization process has consumed the remaining aluminum, the electrolyte solution (3% oxalic acid) will come in to contact with the underlying gold layer, which will cause a sharp increase in the anodization current (Figure 3). At this point, the anodization is stopped. The time should be roughly around the 4 min mark. This rise in current is not observed in foil samples (Figure 3) because a uniform barrier layer separates the solution and metal substrate.
<ol start="8">
	<li>Perform a pore widening step, similar to the foil sample protocol by submerging the template in 5% phosphoric acid at room temperature for 40 min.</li>
</ol>
Note: This will widen the pores but since the anodization process has eaten through the barrier layer there is none left to thin. Figure 4 shows the layered structure of glass substrate / 20 nm TiO2 / 7 nm Au / 500 nm porous Al2O3 with the absence of a barrier layer and pores clearly exposed to underlying Au thin film. Figure 5a and 5b shows empty AAO templates on foil and glass substrates respectively.
3. Centrifuge Assisted Growth of Small Molecular Organic Nanowires Within the Pores of AAO Template
<ol>
	<li>Prepare a saturated solution of the small molecular organic in a suitable solvent.</li>
</ol>
Note: The following organic molecules and solvents have been used: rubrene in acetone, Alq3 in chloroform and PCBM in toluene. From here on PCBM is referred to as the molecule of interest.
<ol start="2">
	<li>Load the templates in to the bottom of a centrifuge test tube such that the anodized area is facing the top of the test tube. The tube must be large enough to fit the sample inside.</li>
</ol>
Note: For foil samples, it is helpful to use a wafer of similar size to support the foil and prevent bending during centrifugation as described below. Figure 2 shows a schematic description of how the sample is mounted in the centrifuge.
<ol start="3">
	<li>Use a pipette to fill the test tube with enough PCBM solution such that the template is completely submerged.</li>
	<li>Load the test tube in the centrifuge and run for 5 min at 6,000 rpm.</li>
</ol>
Note: If the samples were mounted in the test tube at an angle, ensure the test tube is mounted in such a way that the anodized surface is pointing towards the center of the centrifuge (Figure 2).
<ol start="5">
	<li>Once the centrifuge has stopped, unload the test tubes and pour out the PCBM solution from the tubes.</li>
	<li>Remove the templates from the test tubes, or leave them at the bottom, for ~1 min to dry.</li>
	<li>Repeat steps 3.2-3.6 so that a total of 5-10 centrifuge runs have been performed.</li>
</ol>
Note: In situations where there is low solubility of the small molecule in its solvent, more centrifuge runs will help deposit more material in the nanopores.
<ol start="8">
	<li>Remove the sample from the bottom of the test tube and use a cotton swab soaked in toluene (or the respective solvent) to gently clean the surface of the template, removing any material that is left over on the surface of the template.</li>
</ol>

<ol>
	<li>Martin, C. R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Nanomaterials:+a+membrane-based+synthetic+approach.">Nanomaterials: a membrane-based synthetic approach.</a> Science. , (1994).</li><li>Pramanik, S., Kanchibotla, B., Sarkar, S., Tepper, G., Bandyopadhyay, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Electrochemical+Self-Assembly+of+Nanostructures:+Fabrication+and+Device+Applications.">Electrochemical Self-Assembly of Nanostructures: Fabrication and Device Applications.</a> Encyclopedia of Nanoscience and Nanotechnology. 13, 273-332 (2011).</li><li>Kanchibotla, B., Pramanik, S., Bandyopadhyay, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Self-assembly+of+nanostructures+using+nanoporous+alumina+template.">Self-assembly of nanostructures using nanoporous alumina template.</a> Nano and Molecular Electronics Handbook. Chapter 9, (2007).</li><li>Pramanik, S., Stefanita, C. -. G., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Observation+of+extremely+long+spin+relaxation+times+in+an+organic+nanowire+spin+valve.">Observation of extremely long spin relaxation times in an organic nanowire spin valve.</a> Nat. Nano. 2 (4), 216-219 (2007).</li><li>Alam, K. M., Bodepudi, S. C., Starko-Bowes, R., Pramanik, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Suppression+of+spin+relaxation+in+rubrene+nanowire+spin+valves.">Suppression of spin relaxation in rubrene nanowire spin valves.</a> Applied Physics Letters. 101 (19), 192403 (2012).</li><li>Alam, K. M., Singh, A. P., Starko-Bowes, R., Bodepudi, S. C., Pramanik, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Template-Assisted+Synthesis+of+&#960;-Conjugated+Molecular+Organic+Nanowires+in+the+Sub-100+nm+Regime+and+Device+Implications.">Template-Assisted Synthesis of &#960;-Conjugated Molecular Organic Nanowires in the Sub-100 nm Regime and Device Implications.</a> Advanced Functional Materials. 22 (15), 3298-3306 (2012).</li><li>Zhang, D., Luo, L., Liao, Q., Wang, H., Fu, H., Yao, J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Polypyrrole/ZnS+Core/Shell+Coaxial+Nanowires+Prepared+by+Anodic+Aluminum+Oxide+Template+Methods.">Polypyrrole/ZnS Core/Shell Coaxial Nanowires Prepared by Anodic Aluminum Oxide Template Methods.</a> The Journal of Physical Chemistry C. 115 (5), 2360-2365 (2011).</li><li>Kim, F. S., Ren, G., Jenekhe, S. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=One-Dimensional+Nanostructures+of+&#960;-Conjugated+Molecular+Systems:+Assembly,+Properties,+and+Applications+from+Photovoltaics,+Sensors,+and+Nanophotonics+to+Nanoelectronics.">One-Dimensional Nanostructures of &#960;-Conjugated Molecular Systems: Assembly, Properties, and Applications from Photovoltaics, Sensors, and Nanophotonics to Nanoelectronics.</a> Chem. Mater. 23 (3), 682-732 (2010).</li><li>Brock, T. D. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=.">.</a> Membrane filtration: a user's guide and reference manual. , (1983).</li><li>Valizadeh, S., George, J., Leisner, P., Hultman, L. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Electrochemical+deposition+of+Co+nanowire+arrays;+quantitative+consideration+of+concentration+profiles.">Electrochemical deposition of Co nanowire arrays; quantitative consideration of concentration profiles.</a> Electrochimica Acta. 47 (6), 865-874 (2001).</li><li>Nasirpouri, F., Southern, P., Ghorbani, M., Iraji zad, A., Schwarzacher, W. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=GMR+in+multilayered+nanowires+electrodeposited+in+track-etched+polyester+and+polycarbonate+membranes.">GMR in multilayered nanowires electrodeposited in track-etched polyester and polycarbonate membranes.</a> Journal of Magnetism and Magnetic Materials. 308 (1), 35-39 (2007).</li><li>Diggle, J. W., Downie, T. C., Goulding, C. W. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Anodic+oxide+films+on+aluminum.">Anodic oxide films on aluminum.</a> Chemical Reviews. 69 (3), 365-405 (1969).</li><li>Steinhart, M., Wehrspohn, R. B., G&#246;sele, U., Wendorff, J. H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Nanotubes+by+Template+Wetting:+A+Modular+Assembly+System.">Nanotubes by Template Wetting: A Modular Assembly System.</a> Angewandte Chemie International Edition. 43 (11), 1334-1344 (2004).</li><li>Al-Kaysi, R. O., Ghaddar, T. H., Guirado, G. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Fabrication+of+One-Dimensional+Organic+Nanostructures+Using+Anodic+Aluminum+Oxide+Templates.">Fabrication of One-Dimensional Organic Nanostructures Using Anodic Aluminum Oxide Templates.</a> Journal of Nanomaterials. 2009, 1-14 (2009).</li><li>Lee, J. W., Kim, K., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Light-Emitting+Rubrene+Nanowire+Arrays:+A+Comparison+with+Rubrene+Single+Crystals.">Light-Emitting Rubrene Nanowire Arrays: A Comparison with Rubrene Single Crystals.</a> Advanced Functional Materials. 19 (5), 704-710 (2009).</li><li>Pramanik, S., Bandyopadhyay, S., Garre, K., Cahay, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Normal+and+inverse+spin-valve+effect+in+organic+semiconductor+nanowires+and+the+background+monotonic+magnetoresistance.">Normal and inverse spin-valve effect in organic semiconductor nanowires and the background monotonic magnetoresistance.</a> Physical Review B. 74 (23), 235329 (2006).</li><li>Alam, K. M., Pramanik, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=High-field+magnetoresistance+in+nanowire+organic+spin+valves.">High-field magnetoresistance in nanowire organic spin valves.</a> Physical Review B. 83 (24), 245206 (2011).</li><li>Alam, K. M., Singh, A. P., Bodepudi, S. C., Pramanik, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Fabrication+of+hexagonally+ordered+nanopores+in+anodic+alumina:+An+alternative+pretreatment.">Fabrication of hexagonally ordered nanopores in anodic alumina: An alternative pretreatment.</a> Surface Science. 605 (3-4), 441-449 (2011).</li><li>Masuda, H., Hasegwa, F., Ono, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Self-Ordering+of+Cell+Arrangement+of+Anodic+Porous+Alumina+Formed+in+Sulfuric+Acid+Solution.">Self-Ordering of Cell Arrangement of Anodic Porous Alumina Formed in Sulfuric Acid Solution.</a> Journal of The Electrochemical Society. 144 (5), L127-L130 (1997).</li><li>Stec, H. M., Williams, R. J., Jones, T. S., Hatton, R. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Ultrathin+Transparent+Au+Electrodes+for+Organic+Photovoltaics+Fabricated+Using+a+Mixed+Mono-Molecular+Nucleation+Layer.">Ultrathin Transparent Au Electrodes for Organic Photovoltaics Fabricated Using a Mixed Mono-Molecular Nucleation Layer.</a> Advanced Functional Materials. 21 (9), 1709-1716 (2011).</li><li>Schettino, V., Pagliai, M., Ciabini, L., Cardini, G. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=The+Vibrational+Spectrum+of+Fullerene+C60.">The Vibrational Spectrum of Fullerene C60.</a> J. Phys. Chem. A. 105, 11192-11196 (2001).</li><li>Lee, Y., Lee, S., Kim, K., Lee, J., Han, K., Kim, J., Joo, J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Single+nanoparticle+of+organic+p-type+and+n-type+hybrid+materials:+nanoscale+phase+separation+and+photovoltaic+effect.">Single nanoparticle of organic p-type and n-type hybrid materials: nanoscale phase separation and photovoltaic effect.</a> J. Mater. Chem. 22, 2485-2490 (2012).</li><li>Bodepudi, S. C., Bachman, D., Pramanik, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Fabrication+of+Highly+Ordered+Cylindrical+Nanopores+with+Modulated+Diameter+Using+Anodic+Alumina.">Fabrication of Highly Ordered Cylindrical Nanopores with Modulated Diameter Using Anodic Alumina.</a> , 1-4 (2011).</li><li>Vlad, A., Melinte, S., M&#225;t&#233;fi-Tempfli, M., Piraux, L., M&#225;t&#233;fi-Tempfli, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Vertical+Nanowire+Architectures:+Statistical+Processing+of+Porous+Templates+Towards+Discrete+Nanochannel+Integration.">Vertical Nanowire Architectures: Statistical Processing of Porous Templates Towards Discrete Nanochannel Integration.</a> Small. 6 (18), 1974-1980 (2010).</li><li>Jo, S. H., Kim, K. -. H., Lu, W. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=High-Density+Crossbar+Arrays+Based+on+a+Si+Memristive+System.">High-Density Crossbar Arrays Based on a Si Memristive System.</a> Nano Letters. 9 (2), 870-874 (2009).</li><li>Haberkorn, N., Gutmann, J. S., Theato, P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Template-Assisted+Fabrication+of+Free-Standing+Nanorod+Arrays+of+a+Hole-Conducting+Cross-Linked+Triphenylamine+Derivative:+Toward+Ordered+Bulk-Heterojunction+Solar+Cells.">Template-Assisted Fabrication of Free-Standing Nanorod Arrays of a Hole-Conducting Cross-Linked Triphenylamine Derivative: Toward Ordered Bulk-Heterojunction Solar Cells.</a> ACS Nano. 3 (6), 1415-1422 (2009).</li><li>Aryal, M., Buyukserin, F., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Imprinted+large-scale+high+density+polymer+nanopillars+for+organic+solar+cells.">Imprinted large-scale high density polymer nanopillars for organic solar cells.</a> Journal of Vacuum Science &amp; Technology B: Microelectronics and Nanometer Structures. 26 (6), 2562 (2008).</li><li>Lee, J. H., Kim, D. W., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Enhanced+solar-cell+efficiency+in+bulk-heterojunction+polymer+systems+obtained+by+nanoimprinting+with+commercially+available+AAO+membrane+filters.">Enhanced solar-cell efficiency in bulk-heterojunction polymer systems obtained by nanoimprinting with commercially available AAO membrane filters.</a> Small (Weinheim an Der Bergstrasse, Germany). 5 (19), 2139-2143 (2009).</li><li>Allen, J. E., Black, C. T. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Improved+Power+Conversion+Efficiency+in+Bulk+Heterojunction+Organic+Solar+Cells+with+Radial+Electron+Contacts.">Improved Power Conversion Efficiency in Bulk Heterojunction Organic Solar Cells with Radial Electron Contacts.</a> ACS Nano. 5 (10), 7986-7991 (2011).</li><li>Slota, J. E., He, X., Huck, W. T. S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Controlling+nanoscale+morphology+in+polymer+photovoltaic+devices.">Controlling nanoscale morphology in polymer photovoltaic devices.</a> Nano Today. 5 (3), 231-242 (2010).</li><li>Chidichimo, G., Filippelli, L. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Organic+Solar+Cells:+Problems+and+Perspectives.">Organic Solar Cells: Problems and Perspectives.</a> International Journal of Photoenergy. 2010, 1-11 (2010).</li><li>O'Carroll, D. M., Fakonas, J. S., Callahan, D. M., Schierhorn, M., Atwater, H. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Metal-Polymer-Metal+Split-Dipole+Nanoantennas.">Metal-Polymer-Metal Split-Dipole Nanoantennas.</a> Advanced Materials. 24 (23), (2012).</li><li>Zheng, J. Y., Yan, Y., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Hydrogen+Peroxide+Vapor+Sensing+with+Organic+Core/Sheath+Nanowire+Optical+Waveguides.">Hydrogen Peroxide Vapor Sensing with Organic Core/Sheath Nanowire Optical Waveguides.</a> Advanced Materials. 24 (35), (2012).</li><li>Zhang, L., Meng, F., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=A+novel+ammonia+sensor+based+on+high+density,+small+diameter+polypyrrole+nanowire+arrays.">A novel ammonia sensor based on high density, small diameter polypyrrole nanowire arrays.</a> Sensors and Actuators B: Chemical. 142 (1), 204-209 (2009).</li><li>Cui, Q. H., Jiang, L., Zhang, C., Zhao, Y. S., Hu, W., Yao, J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Coaxial+Organic+p-n+Heterojunction+Nanowire+Arrays:+One-Step+Synthesis+and+Photoelectric+Properties.">Coaxial Organic p-n Heterojunction Nanowire Arrays: One-Step Synthesis and Photoelectric Properties.</a> Advanced Materials. 24 (17), 2332-2336 (2012).</li><li>Duvail, J. L., Long, Y., Cuenot, S., Chen, Z., Gu, C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Tuning+electrical+properties+of+conjugated+polymer+nanowires+with+the+diameter.">Tuning electrical properties of conjugated polymer nanowires with the diameter.</a> Applied Physics Letters. 90, 102114 (2007).</li><li>Briseno, A. L., Mannsfeld, S. C. B., Jenekhe, S. A., Bao, Z., Xia, Y. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Introducing+organic+nanowire+transistors.">Introducing organic nanowire transistors.</a> Materials Today. 11 (4), 38-47 (2008).</li><li>Kippelen, B., Br&#233;das, J. -. L. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Organic+photovoltaics.">Organic photovoltaics.</a> Energy &amp; Environmental Science. 2 (3), 251-261 (2009).</li><li>G&#252;nes, S., Neugebauer, H., Sariciftci, N. S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Conjugated+polymer-based+organic+solar+cells.">Conjugated polymer-based organic solar cells.</a> Chemical Reviews. 107 (4), 1324-1338 (2007).</li><li>Coakley, K. M., McGehee, M. D. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Conjugated+Polymer+Photovoltaic+Cells.">Conjugated Polymer Photovoltaic Cells.</a> Chem. Mater. 16 (23), 4533-4542 (2004).</li></ol>

The authors declare that they have no competing financial interests.

Physical Picture for Nanowire Growth
It is first important to fully understand the growth method of the organic nanowires. Once we know exactly how they grow and form themselves in the pores we can use this deposition method to engineer nanostructures, devices and materials. In the past, polymer nanowires have been fabricated using the template wetting procedure without the assistance of a centrifuge, but for some materials such as organic small molecules, we have found this to be ineffective. D...

A template-assisted method is commonly used for the fabrication of vertically oriented nanowire arrays 1-3. This method allows straightforward fabrication of complex nanowire geometries such as an axially 4-6 or radially 7 heterostructured nanowire superlattice, which are often desirable in various electronic and optical applications. In addition, this is a low-cost, bottom-up nanosynthesis method with high throughput and versatility. As a result, template-directed methods have gained immense popularity among researchers worldwide 2,3.
The basic idea of the "template-directed method" is as follows. First a template is fabricated, which contains an array of vertically oriented cylindrical nanopores. Next, the desired material is deposited within the nanopores until the pores are filled. As a result the desired material adopts the pore morphology and forms a nanowire array hosted within the template. Finally, depending on the target application, the host template may be removed. However, this also destroys the vertical order. The geometry and dimensions of the final nanostructures mimic the pore morphology and hence synthesis of the host template is a critical part of the fabrication process.
Various types of nanoporous templates have been reported in literature 8. The most commonly used templates include (a) polymer track-etched membranes, (b) block copolymers and (c) anodic aluminum oxide (AAO) templates. To create the polymer track etched membranes a polymer foil is irradiated with high-energy ions, which completely penetrate the foil and leave latent ion tracks within the bulk foil 9. The tracks are then selectively etched to create nanosized channels within the polymer foil 9. The nanosized channels can be further widened by a suitable etching step. Key problems with this method are the non-uniformity of the nanochannels, lack of control of location, non-uniform relative distance between the channels, low density (number of channels per unit area ~108/cm2), and poorly ordered porous structure 1. In the block copolymer method a similar cylindrical nanoporous template is first created, followed by the growth of desired material within the pores 8.
In the past, methods (a) and (b) mentioned above have been used to fabricate polymer nanowires 8. However, these methods may not be suitable for synthesizing nanowires of any arbitrary organic material due to the potential absence of selective etching during post-processing steps. Post-processing typically involves removal of the host template, which for the above-mentioned templates would require organic solvents. Such solvents may have deleterious effect on the structural and physical properties of the organic nanowires. However, these templates work as ideal hosts for inorganic nanowires such as cobalt 10, nickel, copper and metallic multilayers 11, which remain unaffected in the etching process that removes the polymer host. Another potential challenge for the above-mentioned methods is the poor thermal stability of the host matrix at higher temperatures. High temperature annealing is often required to improve crystallinity of the organic nanowires, which indicates the necessity of good thermal stability of the host matrix.
Controlled electrochemical oxidation of aluminum (also known as "anodization" of aluminum) is a well-known industrial process and is commonly used in the automobile, cookware, aerospace and other industries to protect aluminum surface from corrosion 12. The nature of the oxidized aluminum (or "anodic alumina") depends critically on the pH of the electrolyte used for anodization. For corrosion-resistance applications, anodization is generally performed with weak acids (pH ~5-7), which create a compact, non-porous, "barrier-type" alumina film 12. However, if the electrolyte is strongly acidic (pH &lt; 4), the oxide becomes "porous" due to local dissolution of the oxide by the H+ ions. The local electric field across the oxide determines the local concentration of the H+ ions and hence surface pre-patterning prior to anodization offers some control over the final porous structure. The pores are cylindrical, with small diameter (~10-200 nm) and hence such nanoporous anodic alumina films have been used extensively in recent years for synthesizing nanowires of various materials 2,3.
Nanoporous anodic alumina templates offer better thermal stability, high pore density, long-range pore order, and excellent tunability of pore diameter, length, inter-pore separation and pore density via judicious choice of anodization parameters such as pH of the electrolyte and anodization voltage 2,3. Due to these reasons we choose AAO templates as the host matrix for the organic nanowire growth. Further, inorganic oxides such as alumina have high surface energy, thus facilitating uniform spreading of the organic solution (low surface energy) on the alumina surface 13. In addition, our goal is to grow these nanowire arrays directly on a conductive and/or transparent substrate. As a result, the pore is closed at the bottom end, which needs additional consideration as we describe below. Growth of nanowires within a through-pore template and subsequent transfer to the desired substrate is often undesirable due to poor interface quality and this method is not even feasible for short-length nanowires (or thin templates) due to poor mechanical stability of the thin templates.
&pi;-conjugated organic materials can be broadly classified into two categories: (a) long-chain conjugated polymers and (b) small molecular weight organic semiconductors. Many groups have reported synthesis of long chain polymer nanowires within the cylindrical nanopores of an AAO template in the past. Comprehensive review on this topic is available in refs 8,14. However, synthesis of nanowires of commercially important small molecular organics (such as rubrene, tris-8-hydroxyquinoline aluminum (Alq3), and PCBM) in AAO is extremely rare. Physical vapor deposition of rubrene and Alq3 within the nanopores of AAO template has been reported by several groups 4,15-17. However, only a thin layer (~30 nm) of organics can be deposited within the pores (~50 nm diameter) and prolonged deposition tends to block the pore entrance 4,16,17. Complete pore filling can be achieved in this method if the pore diameter is sufficiently large (~200 nm) 15. Thus it is important to find an alternative method that is applicable for pore diameters in the sub 100 nm range.
Another approach that has been used for some other small-molecular organics is a so-called "template wetting" method 8,14. However, in most reports thick commercial templates (~50 &mu;m) with both side open pores and large diameter (~200 nm) have been used. Such method has not produced nanowires in one-side closed pores as mentioned before, presumably due to the presence of trapped air pockets within the pores, which prevents infiltration of the solution within the pores. We have previously reported a novel method that overcomes these challenges and allows growth of small molecular organic nanowire arrays with arbitrary dimensions on any desired substrate. In what follows, we will describe the detailed protocol, potential limitations and future modifications.

<table border="1">
		<tbody>
		 <tr>
			<td></td>
			<td></td>
			<td></td>
			<td>Reagents</td>
		 </tr>
		 <tr>
			<td>Toluene</td>
			<td>Fisher Scientific</td>
			<td>T324-4</td>
			<td></td>
		 </tr>
		 <tr>
			<td>68% Nitric Acid</td>
			<td>Fisher Scientific</td>
			<td>A200-212</td>
			<td></td>
		 </tr>
		 <tr>
			<td>85% Phosphoric Acid</td>
			<td>Fisher Scientific</td>
			<td>A242-4</td>
			<td></td>
		 </tr>
		 <tr>
			<td>10% Chromic Acid</td>
			<td>RICCA Chemical Company</td>
			<td>2077-32</td>
			<td></td>
		 </tr>
		 <tr>
			<td>10% Oxalic Acid</td>
			<td>Alfa Aesar</td>
			<td>FW.90.04</td>
			<td></td>
		 </tr>
		 <tr>
			<td>Chloroform</td>
			<td>Fisher Scientific</td>
			<td>C607-4</td>
			<td></td>
		 </tr>
		 <tr>
			<td>Aluminum Sheets</td>
			<td>Alfa Aesar</td>
			<td>7429-90-5</td>
			<td></td>
		 </tr>
		 <tr>
			<td>PCBM</td>
			<td>Nano-C</td>
			<td>Nano-CPCBM-BF</td>
			<td></td>
		 </tr>
		 <tr>
			<td>Alq3</td>
			<td>Sigma Aldrich</td>
			<td>444561-5G</td>
			<td></td>
		 </tr>
		 <tr>
			<td>Rubrene</td>
			<td>Sigma Aldrich</td>
			<td>551112-1G</td>
			<td></td>
		 </tr>
		 <tr>
			<td></td>
			<td></td>
			<td></td>
			<td>Equipment</td>
		 </tr>
		 <tr>
			<td>FlexAL Atomic Layer Deposition (ALD)</td>
			<td>Oxford Instruments</td>
			<td></td>
			<td>For deposition of TiO2</td>
		 </tr>
		 <tr>
			<td>PVD Sputter System</td>
			<td>Kurt J. Lesker</td>
			<td></td>
			<td>For deposition of Au &amp; Al</td>
		 </tr>
		 <tr>
			<td>Flat Cell</td>
			<td>Princeton Applied Research</td>
			<td>K0235</td>
			<td>For anodization of Al</td>
		 </tr>
		 <tr>
			<td>Centrifuge</td>
			<td>HERMLE Labnet</td>
			<td>Z206 A</td>
			<td>For deposition of organic nanowires</td>
		 </tr>
	 </tbody>
 </table>

ultrahigh density array of vertically aligned small-molecular organic nanowires on arbitrary substrates

In recent years &pi;-conjugated organic semiconductors have emerged as the active material in a number of diverse applications including large-area, low-cost displays, photovoltaics, printable and flexible electronics and organic spin valves. Organics allow (a) low-cost, low-temperature processing and (b) molecular-level design of electronic, optical and spin transport characteristics. Such features are not readily available for mainstream inorganic semiconductors, which have enabled organics to carve a niche in the silicon-dominated electronics market. The first generation of organic-based devices has focused on thin film geometries, grown by physical vapor deposition or solution processing. However, it has been realized that organic nanostructures can be used to enhance performance of above-mentioned applications and significant effort has been invested in exploring methods for organic nanostructure fabrication.	
A particularly interesting class of organic nanostructures is the one in which vertically oriented organic nanowires, nanorods or nanotubes are organized in a well-regimented, high-density array. Such structures are highly versatile and are ideal morphological architectures for various applications such as chemical sensors, split-dipole nanoantennas, photovoltaic devices with radially heterostructured "core-shell" nanowires, and memory devices with a cross-point geometry. Such architecture is generally realized by a template-directed approach. In the past this method has been used to grow metal and inorganic semiconductor nanowire arrays. More recently &pi;-conjugated polymer nanowires have been grown within nanoporous templates. However, these approaches have had limited success in growing nanowires of technologically important &pi;-conjugated small molecular weight organics, such as tris-8-hydroxyquinoline aluminum (Alq3), rubrene and methanofullerenes, which are commonly used in diverse areas including organic displays, photovoltaics, thin film transistors and spintronics.	
Recently we have been able to address the above-mentioned issue by employing a novel "centrifugation-assisted" approach. This method therefore broadens the spectrum of organic materials that can be patterned in a vertically ordered nanowire array. Due to the technological importance of Alq3, rubrene and methanofullerenes, our method can be used to explore how the nanostructuring of these materials affects the performance of aforementioned organic devices. The purpose of this article is to describe the technical details of the above-mentioned protocol, demonstrate how this process can be extended to grow small-molecular organic nanowires on arbitrary substrates and finally, to discuss the critical steps, limitations, possible modifications, trouble-shooting and future applications.

As evidenced by the figures shown below (Figures 5 and 6), this centrifuge assisted drop casting method produces continuous nanowires. The nanowires, fabricated inside the pores of the AAO template, are vertically aligned, uniform, and electrically isolated from one another with capped bottoms. The diameter of the nanowires is determined by the diameter of pores in the template. They can be successfully fabricated on several different substrates, which lead to the potential application o...

Watch this Scientific Journal Video about Ultrahigh Density Array of Vertically Aligned Small-molecular Organic Nanowires on Arbitrary Substrates at JoVE.com

Ultrahigh Density Array of Vertically Aligned Small-molecular Organic Nanowires on Arbitrary Substrates

We report a simple method for fabricating an ultrahigh density array of vertically ordered small-molecular organic nanowires. This method allows for synthesis of complex heterostructured hybrid nanowire geometries, which can be inexpensively grown on arbitrary substrates. These structures have potential applications in organic electronics, optoelectronics, chemical sensing, photovoltaics and spintronics.

In  recent years &pi;-conjugated  organic semiconductors have emerged as the active material in a number of  diverse applications including large-area, ...

ultrahigh-density-array-vertically-aligned-small-molecular-organic

Research

JoVE Journal

Engineering

14.9K 次观看.  University of Alberta. 我们报告一个简单的方法制造的超高密度垂直有序的小分子有机纳米线阵列。这种方法可以合成复杂的异质结构的混合纳米线的几何形状，可以廉价地在任意衬底上生长的。这些结构有机电子学，光电子学，化学传感，光电和自旋电子学中具有潜在的应用。

视频: Ultrahigh Density Array of Vertically Aligned Small-molecular Organic Nanowires on Arbitrary Substrates

Micropunching Lithography for Generating Micro- and Submicron-patterns on Polymer Substrates

Conducting polymers have attracted great attention since the discovery of high conductivity in doped polyacetylene in 19771. They offer the advantages of low weight, easy tailoring of properties and a wide spectrum of applications2,3. Due to sensitivity of conducting polymers to environmental conditions (e.g., air, oxygen, moisture, high temperature and chemical solutions), lithographic techniques present significant technical challenges when working with these materials4. For example, current photolithographic methods, such as ultra-violet (UV), are unsuitable for patterning the conducting polymers due to the involvement of wet and/or dry etching processes in these methods. In addition, current micro/nanosystems mainly have a planar form5,6. One layer of structures is built on the top surfaces of another layer of fabricated features. Multiple layers of these structures are stacked together to form numerous devices on a common substrate. The sidewall surfaces of the microstructures have not been used in constructing devices. On the other hand, sidewall patterns could be used, for example, to build 3-D circuits, modify fluidic channels and direct horizontal growth of nanowires and nanotubes.
A macropunching method has been applied in the manufacturing industry to create macropatterns in a sheet metal for over a hundred years. Motivated by this approach, we have developed a micropunching lithography method (MPL) to overcome the obstacles of patterning conducting polymers and generating sidewall patterns. Like the macropunching method, the MPL also includes two operations (Fig. 1): (i) cutting; and (ii) drawing. The "cutting" operation was applied to pattern three conducting polymers4, polypyrrole (PPy), Poly(3,4-ethylenedioxythiophen)-poly(4-styrenesulphonate) (PEDOT) and polyaniline (PANI). It was also employed to create Al microstructures7. The fabricated microstructures of conducting polymers have been used as humidity8, chemical8, and glucose sensors9. Combined microstructures of Al and conducting polymers have been employed to fabricate capacitors and various heterojunctions9,10,11. The "cutting" operation was also applied to generate submicron-patterns, such as 100- and 500-nm-wide PPy lines as well as 100-nm-wide Au wires. The "drawing" operation was employed for two applications: (i) produce Au sidewall patterns on high density polyethylene (HDPE) channels which could be used for building 3D microsystems12,13,14, and (ii) fabricate polydimethylsiloxane (PDMS) micropillars on HDPE substrates to increase the contact angle of the channel15.

A micropunching lithography approach is developed to generate micro- and submicron-patterns on top, sidewall and bottom surfaces of polymer substrates. It overcomes the obstacles of patterning conducting polymers and generating sidewall patterns. This method allows rapid fabrication of multiple features and is free of aggressive chemistry.

Conducting polymers have attracted great attention since the discovery of high conductivity in doped polyacetylene in 19771. They offer the advantages of ...

Controlling the Size, Shape and Stability of Supramolecular Polymers in Water

For aqueous based supramolecular polymers, the simultaneous control over shape, size and stability is very difficult1. At the same time, the ability to do so is highly important in view of a number of applications in functional soft matter including electronics, biomedical engineering, and sensors. In the past, successful strategies to control the size and shape of supramolecular polymers typically focused on the use of templates2,3, end cappers4 or selective solvent techniques5. 
Here we disclose a strategy based on self-assembling discotic amphiphiles that leads to the control over stack length and shape of ordered, chiral columnar aggregates. By balancing electrostatic repulsive interactions on the hydrophilic rim and attractive non-covalent forces within the hydrophobic core of the polymerizing building block, we manage to create small and discrete spherical objects6,7. Increasing the salt concentration to screen the charges induces a sphere-to-rod transition. Intriguingly, this transition is expressed in an increase of cooperativity in the temperature-dependent self-assembly mechanism, and more stable aggregates are obtained. 
For our study we select a benzene-1,3,5-tricarboxamide (BTA) core connected to a hydrophilic metal chelate via a hydrophobic, fluorinated L-phenylalanine based spacer (Scheme 1). The metal chelate selected is a Gd(III)-DTPA complex that contains two overall remaining charges per complex and necessarily two counter ions. The one-dimensional growth of the aggregate is directed by &pi;-&pi; stacking and intermolecular hydrogen bonding. However, the electrostatic, repulsive forces that arise from the charges on the Gd(III)-DTPA complex start limiting the one-dimensional growth of the BTA-based discotic once a certain size is reached. At millimolar concentrations the formed aggregate has a spherical shape and a diameter of around 5 nm as inferred from 1H-NMR spectroscopy, small angle X-ray scattering, and cryogenic transmission electron microscopy (cryo-TEM). The strength of the electrostatic repulsive interactions between molecules can be reduced by increasing the salt concentration of the buffered solutions. This screening of the charges induces a transition from spherical aggregates into elongated rods with a length &gt; 25 nm. Cryo-TEM allows to visualise the changes in shape and size. In addition, CD spectroscopy permits to derive the mechanistic details of the self-assembly processes before and after the addition of salt. Importantly, the cooperativity -a key feature that dictates the physical properties of the produced supramolecular polymers- increases dramatically upon screening the electrostatic interactions. This increase in cooperativity results in a significant increase in the molecular weight of the formed supramolecular polymers in water.

The goal of this experiment is to determine and control the size, shape and stability of self-assembled discotic amphiphiles in water. For aqueous based supramolecular polymers such level of control is very difficult. We apply a strategy using both repulsive and attractive interactions. The experimental techniques applied to characterize this system are broadly applicable.

For aqueous based supramolecular polymers, the simultaneous control over shape, size and stability is very difficult1. At the same time, the ability to do ...

Monolayer Contact Doping of Silicon Surfaces and Nanowires Using Organophosphorus Compounds

Monolayer Contact Doping (MLCD) is a simple method for doping of surfaces and nanostructures1. MLCD results in the formation of highly controlled, ultra shallow and sharp doping profiles at the nanometer scale. In MLCD process the dopant source is a monolayer containing dopant atoms.
In this article a detailed procedure for surface doping of silicon substrate as well as silicon nanowires is demonstrated. Phosphorus dopant source was formed using tetraethyl methylenediphosphonate monolayer on a silicon substrate. This monolayer containing substrate was brought to contact with a pristine intrinsic silicon target substrate and annealed while in contact. Sheet resistance of the target substrate was measured using 4 point probe. Intrinsic silicon nanowires were synthesized by chemical vapor deposition (CVD) process using a vapor-liquid-solid (VLS) mechanism; gold nanoparticles were used as catalyst for nanowire growth. The nanowires were suspended in ethanol by mild sonication. This suspension was used to dropcast the nanowires on silicon substrate with a silicon nitride dielectric top layer. These nanowires were doped with phosphorus in similar manner as used for the intrinsic silicon wafer. Standard photolithography process was used to fabricate metal electrodes for the formation of nanowire based field effect transistor (NW-FET). The electrical properties of a representative nanowire device were measured by a semiconductor device analyzer and a probe station.

A detailed procedure for surface doping of Silicon interfaces is provided. The ultra-shallow surface doping is demonstrated by using phosphorus containing monolayers and rapid annealing process. The method can be used for doping of macroscopic area surfaces as well as nanostructures.

Monolayer Contact Doping (MLCD) is a simple method for doping of surfaces and nanostructures1. MLCD results in the formation of highly controlled, ultra ...

Evaluating Plasmonic Transport in Current-carrying Silver Nanowires

Plasmonics is an emerging technology capable of simultaneously transporting a plasmonic signal and an electronic signal on the same information support1,2,3. In this context, metal nanowires are especially desirable for realizing dense routing networks4. A prerequisite to operate such shared nanowire-based platform relies on our ability to electrically contact individual metal nanowires and efficiently excite surface plasmon polaritons5 in this information support. In this article, we describe a protocol to bring electrical terminals to chemically-synthesized silver nanowires6 randomly distributed on a glass substrate7. The positions of the nanowire ends with respect to predefined landmarks are precisely located using standard optical transmission microscopy before encapsulation in an electron-sensitive resist. Trenches representing the electrode layout are subsequently designed by electron-beam lithography. Metal electrodes are then fabricated by thermally evaporating a Cr/Au layer followed by a chemical lift-off. The contacted silver nanowires are finally transferred to a leakage radiation microscope for surface plasmon excitation and characterization8,9. Surface plasmons are launched in the nanowires by focusing a near infrared laser beam on a diffraction-limited spot overlapping one nanowire extremity5,9. For sufficiently large nanowires, the surface plasmon mode leaks into the glass substrate9,10. This leakage radiation is readily detected, imaged, and analyzed in the different conjugate planes in leakage radiation microscopy9,11. The electrical terminals do not affect the plasmon propagation. However, a current-induced morphological deterioration of the nanowire drastically degrades the flow of surface plasmons. The combination of surface plasmon leakage radiation microscopy with a simultaneous analysis of the nanowire electrical transport characteristics reveals the intrinsic limitations of such plasmonic circuitry.

Silver nanowires can simultaneously transport electrons and optical information in the form of surface plasmons. A procedure is described here to realize such a shared circuitry and the limitations at propagating both information carriers are evaluated.

Plasmonics is an emerging technology capable of simultaneously transporting a plasmonic signal and an electronic signal on the same information ...

Preparation and Use of Photocatalytically Active Segmented Ag|ZnO and Coaxial TiO2-Ag Nanowires Made by Templated Electrodeposition

Photocatalytically active nanostructures require a large specific surface area with the presence of many catalytically active sites for the oxidation and reduction half reactions, and fast electron (hole) diffusion and charge separation. Nanowires present suitable architectures to meet these requirements. Axially segmented Ag|ZnO and radially segmented (coaxial) TiO2-Ag nanowires with a diameter of 200 nm and a length of 6-20 &#181;m were made by templated electrodeposition within the pores of polycarbonate track-etched (PCTE) or anodized aluminum oxide (AAO) membranes, respectively. In the photocatalytic experiments, the ZnO and TiO2 phases acted as photoanodes, and Ag as cathode. No external circuit is needed to connect both electrodes, which is a key advantage over conventional photo-electrochemical cells. For making segmented Ag|ZnO nanowires, the Ag salt electrolyte was replaced after formation of the Ag segment to form a ZnO segment attached to the Ag segment. For making coaxial TiO2-Ag nanowires, a TiO2 gel was first formed by the electrochemically induced sol-gel method. Drying and thermal annealing of the as-formed TiO2 gel resulted in the formation of crystalline TiO2 nanotubes. A subsequent Ag electrodeposition step inside the TiO2 nanotubes resulted in formation of coaxial TiO2-Ag nanowires. Due to the combination of an n-type semiconductor (ZnO or TiO2) and a metal (Ag) within the same nanowire, a Schottky barrier was created at the interface between the phases. To demonstrate the photocatalytic activity of these nanowires, the Ag|ZnO nanowires were used in a photocatalytic experiment in which H2 gas was detected upon UV illumination of the nanowires dispersed in a methanol/water mixture. After 17 min&#160;of illumination, approximately 0.2 vol% H2 gas was detected from a suspension of ~0.1 g of Ag|ZnO nanowires in a 50 ml 80 vol% aqueous methanol solution.

Preparation and Use of Photocatalytically Active Segmented Ag|ZnO and Coaxial TiO2-Ag Nanowires Made by Templated Electrodeposition

Procedures are outlined to prepare segmented and coaxial nanowires via templated electrodeposition in nanopores. As examples, segmented nanowires consisting of Ag and ZnO segments, and coaxial nanowires consisting of a TiO2 shell and a Ag core were made. The nanowires were used in photocatalytic hydrogen formation experiments.

Photocatalytically active nanostructures require a large specific surface area with the presence of many catalytically active sites for the oxidation and ...

Resonance Raman Spectroscopy of Extreme Nanowires and Other 1D Systems

This paper briefly describes how nanowires with diameters corresponding to 1 to 5 atoms can be produced by melting a range of inorganic solids in the presence of carbon nanotubes. These nanowires are extreme in the sense that they are the limit of miniaturization of nanowires and their behavior is not always a simple extrapolation of the behavior of larger nanowires as their diameter decreases. The paper then describes the methods required to obtain Raman spectra from extreme nanowires and the fact that due to the van Hove singularities that 1D systems exhibit in their optical density of states, that determining the correct choice of photon excitation energy is critical. It describes the techniques required to determine the photon energy dependence of the resonances observed in Raman spectroscopy of 1D systems and in particular how to obtain measurements of Raman cross-sections with better than 8% noise and measure the variation in the resonance as a function of sample temperature. The paper describes the importance of ensuring that the Raman scattering is linearly proportional to the intensity of the laser excitation intensity. It also describes how to use the polarization dependence of the Raman scattering to separate Raman scattering of the encapsulated 1D systems from those of other extraneous components in any sample.

The paper describes a method for producing extreme nanowires by melt infiltration into carbon nanotubes and how 1D systems may be characterized and investigated using Resonance Raman Spectroscopy to determine vibrational and optical excitation energies.

This paper briefly describes how nanowires with diameters corresponding to 1 to 5 atoms can be produced by melting a range of inorganic solids in the ...

A Fabrication Method for Highly Stretchable Conductors with Silver Nanowires

Stretchable electronics are identified as a key technology for electronic applications in the next generation. One of the challenges in fabrication of stretchable electronic devices is the preparation of stretchable conductors with great mechanical stability. In this study, we developed a simple fabrication method to chemically solder the contact points between silver nanowire (AgNW) networks. AgNW nanomesh was first deposited on a glass slide via spray coating method. A reactive ink composed of silver nanoparticle (AgNPs) precursors was applied over the spray coated AgNW thin films. After heating for 40 min, AgNPs were preferentially generated over the nanowire junctions to solder the AgNW nanomesh, and reinforced the conducting network. The chemically modified AgNW thin film was then transferred to polyurethane (PU) substrates by casting method. The soldered AgNW thin films on PU exhibited no obvious change in electrical conductivity under stretching or rolling process with elongation strains up to 120%.

A simple synthesis method is used to chemically solder silver nanowire thin film to fabricate highly stretchable and conductive metal conductors.

Stretchable electronics are identified as a key technology for electronic applications in the next generation. One of the challenges in fabrication of ...

Effect of Bending on the Electrical Characteristics of Flexible Organic Single Crystal-based Field-effect Transistors

The charge transport in an organic semiconductor depends highly on the molecular packing in the crystal, which influences the electronic coupling immensely. However, in soft electronics, in which organic semiconductors play a critical role, the devices will be bent or folded repeatedly. The effect of bending on the crystal packing and thus the charge transport is crucial to the performance of the device. In this manuscript, we describe the protocol to bend a single crystal of 5,7,12,16-tetrachloro-6,13-diazapentacene (TCDAP) in the field-effect transistor configuration and to obtain reproducible I-V characteristics upon bending the crystal. The results show that bending a field-effect transistor prepared on a flexible substrate results in nearly reversible yet opposite trends in charge mobility, depending on the bending direction. The mobility increases when the device is bent toward the top gate/dielectric layer (upward, compressive state) and decreases when bent toward the crystal/substrate side (downward, tensile state). The effect of bending curvature was also observed, with greater mobility change resulting from higher bending curvature. It is suggested that the intermolecular &#960;-&#960; distance changes upon bending, thereby influencing the electronic coupling and the subsequent carrier transport ability.

This manuscript describes the bending process of an organic single crystal-based field-effect transistor to maintain a functioning device for electronic property measurement. The results suggest that bending causes changes in the molecular spacing in the crystal and thus in the charge hopping rate, which is important in flexible electronics.

The charge transport in an organic semiconductor depends highly on the molecular packing in the crystal, which influences the electronic coupling ...

Morphology Control for Fully Printable Organic&#8211;Inorganic Bulk-heterojunction Solar Cells Based on a Ti-alkoxide and Semiconducting Polymer

The photoactive layer of a typical organic thin-film bulk-heterojunction (BHJ) solar cell commonly uses fullerene derivatives as the electron-accepting material. However, fullerene derivatives are air-sensitive; therefore, air-stable material is needed as an alternative. In the present study, we propose and describe the properties of Ti-alkoxide as an alternative electron-accepting material to fullerene derivatives to create highly air-stable BHJ solar cells. It is well-known that controlling the morphology in the photoactive layer, which is constructed with fullerene derivatives as the electron acceptor, is important for obtaining a high overall efficiency through the solvent method. The conventional solvent method is useful for high-solubility materials, such as fullerene derivatives. However, for Ti-alkoxides, the conventional solvent method is insufficient, because they only dissolve in specific solvents. Here, we demonstrate a new approach to morphology control that uses the molecular bulkiness of Ti-alkoxides without the conventional solvent method. That is, this method is one approach to obtain highly efficient, air-stable, organic-inorganic bulk-heterojunction solar cells.

Morphology Control for Fully Printable Organic&amp;#8211;Inorganic Bulk-heterojunction Solar Cells Based on a Ti-alkoxide and Semiconducting Polymer

A method for fully printable, fullerene-free, highly air-stable, bulk-heterojunction solar cells based on Ti alkoxides as the electron acceptor and the electron-donating polymer fabrication is described here. Moreover, a method for controlling the morphology of the photoactive layer through the molecular bulkiness of the Ti-alkoxide units is reported.

The photoactive layer of a typical organic thin-film bulk-heterojunction (BHJ) solar cell commonly uses fullerene derivatives as the electron-accepting ...

Well-aligned Vertically Oriented ZnO Nanorod Arrays and their Application in Inverted Small Molecule Solar Cells

This manuscript describes how to design and fabricate efficient inverted solar cells, which are based on a two-dimensional conjugated small molecule (SMPV1) and [6,6]-phenyl-C71-butyric acid methyl ester (PC71BM), by utilizing ZnO nanorods (NRs) grown on a high quality Al-doped ZnO (AZO) seed layer. The inverted SMPV1:PC71BM solar cells with ZnO NRs that grew on both a sputtered and sol-gel processed AZO seed layer are fabricated. Compared with the AZO thin film prepared by the sol-gel method, the sputtered AZO thin film exhibits better crystallization and lower surface roughness, according to X-ray diffraction (XRD) and atomic force microscope (AFM) measurements. The orientation of the ZnO NRs grown on a sputtered AZO seed layer shows better vertical alignment, which is beneficial for the deposition of the subsequent active layer, forming better surface morphologies. Generally, the surface morphology of the active layer mainly dominates the fill factor (FF) of the devices. Consequently, the well-aligned ZnO NRs can be used to improve the carrier collection of the active layer and to increase the FF of the solar cells. Moreover, as an anti-reflection structure, it can also be utilized to enhance the light harvesting of the absorption layer, with the power conversion efficiency (PCE) of solar cells reaching 6.01%, higher than the sol-gel based solar cells with an efficiency of 4.74%.

This manuscript describes how to design and fabricate efficient inverted SMPV1:PC71BM solar cells with ZnO nanorods (NRs) grown on a high quality Al-doped ZnO (AZO) seed layer. The well-aligned vertically oriented ZnO NRs exhibit high crystalline properties. The power conversion efficiency of solar cells can reach 6.01%.

This manuscript describes how to design and fabricate efficient inverted solar cells, which are based on a two-dimensional conjugated small molecule ...